Article
Preparation and Characterization of Eggshell Powder (ESP) and Study its Effect on Unsaturated Polyester Composites Material

Author: Rafah A. Nasif
Journal: Iraqi Journal of Applied Physics المجلة العراقية للفيزياء التطبيقية ISSN: 18132065 23091673 Year: 2015 Volume: 11 Issue: 1 Pages: 25-28
Publisher: iraqi society for alternative and renewable energy sources and techniques الجمعية العراقية لمصادر وتقنيات الطاقة البديلة والمستجدة

Loading...
Loading...
Abstract

Microcomposites of unsaturated polyester (UP) with different loading of eggshell powder of grain size (36µ) ranging from 0 to 25wt% were prepared by hand – layup method. The mechanical properties of the composites such as: tensile strength, young's modulus and impact strength were studied as a function of filler loading. All of these mechanical properties values were decreased with increasing the filler concentration. To improve adhesion between the filler and matrix some coupling agents have been used like: NaOH, silane and stearic acid. The results showed that tensile strength and young modulus for stearic acid treated filler increase with increasing of filler loading followed by a decrease beyond 15wt%. Silane treated filler showed similar results o fimpact strength compared to untreated system. Impact strength of all coupling agent systems were increased with increasing the filler concentration, while decrease for untreated system. Finally, stearic acid treated filler have higher values of impact strength as compared to the other composites.


Article
EXPERIMENTAL INVESTIGATION ON PROPERTIES OF CEMENT MORTAR INCORPORATING EGGSHELL POWDER
التحري العملي لخواص مونة الاسمنت الحاوية على مسحوق قشور البيض

Author: Rawaa A. Al-Safy
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2015 Volume: 19 Issue: 6 Pages: 198-209
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

The use of waste materials in buildings is an innovative approach towards sustainability. The objective of this paper is to study the properties and behaviour of cement mortar using eggshells wastes. Various low concentrations of eggshell powder (ESP) (0,1,3 ,5, 7 and 10 wt%) were used as partial replacement of cement in mortar of (1:2) mixing ratio by weight. The maximum particle size of ESP is 75 μm. Soundness of cement in ESP-cement pastes was evaluated using Le Chatelier method. The influence of ESP on strengths of cement mortar was investigated by means of compression and flexural tests at various curing periods. It was found that, there was no negative impact of ESP on soundness of cement. A significant enhancement in compressive strength was recorded for all ESP-cement mortars at 7 days and 28 days. The highest improvements, (31.63%) and (11.65%), were observed for samples with 10wt% and 5 wt% of ESP respectively. At moderate periods of curing, samples with 1 wt% of ESP have the highest enhancements in compressive strength of about (8.93%) and (1.75%) for 42 days and 56 days respectively. A reduction in compressive strength was observed for all samples at late ages (70 days and 90 days). In terms of flexural strength, the addition of ESP (up to 5 wt%) results in improvement in the flexural strength when compared with the control samples. The highest enhancement (21.20%) was recorded when cement was replaced with only 1 wt% at 7 days.

ان استخدام مواد المخلفات في البناء هو نهج مبتكر نحو االستدامة.ان الهدف من هذا البحث هو دراسة خواص و سلوك مونة االسمنتباستخدام مخلفات قشور البيض. استخدمت نسب اضافة قليلة و مختلفة من مسحوق قشور البيض )ESP( )0 ، % 1 ، % 3 ، %5 ،%7 %و10 %وزنا( كبديل جزئي عن االسمنت في مونة ذات نسبة خلط وزنية )2:1 .)ان الحجم الحبيبي االقصى لمسحوق قشور البيض كان 75 مايكرون. تم التحري عن ثبات عجينة االسمنت الحاوية على ESP باستخدام طريقة لي شاتليه. ان تأثير ESP على مقاومة مونة االسمنت تم التحري عنهبواسطة فحصي االنضغاط و االنثناء و العمار انضاج مختلفة. لقد وجد بانه ال يوجد تاثير سلبي ل ESP على ثبات االسمنت. فيما يخص مقاومةالالنضغاط ، فقد زادت زيادة ملحوظة عند استخدام نسب مختلفة من ESP و العمار انضاج 7 أيام و 28 يوما. أعلى زيادة سجلت كانت بحدود)63.31 )%و )65.11 )%و لنماذج مونة االسمنت الحاوية على 5 %و 10 %وزنا من ESP على التوالي. اما في الفترات المعتدلة من المعالجة،فقد وجد ان النماذج الحاوية على 1 %وزنا من ESP اظهرت أعلى زيادة في مقاومة االنضغاط و كانت حوالي )93.8 )%و )75.1 )%والعمار انضاج 42 يوما و 56 يوما على التوالي. ولوحظ وجود انخفاض في مقاومة االنضغاط و لجميع العينات في اعمار انضاج متاخرة )70يوما و 90 يوما(. فيما يخص مقاومة االنثناء، فقد وجد بان إضافة ESP( إلى حد 5 %بالوزن( يؤدي الى تحسن مقاومة االنثناء عند مقارنتها معالنماذج المرجعية. وسجلت أعلى زيادة )20.21 )%عندما تم استبدال األسمنت فقط مع 1 %بالوزن و لعمر انضاج 7 أيام.