Article
Effect of Cooling Rate on the Phase Transformations Behavior and Hardness of NiTi Shape Memory Alloys

Authors: Hiba Adil --- Abeer Sami --- Moqdad Juber --- Nawal Mohammed Dawood
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2015 Volume: 23 Issue: 2 Pages: 363-371
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

NiTi alloy is well- known shape memory alloys and has been widely used for bio-medical, mechanical and electrical applications. In this study, a Ni - rich porous NiTi alloys are produced by powder metallurgy technique. Three samples of these alloys were cooled in three media: furnace, water, and ice bath. X-ray diffraction (XRD) was used in the study as characterization techniques, hardness measurement and shape memory effect (SME) properties were carried out to investigate the effect of cooling rate on phases and mechanical properties. XRD test shows that the sintered samples consist of three phases at room temperature (NiTi monoclinic phase, NiTi cubic phase and Ni3Ti hexagonal phase) .The results show the correlation between cooling rate and properties of the alloy

تعرف سبيكة NiTi بانها من السبائك ذاكرة الشكل وتستخدم بشكل واسع في التطبيقات الاحيائية الطبية والميكانيكية والكهربائية. في هده الدراسة حضرت سبيكة NiTi المسامية الغنية بالنيكل بتقنية ميتالورجيا المساحيق. بردت ثلاثة عينات من هده السبائك في ثلاثة أوساط: الفرن، الماء، الثلج. استخدمت تقنية حيود الاشعة السينية (XRD) لوصف الاطوار المتكونة. كما أجري اختبار فيكرز للصلادة وتأثير استعادة الشكل (SME) لمعرفة تأثير معدل التبريد على الاطوار والخواص الميكانيكية. أظهرت اختبارات XRD تكون العينات الملبدة من ثلاثة اطوار في درجة حرارة الغرفة (احادي الميل NiTi، الطور المكعب، NiTiالطور السداسي Ni3Ti. أظهرت النتائج وجود علاقة بين معدل التبريد وخواص السبيكة.


Article
PREPARATION AND CORROSION BEHAVIOR OF NITI SHAPE MEMORY ALLOY COATED WITH BIOCOMPATABLE LAYER
تحضير ودراسة سلوك التاكل لسبيكه نيكل- تيتانيوم المتذكرة للشكل مطليه بطلاء ذو توافق حيوي

Loading...
Loading...
Abstract

In this paper NiTi shape memory alloy has prepared from elemental Nickel and Titanium powders by powder metallurgy Technique, the is 620 MPa compacting pressure , 850 ˚C temperature and10-3 torr vacuum atmosphere. The Porosity and density before and after sintering have been calculated. X-ray diffraction analysis showed that Nickel and Titanium are completely transformed into NiTi and Ni3Ti phase. Poly Methyl Methane Acrylate and Poly Methyl Methane Acrylate / Hydroxy apatite coating are applied to the surface of the alloy. Optical microscopy technique is used to characterize the surface of each sample. The corrosion rate has been studied in vitro by using electrochemical technique by a potentiostate in Hank’s Solution, Artificial saliva and 0.9% NaCl solution at 37 ºC. Atomic Absorption Spectroscopy technique is used to detect the Ni ion release from the alloy in 0.9% NaCl solution. The corrosion test results shows that the corrosion rate after Poly Methyl Methane Acrylate / Hydroxyapatite coating decreased from 12.14 mpy for bare sample into 0.132 mpy in 0.9% NaCl solution , from 4.94 mpy into 0.39 mpy Artificial saliva and from 12.66 mpy into 0.217 mpy in Hank Solution. The Ni release test shows that the amount of releasing Ni ion decreased into undetectable amount after coating with Poly Methyl Methane Acrylate and Poly Methyl Methane Acrylate / Hydroxyapatite.

في هذا البحث تم تحضير سبيكة نيكل-تيتانيوم المتذكره للشكل بواسطة تقنية ميتالورجيا المساحيق باستخدا ضغط كبس مساوي 620 MPa ودرجهة حراره تلبيد850 ˚C وبجو مفرغ 10-3 torr .تم حساب المساميه والكثافه قبل وبعد عملية التلبيد.فحص حيود الاشعه السينية اظهر ان النيكل والتيتانيوم تولا بالكامل الى NiTi و Ni3Ti .تم طلاء سطح العينات بطبقة بولي مثيل ميثان اكريليت وطبقة بولي مثيل ميثان اكريليتهيدروكسي اباتايت ومن ثم دراسة سطح العينات بواسطة المجهر الضوئي.معدل التاكل تم حسابه بالطريقه الكهروكيمائيه باستخدام جهاز المجهاد الساكن في محلول هانك,محلول اللعاب الصناعي,ومحلول 0.9% كلوريد الصوديوم بدرجة 37 ºC.كميه ايون النيكل المتحرر تم حسابها بواسطة مطيافية الامتصاص الذري بعد الغمر بمحلول 0.9% كلوريد الصوديوم .نتائج التاكل بينت ان معدل التاكل قد انخفض بعد الطلاء ب بولي مثيل ميثان اكريليتهيدروكسي اباتايت من 12.14 mpy قبل الطلاء الى 0.132 mpy في محلول0.9% كلوريد الصوديوم,ومن 4.94 mpy الى 0.39 mpy في محلول اللعاب الصناعي ومن 12.66 mpy الى 0.217 mpy في محلول هانك. فحص تحرر ايون النيكل اظهر ان تحرر ايون النيكل تم تقليله الى قيم لا يتحسسها جهاز مطيافيه الامتصاص الذري بعد الطلاء ب بطبقة بولي مثيل ميثان اكريليت وطبقة بولي مثيل ميثان اكريليت هيدروكسي اباتايت.


Article
Experimental and Finite Elements Analysis Study of Warming Effect on Deboned Force for Embedded NiTinol Wire into Linear Low Density Polyethylene
دراسة عملية وتحليل العناصر المحددة لتاثير التسخين على قوة الانسلاخ لسلك النيتينول مغمور داخل بولي اثيلين خطي منخفض الكثافة

Authors: Ali Yasser Hassan علي ياسر حسن --- Samir Ali Amin سمير أمين علي
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2018 Volume: 14 Issue: 4 Pages: 1-8
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This study presents the debonding propagation in single NiTi wire shape memory alloy into linear low-density polyethylene matrix composite the study of using the pull-out test. The aim of this study is to investigate the pull-out tests to check the interfacial strength of the polymer composite in two cases, with activation NiTinol wire and without activation. In this study, shape memory alloy NiTinol wire 2 mm diameter and linear fully annealed straight shape were used. The study involved experimental and finite element analysis and eventually comparison between them. This pull-out test is considered a substantial test because its results have a relation with behavior of smart composite materials. The pull-out test was carried out by a universal tensile test machine type (Laryee), load capacity (50 kN), and a test speed of 1mm/min. The finite elements modeling was performed by ANSYS V.15. The results of pull-out test showed that in the activation of NiTinol wire embedded in host matrix linear low-density polyethylene (LLDPE), the deboned force was about 74 N, but for the case without activation, it was about 106 N. Deboned shear stress for the case with activation was about 0.73 MPa, but for the case of without activation, it was about 1.05 MPa. ANSYS result for deboned shear stress in case with activation was about 0.8 MPa. As for the case of without activation, deboned shear stress was about 0.99 MPa. The activation of the ratio of deboned shear stress and deboned force decreased by 30.47% and 30.13%, respectively. The error ratio between experimental and ANSYS results was equal to 8% for the case with activation and 5.7% for the case without activation.

هذا البحث يقدم دراسة نشوء الانسلاخ لسلك نيتينول مفرد سبيكة ذاكرة الشكل داخل بولي اثيلين خطي منخفض الكثافة مصفوفة مركبة دراسة باستخدام فحص السحب. الهدف من هذا البحث دراسة فحص السحب لتحقق من قوة التداخل لمركب بوليميري في حالتين, مع تنشيط سلك النيتينول وبدون تنشيط . في هذا البحث سيكة ذاكرة الشكل سلك نيتينول قطر 2 مليمتر شكل مستقيم كامل التصليب قد استخدم. الدراسة شملت العملي وتحليل العناصر المحددة واخيرا المقارنة بينهم. يعد فحص السحب فحصاً اساسياً بسبب نتائجه لها علاقة بسلوك المواد المركبة الذكية. فحص السحب قد نفذه بواسطة آلة اختبار الشد العالمي نوع (لاري) , ذو سعة حمل 50 كيلو نيوتن, سرعة الفحص 1 ملم/دقيقة قد استخدمت. نفذت نمذجة العناصرالمحدد بوساطة انسيز الاصدار 15. نتائج فحص السحب اثبتت عند تنشيط سلك النيتينول المغمورداخل مصفوفة المضيف بولي اثيلين خطي منخفض الكثافة, قوة الانسلاخ حوالي 74 نيوتن, لكن في حالة بدون تنشيط حوالي 106 نيوتن. اجهاد قص الانسلاخ في التنشيط حوالي 0.73 ميكا باسكال, لكن بدون تنشيط حوالي 0.99 ميكا باسكال. خلال التنشيط النسبة لاجهاد قص الانسلاخ تقل بي 30.47% و 30.13%, على التوالي. نسبة الخطأ بين النتائج العملية والانسزز 8% في حالة التنشيط و 5.7% في حالة بدون تنشيط.


Article
NUMERICAL AND EXPERIMENTAL STUDY OF SHAPE EFFECT BEHAVIOR OF NITINOL WIRE

Authors: Samir Ali Amin --- Ali Yasser Hassan
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2019 Volume: 23 Issue: 2 Pages: 1-11
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

The aim of this research, returned NiTinol wire to original length by activation. The experimental test and ANSYS v15 software were conducted to study the shape memory effect behavior for NiTinol wire has high temperature about 80°C±10°C. Full annealing of NiTinol wire was employed with a straight shape, this alloy it consists of (Ni-55%, H-0.001%, O-0.05%, N-0.001%, C-0.05% and Ti-Balance). In this research, a NiTinol wire was implemented (2 mm diameter) and (100 mm length). The experimental results and ANSYS software were almost near. Shape memory effect data constants used in ANSYS software were extracted from the experimental test by applying linear interpolation. These data were hardening parameter (C1) about 900 MPa and elastic limit (C3) about 30 MPa. These data were temperature scaling parameter C4=0.89, maximum transformation strain C5=0.074%, martensite modulus C6=20000 MPa and dependency parameter C7=0. The amount of strain (7 %) applied in this test returned to zero after activation NiTinol wire, and that gives an indication that the permanent deformation is decline. The start austenite temperature (As) was about 58°C±2℃ and finish austenite temperature (Af) was about 70°C±2℃. ANSYS software provided good results when compared with the experimental work.

Listing 1 - 4 of 4
Sort by
Narrow your search

Resource type

article (4)


Language

English (3)

Arabic and English (1)


Year
From To Submit

2019 (1)

2018 (1)

2016 (1)

2015 (1)