Article
The Effective of Pressure and Sintering Temperature for Hardness Characteristics of Shape Memory Alloy by Using Taguchi Technique
تأثير الضغط ودرجة حرارة التلبيد على الصلادة لسبيكة ذكية باستخدام تقنية تاكوشي

Authors: Ahmed Abdulrusool أحمد عبد الرسول --- Sarah Jalal Mosa سارة جلال موسى
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2016 Volume: 22 Issue: 1 Pages: 159-171
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This paper presents the Taguchi approach for optimization of hardness for shape memory alloy (Cu-Al-Ni) . The influence of powder metallurgy parameters on hardness has been investigated. Taguchi technique and ANOVA were used for analysis. Nine experimental runs based on Taguchi’s L9 orthogonal array were performed (OA),for two parameters was study (Pressure and sintering temperature) for three different levels (300 ,500 and 700) MPa ,(700 ,800 and 900)oC respectively . Main effect, signal-to-noise (S/N) ratio was study, and analysis of variance (ANOVA) using to investigate the micro-hardness characteristics of the shape memory alloy .after application the result of study shown the height hardness at the level 2 of pressure and level 1 of temperature (A2B1) by taguchi technique at magnitude value 500MPa and 700 ºC. The best effective factor at ANOVA has pressure 36.39%. the interaction given the best pressure 500 MPa and Temperature 800 ºC.

هذا البحث بين استخدام طريقة تاكوشي للوقوف على امثلية الصلادة لسبيكة ذكية وتضمن المتغيرات المؤثرة على صلادة نماذج مصنعة بطريقة ميتالورجيا المساحيق.تقنية تاكوشي و تحليل التباين, استعملت في عملية تحليل تسع عينات تمت تصنيعها اعتمادا على خوارزمية تاكوشي لمتغيرين اساسين للدراسة (ضغط ودرجة حرارة التلبيد) لثلاث مستويات مختلفة (300,500and 700) Mpaودرجة حرارة التلبيد (700,800 and 900) ºC على التوالي تم دراسة تأثير العامل الرئيسي ونسبة الضوضاء وكذلك تمت تحليل التباين للصلادة المايكروية للسبيكة الذكية.نتائج الدراسة بينت بعد التطبيق ان اعلى صلادة كانت في A2B1) )اي عند المستوى الثاني للضغط والمستوى الاول للحرارة وكانت قيمة الضغط 500Mpaوحرارةالتلبيد 700 ºC تحليل التباين بين ان افضل عامل مؤثر هو الضغط بنسبة36.39 % .العامل المؤثر ضمن مستويات مختلفة(interaction) بينت ان افضل ضغط 500MPa ودرجة حرارة التلبيد 800 ºC.


Article
The Effect of Iron Addition on the Dry Sliding Wear and Corrosion Behavior of Cu Al Ni Shape Memory Alloy
تأثیر إضافة الحدید في البلى ألانزلاقي الجاف وسلوك التآكل لسبیكة ( نحاس ألمنیوم نیكل ) التي تتذكر شكلھا.

Authors: Abdul Raheem . K. Abid Ali --- Zuheir T. Khulief.Al-Tai
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2010 Volume: 28 Issue: 24 Pages: 6888-6902
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this paper, dry sliding wear and corrosion behavior of Cu + 13wt% Al + 3.8 wt% Ni was prepared by powder metallurgy. Dry sliding wear has been studied based on pin on disk at constant velocity and constant sliding distance .Corrosion behavior in 5 wt% NaOH solution based up on potentiostatic ( Tafel ) has been presented for base shape memory alloy ( Cu + 13% Al + 3.8 % Ni ) in two cases austenitic and martensitic phase state . Further more , the effect of Fe additions as ( 0.4 , 0.8 and 1.2 wt% ) on the sliding wear and corrosion behavior ofbase alloy has also been studied .It is clear that Cu Al Ni shape memory alloy in martensitic state has more wear resistance than in austenitic structure . Also , corrosion resistances are better than in martensitic structure because the alloy has corrosion current density as 336.45 μA/cm2 in martansitic where as the corrosion current density is 633.62 μA/cm2 in austenitic structure . Further more , when theiron content increases , wear and corrosion rate increase too .

في هذا البحث تم دراسة البلى ألانزلاقي الجاف وسلوك التآكل للسبيكة ( نحاس + % 13 ألمنيوم + % 3.8 نيكل ) المحضرة بطريقة ميتالورجيا المساحيق. البلى ألانزلاقي الجاف درس باستخدام الترتيب المسماري إلى القرص تحت سرعة ثابتة ومسافة انزلاق ثابتة , السلوك التاكلي في محلول (% 5 هيدروكسيد الصوديوم ) كنسبة وزنيه تم دراسته للسبيكة باستخدام طريقة استكمال منحنى تافل , حيث تم تحضير السبيكة الأساس ( نحاس + % 13 ألمنيوم + % 3.8 نيكل ) في حالتين الأولى السبيكة في طور الاوستنايت والثانية في طور المارتنسايت .بالإضافة0.4 ) كنسب وزنيه في سلوك البلى , 0.8 , إلى ذلك تم دراسة تأثير إضافة الحديد وبنسب ( 1.2 ألانزلاقي الجاف وسلوك التآكل . أظهرت النتائج إن سبيكة ( نحاس- ألمنيوم- نيكل ) في طور المارتنسايت أكثر مقاومة للبلى مقارنة بالسبيكة في طور الاوستنايت , كذلك مقاومة التآكل أفضل للسبيكة في طور المارتنسايت والتي امتلكت كثافة تيار تاكل بمقدار ( 336.45.( مايكروامبيرسم 2) في حين للسبيكة في طور الاوستنايت ( 633.62 مايكروامبير سم 2 بالإضافة إلى ذلك عند زيادة محتوى الحديد فان معدل البلى والتآكل يزداد أيضا.


Article
The Physical and Mechanical Properties of a Shape Memory Alloy Reinforced with Carbon Nanotubes (CNTs)
الخواص الفيزيائية والميكانيكية لسبيكة ذاكرة للشكل مقواة بأنابيب الكاربون النانوية

Loading...
Loading...
Abstract

The shape Memory Alloy (SMA) (Copper-Aluminum-Nickel) was prepared in the research by Powder metallurgy (PM) in component percentage (Cu-13% Al-4% Ni), pressure of (500 Mpa) in one direction, and sintering in (800°C) with Nitrogen gas for three hours. (CNTs) was added in percentage (0,0.5,1.0,1.5,2.0,2.5) % as a volumetric ratio at the relatively of the copper ratio to obtain advanced composites for Carbon Nanotubes with a distinct effect on properties.The elements of the alloy were analyzed using the (EDS) system attached to the Scanning Electron Microscopy (SEM) and study the X-ray Diffraction (XRD) to definition the elements and compounds formed after the process of sintering while imaging the microscopic structure by both Optical Microscopes and (SEM).The physical characteristics were studied as the results showed that by increasing the content of the Carbon Nanotubes (CNTs), The Bulk Density values of the (Cu-13% Al-4% Ni) decrease by ratio (23.5%) for content of Carbon Nanotubes (0%) to (2.0%) associated with an increase in True Porosity with the increase of the (CNTs) content at the same ratio (27.85%) and the impact is reversed when the content is increased to (2.5%) as it corresponds to the Water Absorption. The decrease in thermal conductivity corresponds to the increase in the True porosity ratio while slightly improving the amount Thermal Conductivity at an add (2.5%) percentage (2.0%) of the (CNTs). Some Mechanical properties, such as Hardness and Compressive Strength, have been reduced by increasing the content of the (CNTs) to (2%) While there has been a slight improvement in these two characteristics at the corresponding ratio.

حُضرت سبيكة الذاكرة للشكل (Cu - Al – Ni) في بحثنا هذا بتقانة ميتالورجيا المساحيق (PM) وبنسبة مكونـــــــات (Cu – 13% Al- 4% Ni) وضغط كبس (500 Mpa) باتجاه واحد والتلبيد بدرجة حرارة (800°C) ولمدة ثلاث ساعات وبوجود غاز النيتروجين (N₂) وكانت إضافة انابيب الكاربون النانوية (CNTs) بالنسب %(0,0.5,1.0,1.5,2.0,2.5) كنسبة حجمية على حساب نسبة النحاس للحصول على متراكبات متقدمة لما لأنابيب الكاربون النانوية من تأثير متميز على الخواص.تم تحليل العناصر للسبيكة ومتراكباتها باستخدام منظومة (EDS) الملحقة بالمجهر الإلكتروني الماسح (SEM) ودراسة حيود الأشعة السينية (XRD) لتحديد العناصر والمركبات المتكونة بعد إجراء عملية التلبيد وتصوير البنية المجهرية بكل من المجهر الضوئي (Optical Microscope) و الـ (SEM) .درست الخصائص الفيزيائية إذ أظهرت النتائج أنَّه بزيادة محتوى أنابيب الكاربون النانوية (CNTs) تنخفض قيم الكثافة الحجمية للسبيكة (Cu-13% Al-4% Ni) ومتراكباتها بنسبة مقدارها (%23.5) لمحتوى أنابيب الكاربون النانوية من (%0) الى (%2.0) وترافقت زيادة المسامية الحقيقية مع زيادة محتوى الـ (CNTs) عند ذات النسب بنسبة مقدارها (%27.85) ويكون الفعلُ معاكسً عند زيادة المحتوى إلى (%2.5) إذ يتطابق السلوك مع قابلية امتصاصية الماء, واما الموصلية الحرارية فان سلوكها يتطابق مع سلوك الكثافة الحجمية والظاهرية ولذات النسب, وانخفضت بعض الخصائص الميكانيكية كالصلادة ومقاومة الانضغاط بزيادة محتوى الـ (CNTs) الى نسبة (%2) بينما حدث تحسن طفيف لتلك الخاصيتين عند النسب المتوافقة.


Article
Effect of Nb Addition on Hardness and Wear Resist of Cu-Al-Ni Shape Memory Alloy Fabricated By Powder Metallurgy
تاثير اضافة عنصر النايبيوم Nb على الصلادة ومقاومة البلاء الاحتكاكي لسبيكة Cu-Al-Ni ذات خاصية تذكر الشكل المصنعة بتكنولوجيا المساحيق

Authors: Raied Z. Alfay رائد زيور جميل --- Ayad M. Takhakh اياد مراد طخاخ --- Abdul Rahim K. Abid Ali عبد الرحيم كاظم عبد علي
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2014 Volume: 20 Issue: 1 Pages: 42-49
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Cu-Al-Ni shape memory alloy specimens has been fabricated using powder metallurgy technique with tube furnace and vacuum sintering environment , three range of Nb powder weight percentage (0.3,0.6,0.9)% has been added. Micro hardness and sliding wear resist has been tested followed by X-ray diffraction, scanning electron microscope (SEM) and energy dispersive X-ray spectroscope (EDX) for micro structure observation. The experimental test for the samples has showed that the increase of Nb powder weight percentage in the master alloy has a significant effect on increasing the hardness and decreasing the wear resist therefore it will enhance the mechanical properties for this alloy.

سبائك ذات قابلية التذكر للشكل Cu-Al-Ni قد تم تصنيعها باستخدام تكنولوجيا المساحيق وباستخدام الخواء كمحيط واقي في اثناء عملية التلبيد , ثلاثة مستويات للنسب الوزنية لعنصر النايبيوم Nb وهي (0.3 ، 0.6، 0.9) تمت اضافتها الى السبيكة الرئيسية .اختبارالصلادة الدقيقة ومقاومة البلاء الاحتكاكي تمت لجميع العينات والحقت بفحص مطياف الاشعة السينية. وتم استعمال المجهر الالكتروني SEM مع مطياف الاشعة السينية EDX لغرض معايتة البنية المجهرية للعينات .النتائج العملية اظهرت ان زيادة النسبة المئوية الوزنية المضافة من عنصر النايبيوم Nb الى السبيكة الرئيسية له تاثير كبير في زيادة الصلادة الدقيقة وزيادة مقاومة السبيكة للبلاء الاحتكاكي والتي بالتالي تؤدي الى تحسين في الخواص الميكانيكية للسبيكة الرئيسية .

Listing 1 - 4 of 4
Sort by
Narrow your search

Resource type

article (4)


Language

English (4)


Year
From To Submit

2018 (1)

2016 (1)

2014 (1)

2010 (1)