Article
Influence of Coating with Some Natural Based Materials on the Erosion Wear Behavior of Glass Fiber Reinforced Epoxy Resin
تأثير الطلاء لبعض المواد المتراكبة التي اساسها مواد طبيعية على سلوك بلى التعرية لراتنج الايبوكسي المدعم بالالياف الزجاجية

Loading...
Loading...
Abstract

In the present study, composites were prepared by Hand lay-up molding. The composites constituents were epoxy resin as a matrix, 6% volume fractions of glass fibers (G.F) as reinforcement and 3%, 6% volume fractions of preparation natural material (Rice Husk Ash, Carrot Powder, and Sawdust) as filler. Studied the erosion wear behavior and coating by natural wastes (Rice Husk Ash) with epoxy resin after erosion. The results showed the non – reinforced epoxy have lower resistance erosion than natural based material composites and the specimen (Epoxy+6%glass fiber+6%RHA) has higher resistance erosion than composites reinforced with carrot powder and sawdust at 30cm , angle 60°, grin size of sand 425µm , temperature 30Ċ , 300 gm salt content in 2liter of water and 15 hour. Coating specimen with mixed epoxy resin -RHA with particles size in the range (1.4-4.2) µm improves erosion wear resistance characteristics of the coated specimen, coating thickness was (16 ± 1) μm and after erosion at (15 hour) the thickness was (10) μm .

تم في هذا البحث تحضير المواد المتراكبة بوساطة طريقة القولبة اليدوية . تتكون المواد المتراكبة من راتنج الايبوكسي ماده اساس والياف الزجاج مادة تقوية بكسر حجمي 6% و مساحيق طبيعية محضرة ( رماد قشور الرز و مسحوق الجزر و بودرة الخشب ) بكسر حجمي (3% , 6% ) . دراسة سلوك بلى التعرية والطلاء بوساطة النفايات الطبيعية (رماد قشور الرز) مع راتنج الايبوكسي بعد التعرية . النتائج اظهرت بان الايبوكسي غير المقوى يمتلك مقاومة للتعرية قليلة من المواد المتراكبة التي اساسها مواد طبيعة والعينة (الايبوكسي + 6%الالياف زجاج + 6% رماد قشور الرز) تملك مقاومة للتعرية من المواد المتراكبة المدعمة بمسحوق الجزر وبودرة الخشب عند25 سم ، زاوية 30º، حجم دقائق تعرية 850 مايكرون , ودرجة حرارة 25Ċ ,200 غم ملح في 3 لتر من ماء 15 ساعة . طلاء العينات براتنج الايبوكسي مع رماد قشور الرز مع حجم حبيبي ضمن المدى (1.4-2.4) مايكرون لتحسين خواص مقاومة التعرية للعينات التي تم طلائها , وسمك الطلاء كان (16 ± 1) مايكرون وبعد التعرية عند 15 ساعة اصبح سمك الطلاء (10) مايكرون .


Article
Investigation of Tensile and Impact of Composite Materials Reinforced with Natural Materials
التقصي عن الشد والصدمة للمواد المتراكبة المقواة بمواد طبيعية

Author: Alaa Abd Mohammed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 4 Part (A) Engineering Pages: 919-933
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This work focuses on studying the effect of Data Seeds (DS) and Olive Seeds (OS) particles on tensile and impact properties of epoxy resin. Olive and dates seeds powder were added to epoxy matrix at weight fraction (0, 8, 13, &18 wt %) with grain size (300, 450 & 600µm). The composite specimens were prepared by Hand-Lay-up technique and cut according to standard test. It's found the higher value of modulus of elasticity and tensile strength happened at (=18 wt %) and grain size (300µm) for specimens reinforced with olive seeds powder, but obtained the lower percentage of elongation at break, impact strength and fracture toughness at this value. Also the mathematical model results show that the weight fraction of powder have higher effect than grain size on properties.

يتركز هذا العمل على دراسة تأثيرمسحوق نوى الزيتون والتمر على خواص الشد والصدمة لمادة الايبوكسي. تم أضافة كل من مسحوق نوى الزيتون والتمر الى مادة الاساس الايبوكسي بالكسورالوزنية التالية (0, 8, 13 &18 wt%) مع حجم حبيبي300, 450 & 650µm) ). حضرت العينات المتراكبة بطريقة الخلط اليدوي ثم تم اجراء تقطيع للعينات حسب المواصفة القياسية لكل فحص. بينت النتائج بإن اعلى قيم لمعامل المرونة, و اجهاد شد حدثت عند كسر وزني (=18 wt%) وحجم حبيبي(300µm) عند التقوية بمسحوق نوى الزيتون لكن أقل قيمة للأستطالة النسبية ومقاومة الصدمة ومتانة الكسر حدثت عند هذه النسبة. كذلك بينت نتائج الموديل الرياضي بإن الكسرالوزني لمادة التقوية كانت ذو تأثير أكثر من الحجم الحبيبي على الخواص.


Article
THE EXPERIMENTAL STUDY AND STATISTICAL EVALUATION OF THE WEAR AND HARDNESS OF EPOXY REINFORCED WITH NATURAL MATERIALS
الدراسة العملية والتقييم الاحصائي للبلى والصلادة لمادة الايبوكسي المدعم بمواد طبيعية

Author: Alaa Abd Mohammed
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2016 Volume: 20 Issue: 3 Pages: 14-24
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

This work focuses on study the effect of Date Seeds (DS) and Olive Seeds (OS) on wear rate and hardness property of epoxy resin. Olive and dates seeds were added to epoxy at weight fraction (0, 8, 13, &18wt%) with grain size (300, 450 & 600µm). The composite specimens were prepared by Hand-Lay up technique and cut according to standard test. The results show that the hardness of composites increases with weight fraction of powder increase and the wear rate decreases with increasing weight fraction of powder. Also it is found that the higher value of hardness and wear resistance were at (% =18 wt%) with grain size (300µm) for specimens reinforced with olive seeds. The mathematical model results show that the weight fraction of powder have higher effect than particle size on properties.

يتركز هذا العمل على دراسة تأثير مسحوق نوى الزيتون والتمر على خاصية الصلادة ومعدل البلى لمادة الايبوكسي. تم أضافة مسحوق نوى الزيتون والتمر الى الايبوكسي بالنسب الوزنية التالية (0, 8, 13, 18 wt%) مع حجم حبيبي (300, 450&600µm). حضرت العينات المتراكبة بطريقة القولبة اليدوية ثم تم اجراء تقطيع العينات حسب المواصفة القياسية لكل فحص. بينت النتائج بأن الصلادة للمتراكبات تزداد بزيادة الكسر الوزني للمسحوق ومعدل البلى يتناقص مع زيادة الكسر الوزني للمسحوق. أيضاً وجد بإن اعلى قيم صلادة ومقاومة بلى كانت عند نسبة وزنية =18 wt%)) وبحجم حبيبي (=300µm) للمتراكبات المقواة بمسحوق نوى الزيتون. بينت نتائج الموديل رياضي بإن الكسر الوزني لمادة التقوية كانت ذات تأثير أكثر من الحجم الحبيبي على الخواص.


Article
Studying the Effect of Mixture of Pomegranate Peel and Licorice on the Mechanical Properties of Epoxy

Author: Najmuldeen Yousif Mahmood
Journal: AL-NAHRAIN JOURNAL FOR ENGINEERING SCIENCES مجلة النهرين للعلوم الهندسية ISSN: 25219154 / eISSN 25219162 Year: 2017 Volume: 20 Issue: 4 Pages: 871-875
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

Reinforcement process of epoxy has been widely used to improvement of mechanical properties. Therefore, this work is concerned with the reinforcement of epoxy by adding natural materials (Pomegranate peel and Licorice particles) at epoxy. Different percentages of particles (5, 10, 15 and 20%) were used. The mechanical testing were included tensile, bending, hardness and impact tests. Hardness of epoxy was increased at increasing of Pomegranate peel (PP) and Licorice (L) percentages. Impact resistance of epoxy with Pomegranate peel (PP) has reached the highest at (10%), while with Licorice (L) has reached the highest at (5%). The results of tensile strength represent that increases of tensile strength at all percentages of (L), while (PP) showed that decreases at (5%) and increases at others percentage. Bending strength of epoxy has increased as increasing of (PP) at all percentage that used, but it has increased at (5, 10 and 20%) of (L), while it has dropped at (15%).

استخدمت عملية تقوية الايبوكسي على نطاق واسع لتحسين الخواص الميكانيكية. لذلك تعلقت الدراسة بتقوية الايبوكسي بأضافة المواد المواد الطبيعية (دقائق قشور الرمان وعرق السوس) الى الايبوكسي. استخدمت نسب مختلفة من الدقائق (5, 10, 15 و 20%). الاختبارات الميكانيكية تظمنت اختبارات الشد , الانحناء , الصلادة و الصدمة. تزداد صلادة الايبوكسي بزيادة نسبة قشور الرمان وعرق السوس. وصلت مقاومة الصدمة للايبوكسي اقصى قيمة عند (10%) من قشور الرمان بينما وصلت القيمة القصوى لمقاومة الصدمة عند (5%) من عرق السوس. بينت نتنائج مقاومة الشد زيادة عند كل نسب عرق السوس بينما تتناقص عند (5%) وازدات عند باقي النسب من قشور الرمان. مقاومة الانحناء للايبوكسي تزداد بزيادة قشور الرمان عند كل النسب في حين تزداد مقاومة الانحناء عند (5 , 10 و 20%) من عرق السوس وتنخفض عند (15%).


Article
Coating of Oil Pipes Products with Erosion-Resistant Composite Materials Reinforced with Carbonates and Natural Wastes

Authors: Reem Alaa Mohammed --- Aseel B. AL-Zubaidi
Journal: Journal of Petroleum Research & Studies مجلة البحوث والدراسات النفطية ISSN: 22205381 Year: 2019 Issue: 25 Pages: E40-E56
Publisher: Ministry of Oil وزارة النفط

Loading...
Loading...
Abstract

Polymer - based components are exposed to many damage influences during their lifetime. One of these influences erosion, which is a crucial problem in many industrial applications such as pipes, boats, sewage…etc. Due to impingements of solid particles being suspended in the fluids flowing at high velocity. This work reports an investigation of erosion wear characteristics and their resistance to erosion wear after coated by using (spin coating) with rice husk ash – mixed (epoxy resin). Composites specimens have been prepared by (Hand lay-up) molding method. The composite specimens are composed of epoxy resin as the matrix, and 6% vf of glass fiber as reinforcing material and filler powders from natural wastes and industrial processed powders at 3% and 6% vf. The natural wastes are rice husk ash (RHA), carrot waste and sawdust (wood powder) while industrial processed powders are Na2CO3, CaCO3 and K2CO3. Solid particles erosion wear tests and coating after erosion are also carried out. The coating specimens with RHA-mixed epoxy resin at an optimized size of the particles 1.4-4.2 µm improvement erosion wear resistance. The optical microscope results of the coated specimens show those coatings are resistant to erosion parameters.


Article
INVESTIGATION THE EFFECT OF NATURAL MATERIALS ON WEAR AND HARDNESS PROPERTIES OF POLYMERIC COMPOSITE MATERIALS
التقصي عن تأثير المواد الطبيعية على خواص البلى والصلادة للمواد المتراكبة البوليميرية

Loading...
Loading...
Abstract

This research studied the properties of orange and pomegranate reinforced unsaturated polyester with different powder weight fraction Wf. The orange and pomegranate powders were added to unsaturated polyester at weight fraction (0,4 ,8 & 11 wt%) with grain size (53µm). The composite specimens were prepared by hand lay-up technique and cutting according to (ASTM) for wear test, hardness test to obtain of the composite specimens. The results show that the wear rate for all tested specimens increases with increase of time of applied load and the wear rate decreases with increasing weight fraction of particles. Also the best value of properties was obtained for composite materials reinforced with pomegranate peel at (=11wt%) than composite materials reinforced with orange peel at this value.

في هذا البحث تم دراسة خواص البلى والصلادة للبولي استر الغير مشبع المقوى بمسحوق البرتقال والرمان عند كسور وزنية مختلفة. تم أضافة كل من مسحوق البرتقال والرمان الى مادة الاساس البولي استر الغير مشبع بالكسور الوزنية التالية (0, 4, 8 &11 wt%) مع حجم حبيبي53µm)).حضرت العينات بطريقة يدوية وقطعت وفق المواصفات القياسية ASTM)) لفحصي البلى والصلادة. النتائج اظهرت بإن معدل البلى لكل عينات الاختبار يزداد بزيادة وقت تسليط الحمل ويقل مع زيادة الكسر الوزني للمساحيق. أيضاً افضل قيم للخواص تم الحصول عليها للمواد المركبة المقواة بمسحوق الرمان حدثت عند كسر وزني (=11 wt%) افضل من مسحوق البرتقال عند هذه النسبة.

Listing 1 - 6 of 6
Sort by
Narrow your search

Resource type

article (6)


Language

English (5)

Arabic and English (1)


Year
From To Submit

2019 (1)

2017 (1)

2016 (2)

2015 (2)