Removal of Phenol Pollutants by Modification Molecular Sieves 13X
أزالة ملوثات الفينول بتطوير المناخل الجزيئية 13X

Authors: Laith S. Sabri --- Jabir Shanshool
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 15 Pages: 2853-2862
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Molecular sieves type 13X was modified by treatment with saturated solution of urea or thiourea and adding of sodium silicate as binder to give homogeneous admixture in approximate weight percent, 20% urea or thiourea, 30% binder, and 50% MS13X. The samples were dried and shaped in cylindrical particles of about 5mm diameter and 4-8mm length. The FTIR studies show some interaction between the added urea and thiourea with the original substrates. These are mainly hydrogen band type interactions through –NH2 moiety with –OH group of framework oxygen inthe substrate or with adsorbed water. The urea displayed more significant interaction with MS13X than thiourea. Molecular sieve 13X and its admixtures with urea and thiourea showed good ability to remove phenol from water. The urea modified sample, which has the largest surface area, was the best adsorbent for phenol followed by thiourea treated sample. Excellent degree of phenol removal, greater than98% was achieved by using 0.2 l/h flow rate of 10ppm phenolic solution and 56cm bed length at 300C. The increasing of inlet phenol concentration in water affected largely the driving force and the rate of adsorption, resulted also in higher capacities. While the percentage removal of phenol was decreased by fixed other operating conditions

13 طورت بمعالجتها مع محلول مشبع من اليوريا والثايويوريا ,ثم X المناخل الجزيئية نوع اضافة سليكات الصوديوم كمادة رابطة,يتكون خليط متجانس بالنسب الوزنية , 50 % مناخل جزيئية %30 مادة رابطة , 20 % مادة التحوير, يوريا او ثايويوريا. تم تشكيل النماذج على شكل اسطواني , 4-8 طول. ان تحاليل مطياف الاشعة تحت الحمراء بينت حصول تاثيرات mm بقطر 5ملم و ملحوضة لليوريا والثايويوريا المضافة للمادة الاساس. انعكس ذلك بصورة رئيسية باتجاه ربطلتركيب الاوكسجين –OH مع مجاميع –NH الهايدروجين في المادة المعززة من خلال مجاميع 2 في المناخل الجزيئية او من خلال الماء الممتز.لوحظ ان اليوريا ادت الى تأثير اكثر مع المناخل 13 وتحويراتها مع اليوريا والثايويوريا X الجزيئية مقارنة بالثايويوريا. تتمتع المناخل الجزيئية نوع بقابلية جيدة لامتزاز الفينول من الماء. حيث تعد النماذج المحسنة باليوريا والتي تتمتع بدورها باكبر مساحة سطحية, افضل النماذج امتزاز للفينول يليها تلك المعاملة بالثايويوريا.تم تحقيق ازالة عالية للفينول اكثر من 98 % باستخدام 0.2 لترساعة سرعة جريان المحلول الحاوي على 10 جزءم ضمن التجارب المستخدمة في البحث. يؤثر ○ بالمليون فينول و 56 سم طول وسط الامتزاز عند 30 زيادة تركيز الفينول في الماء بشدة على القوة الدافعة وبالتالي على سرعة الامتزاز وتعطي ايضا سعة اكبر. بينما تنخفض نسبة الازالة للفينول عند ثبوت ظروف التشغيل الاخرى.


Article
Synthesis and Characterization of Nanocrystalline Aluminophosphate AlPO4-5 Molecular Sieve

Author: Asir Alnaama
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2018 Volume: 24 Issue: 3 Pages: 161-175
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Nanocrystalline aluminophosphate AlPO4-5 molecular sieves were synthesized by hydrothermal method (HTS). Synthesis parameters like time and temperature of crystallization were investigated. Type of template (R) and ratio of R/P2O5 were studied also. Characterization of the synthesized AlPO4-5 were done by powder X-ray diffraction (XRD), scanning electron microscopy (SEM/EDX), Fourier transform infrared (FTIR), differential scanning calorimetry-thermogravimetry analysis (DSC-TGA), and N2 adsorption-desorption BET analysis. XRD patterns results showed excellent crystallinity for two types of templates, di-n-propylamine (DPA) and tetrapropyl ammonium hydroxide (TPAOH) for alumminophosphate five (AFI) structure. Nano-level for particle size of 66 nm was revealed by AFM test. Good thermal stability was obtained in DSC-TGA results. Best time and temperature of crystallization of 24h and 190 O C were got. Optimum R/P2O5 for two kind of template was established.


Article
Synthesis and Characterization of Nanocrystalline Micro-Mesoporous ZSM-5/MCM-41 Composite Zeolite

Authors: Najwa Saber Majeed --- Asir Abduljabbar Saleh
Journal: Iraqi Journal of Chemical and Petroleum Engineering المجلة العراقية للهندسة الكيمياوية وهندسة النفط ISSN: 19974884/E26180707 Year: 2016 Volume: 17 Issue: 1 Pages: 71-82
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Nanocrystalline micro-mesoporous ZSM/MCM-41 composite was synthesized using alkaline treatment method and two step of crystallization in poly tetraflouroethylene (PTFE) lined autoclave. The synthesized zeolites was characterized by X-Ray diffraction (XRD), Scanning electron microscopy (SEM), Transmission electron microscopy (TEM), Atomic force microscopy (AFM), Fourier transport infrared (FTIR), and N2 adsorption-desorption (BET). It was approved that the best results for alkaline leaching can be got with 1.5M NaOH solution. High surface (BET) area of 630 m2/g with pore volume of 0.55 cm3/g has been got. AFM reports showed a nano-level size for average particle size of 50nm.