Types of the Fiber Glass-Mat on Fatigue Characteristic of Composite Materials at Constant Fiber Volume Fraction: Experimental Determination
تأثير نوع حصيرة الا لياف الزجاجية على سلوك الكلال للمواد المتراكبة عند نسبة حجميه ثابتة للالياف الزجاجية

Loading...
Loading...
Abstract

The aim of this work is to study the influence of the type of fiber glass –mat on fatigue behavior of composite material which is manufactured from polyester and E-glass (woven roving, chopped strand mat (CSM)) as a laminate with a constant fiber volume fraction (VF) of 33%. The results showed that the laminates reinforced with E-glass (woven roving) [0/90, ±45.0/90] and [0/90, CSM, 0/90] have lower fatigue strength than the laminates reinforced with E-glass [0/90]3,[CSM]3 and [CSM, 0/90, CSM] although they had different tensile strength; the best laminate was [0/90]3 .

يهدف البحث الحالي الى دراسة تأثير نوع طبقات اللالياف الزجاجية على سلوك الكلال للمواد المتراكبه المصنعه من البولستر وبنسبه حجميه ثابتة للألياف الزجاجية مقدارها 33%. أظهرت نتائج البحث ان المواد المصنعه من ] [0/90, CSM, 0/90], [0/90,±45, 0/90 تمتلك أدنى حد للكلال عند 107 من تلك للمواد المصنعه من[0/90]3 و,[CSM, 0/90, CSM] [CSM]3 على الرغم من انها تمتلك اجهاد شد اقصى مختلف وان أفضل الطبقات هي[0/90]3.


Article
Static tensile strength and fatigue behavior of polyester reinforced with the chopped strand mat (CSM) offiber glassat elevated temperature
مقاومة الشد وسلوك الكلال لمادة البولسنر المدعم بطبقات اللالياف الزجاجية نوع(حصيرة الخيوط القصيرة )عند درجات حرارة مختلف

Authors: Abdul-jabar H. Ali عبد الجبارحسين علي --- Dhafir S. Al-Fattal --- Hussain J. Al-alkaw حسين جاسم العلكاوي
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2013 Volume: 17 Issue: 3 Pages: 37-53
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

In the work present, describes an attempt has been made to study the effect of temperature on fatigue behavior of polyester reinforced with woven of fiber glass manufactured as a laminate [CSM]3.Fatigue tests were carried out at constant stress amplitude at different temperature environment. All fatigue tests were employed at stress ratio R=-1 and under constant fiber volume fraction (VF) of 33%. The results indicated that the tensile and the fatigue strength decreased with increasing temperature up to at 60 0C.The fatigue life reduction factor (FLRF) at 60 oC was in range (41%-61%) in range of applied stresses amplitude between (80-100MPa) compared at (RT).

الهدف من هذا العمل هو دراسة تأثير درجة الحرارة على مقاومة الشد وسلوك الكلال لمادة البولستر المدعم بطبقات الالياف الزجاجية نوع (حصيرة الخيوط القصيرة) وبنسبة حجمية قدرها 33%. اظهرت النتائج ان مقاومة الشد ومقاومة الكلال تقل مع زيادة درجةالحرارة الى 60 درجة مئوية . وان معامل تخفيض عمر الكلال عند 60 درجة مئوية كان بحدود (41%-61%) ضمن تأثير سعة اجهادات مسلطة ما بين (80 -100 ميكا باسكال) مقارنة عند درجة حرارة المختبر