Article
High Temperature Behavior of Yttrium – Doped Siliconized 316L Stainless Steel at CO2 Environment
سلوك الصلب المقاوم للصدأ (316L) المطلي بالسليكون المدعم باليتريوم عند الدرجات الحرارية العالية في وسط CO2

Author: Rajab Mohammed Hussein رجب محمد حسين
Journal: Anbar Journal of Engineering Sciences مجلة الأنبار للعلوم الهندسية ISSN: 19979428 Year: 2009 Volume: 2 Issue: 1 Pages: 49-60
Publisher: University of Anbar جامعة الانبار

Loading...
Loading...
Abstract

In this study, silicon and yttrium were simultaneously co-deposited by diffusion into austenitic stainless steel (AISI 316L) substrates, by a single-step pack cementation process. Cyclic oxidation tests were conducted on the siliconized coating and on the yttrium doped siliconized coating of stainless steel in CO2 atmospheric pressure at temperatures 800° C and 900° C for 100h at 10h cyclic. The results show that the initial weight gain is rapid and increased as the temperature increased. The oxidation resistance of the yttrium doped siliconized of stainless steels was significantly improved as compared with the siliconized stainless steels. The scale formed on coated stainless steel after oxidation in CO2 environment was thick and consisted of Y2O3, SiO2, Fe2O3 and chromium oxide. Optical metallography (LOM) and X-ray diffraction (XRD) were used to characterize the resulting coating and cyclic oxidation structures.

في هذه الدراسة، تم طلاء الصلب الاوستنايتي المقاوم للصدأ (AISI 316L) بنوعين من الطلاء الانتشاري وهما الطلاء بالسليكون والطلاء بالسليكون المدعم باليتريوم باستخدام تقنية الطلاء الانتشاري بالسمنتة.جرت اختبارات التاكسد بشكل دوري للعينات المطلية في وسط ثاني اوكسيد الكاربون Co2 وعند درجات الحرارة 800 م و 900 م° لمدة 100 ساعة وبمعدل 10 ساعة للدورة الواحدة.وقد بينت النتائج بأن الزيادة في الوزن Weight gain كانت في البداية كبيرة وقد زادت بزيادة درجة الحرارة. وان مقاومة الاكسدة للصلب الاوستنايتي المطلي بالسلكون المدعم باليتريوم قد تحسنت مقارنة بطلاء السليكون لوحده. وان طبقة الاوكسيد (scale) المتكونة بعد الاكسدة في وسط Co2 للصلب المطلي كانت سميكة ومتكونة من الاطوار التالية FeO3, SiO2, Y2O3 واوكسيد الكروم.وقد استخدم في هذا البحث المجهر الضوئي (LOM) وجهاز حيود الاشعة السينية (XRD) لتحديد (structures) بعد الطلاء والاكسدة الدورية.


Article
Modeling of Oxidation Kinetics in Air of Steel-T21 Alloy Coated by Simultaneous Germanium-Doped Aluminizing-Silicon zing Process
نمذجة حركيات الأكسدة في الهواء للفولاذ نوع T21 المغلّف باستخدام طريقة الألمنة-سلكنة الآنية المحورة بالجرمانيوم

Author: Abbas Kh.Hussein عباس خماس
Journal: AL-NAHRAIN JOURNAL FOR ENGINEERING SCIENCES مجلة النهرين للعلوم الهندسية ISSN: 25219154 / eISSN 25219162 Year: 2008 Volume: 11 Issue: 3 Pages: 438-449
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

This work includes the application of a pack cementation of germanium-doped aluminum and silicon coatings on low alloy steel type-T21 yields a significant improvement in the oxidation. Steel-T21 was coated with germanium-doped aluminzing-siliconizing. Diffusion coating was carried out at 1050 oC for 6 h under an Ar atmosphere by simultaneous germanium-dopded aluminizing-siliconizing process. Cyclic oxidation tests were conducted on the coated steel-T21 alloy in the temperature range oxide 600-800 oC in air for 30 h at 5 h cycle. The results showed that the oxidation kinetics for coated system in air was found to be parabolic .Oxide phases that formed on coated system are SiO2 and Cr2O3..Mthamatical model using MATLAB show that there is multiple linear model for oxidation kinetics.

يتضمن هذا البحث استخدام طريقة التغليف بالسمنتة للحصول على تغطيات الألمنيوم-سليكون المحورة بالجرمانيوم على الفولاذ المنخفض السبائكية نوع T21 التي تؤدي الى تحسن كبير في الأكسدة.حيث أن الفولاذ قد خضع الى التغطية باستخدام عملية الألمنة-سلكنة المحورة بالجرمانيوم.تم تنفيذ الطلاء الانتشاري عند درجة 1050oC و لمدة 6 ساعة تحت أجواء الآركون باستخدام طريقة الألمنة –سلكنة الآنية المحورة بالجرمانيوم . اختبارات الأكسدة الدورية قد أنجزت على الفولاذ في المدى الحراري 600-800oC في الهواء لمدة 5 ساعة. أظهرت النتائج أن حركيات الأكسدة لنظام الطلاء في الهواء كانت من نوع القطع المكافئ . أما أطوار الأكسدة التي تكونت على أنظمة الطلاء فانها كانت SiO2 , Cr2O3 . أما النموذج الرياضي لحركيات الأكسدة باستخدام الماتلاب فانه كان من النوع الخطي المتعدد المتغيرات


Article
Finite Element Analysis Using MATLAB of Oxidation Properties in H2O Vapor of Steel-T22 Alloy Coated by Simultaneous Y-Doped Chromizing-Siliconizing Process
تحليل العناصر المحددة باستخدم الماتلاب لخواص الأكسدة في بخار الماء للفولاذ T22 المطلي بالكرمنة-السلكنة الآنية المحورة باليتيريوم

Authors: Sabah Kh.Hussein --- Abbas Kh.Husssein --- Kadhim K.Resin
Journal: AL-NAHRAIN JOURNAL FOR ENGINEERING SCIENCES مجلة النهرين للعلوم الهندسية ISSN: 25219154 / eISSN 25219162 Year: 2008 Volume: 11 Issue: 3 Pages: 450-458
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

The application of a pack cementation of Y-doped chromium and silicon coatings on low alloy steel type-T22 yields a significant improvement in the oxidation resistance. Steel-T22 was coated with Y-doped chromizing-siliconizing. Diffusion coating was carried out at 1050 oC for 6 h under an Ar atmosphere by simultaneous Y-dopded chromizing-siliconizing process. Cyclic oxidation tests were conducted on the coated steel-T22 alloy in the temperature range 300-500 oC in H2O for 100 h at 5 h cycle. . The oxidation kinetics for coated system in H2O was found to be parabolic .Oxide phases that formed on coated system are SiO2 and Cr2O3. Finite element results show that there is a good agreement between FEM and experiments results.

ان تطبيق طريقة التغليف بالسمنتة لتغطيات الكروم-السليكون المحورة باليتيريوم على الفولاذ المنخفض السبائكية نوع T22 يؤدي الى تحسين كبير في مقاومة الأكسدة. حيث أن الفولاذ T22 قد خضع الى طلاء كروم-سليكون المحوّر باليتيريوم . و تم تنفيذ الطلاء الانتشاري عند (1050oC) و لمدة 6 ساعة تحت أجواء الآركون باستخدام الطلاء الآني للكروم-سليكون المحور بالتيريوم. و تم اجراء اختبارات الأكسدة الدورية على الفولاذ المطلي في المدى الحراري (300-500) في بخار الماء و لمدة 100 ساعة عند دورة مقدارها 5 ساعة. و لوحظ أن آليات الأكسدة تسلك سلوك القطع المكافئ . اما أطوار الأكسدة فانها تتضمن تكوّن SiO2 و Cr2O3 . نتائج تحليل العناصر المحددة تشير الى التطابق مع النتائج التجريبية.


Article
Optimization of Cyclic Oxidation Parameters in Steel-T21 for Aluminization Coating Using Taguchi-ANOVA analysis by MINITAB13
تحديد عوامل الأكسدة الدورية المثلى لطلاء الألمنة في الفولاذ نوع- T21 باستخدام تحليل Taguchi-ANOVA بواسطة MINITAB13

Author: Abbas Khammas Hussein
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 12 Pages: 2367-2384
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The increasing demands for high quality coatings has made it inevitable thatthe surface coating industry would put more effort into precisely controlling thecoating process relative to media for which is subjected. Statistical design ofexperiments is an effective method for finding the optimum cyclic oxidationparameters for aluminization coating. In the present investigation, an attempt is madeto produce high-quality aluminization coating by optimizing the cyclic oxidationparameters following a (L9-33) Taguchi-design approach. (L9-33) Taguchi orthogonalarray has been used to determine the signal to noise ratio (S/N). The oxidationparameters that were varied include the Temperature (600,700,800oC), Time(15,20,25hr at 5hr cycle) and Media (Air,CO2,H2O). The coating characteristics werequalitified with respect to parabolic oxidation rate constant (KP). The performance ofthe coating was qualitatively evaluated using cyclic oxidation testing. Analysis of theexperiments using Taguchi method indicated that 800oC,25hr and CO2 media are to bethe optimum cyclic oxidation conditions for pack aluminization. The contribution ofeach of these parameters to the parabolic oxidation rate constant (KP) was determinedemploying an analysis of variance (ANOVA) and the effect of the level of eachparameter was determined using Taguchi analysis. ANOVA results show thattemperature and media are the parameters that most significantly affect the parabolicoxidation rate constant (KP) compared to time.

ان الطلب المتزايد حول الطلاء ذي النوعية العالية قد جعل صناعة الطلاء السطحي تبذل الجهودمن أجل السيطرة على الطلاء بشكل دقيق نسبة الى الوسط الذي تتع  رض له. يعتبر التصميمالاحصائي للتجارب طريقة ف  عالة لايجاد عوامل الأكسدة الدورية المثلى لطلاء الألمنة. في هذا البحث،تم الحصول على طلاء الألمنة ذات النوعية العالية من خلال تحديد عوامل الأكسدة الدورية المثلىقد تم استخدامها لتحديد (L9-33) Taguchi ان مصفوفة . (L9-33) Taguchi طبقا لطريقة تصميمان معاملات الأكسد التي خضعت الى التغيير تتضمن، درجة . (S/N) نسبة الاشارة/الضوضاءان . (Air,CO2,H2O) 15,20,25 ) و الوسط hr at 5hr cycle) 600,700,800 ) ، الزمن oC) الحرارةو تم تقييم . (KP) خصائص نوعية الطلاء قد تم تحديدها نسبة الى ثابت معدل أكسدة القطع المكافئأداء الطلاء من خلال اختبارات الأكسدة الدورية. أظهرت نتائج تحليل التجارب باستخدام طريقة800 ) . ان oC,25hr , CO أن عوامل الأكسدة الدورية المثلى لطلاء الألمنة هي: ( 2 ، Taguchiقد تم تحديده باستخدام تحليل (KP) مساهمة تأثير كل عامل على ثابت معدل أكسدة القطع المكافئ. Taguchi و تأثير كل مستوي من هذه العوامل قد تم تحديده باستخدام تحليل (ANOVA) المتغيربأن كل من درجة الحرارة و الوسط كان لها الأثر الأكبر على قيمة ثابت (ANOVA) أظهرت نتائجمقارنة مع الزمن. (KP) معدل أكسدة القطع المكافئ


Article
Oxidation of Simple and Pt-Modified Diffusion Coating on Inconel Alloy 600 in Air
أكسدة سبائك انكونيل - 600 المحورة بالطلاء الأنتشاري الالمنه - بلاتين

Authors: Ahmed Ali Moosa --- Hussein Al-Alqawie --- Khalil Al-Hatab
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2005 Volume: 24 Issue: 7 Pages: 909-922
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract


Article
High Temperature Cyclic Oxidation of Yttrium Modified Aluminide Diffusion Coatings of Stainless Steel
الاكسدة الدورية عند الدرجات الحرارية العالية للصلب المقاوم للصدا المطلي بالالمنيوم المدعم باليتريوم

Author: Rajab Mohammed Hussein رجب محمد حسين
Journal: Anbar Journal of Engineering Sciences مجلة الأنبار للعلوم الهندسية ISSN: 19979428 Year: 2009 Volume: 2 Issue: 1 Pages: 61-70
Publisher: University of Anbar جامعة الانبار

Loading...
Loading...
Abstract

In this study, yttrium and aluminum were simultaneously co-deposited by diffusion into austenitic stainless steel (AISI 316L) substrates, by a single-step pack cementation process. Cyclic oxidation tests were conducted on the aluminide coating and on the yttrium modified aluminide coating of stainless steel in air under atmospheric pressure at temperatures 700 C° and 800 C° for 100h at 10h cyclic.Optical metallography and X-ray diffraction (XRD) techniques were used to characterize the changes in scale morphology and to identify the phases and oxidation products. The yttrium modified aluminde coating showed very good cyclic oxidation resistance compared to aluminide coating

في هذه الدراسة، تم طلاء الصلب الاوستنايتي المقاوم للصدأ (AISI 316L) بنوعين من الطلاء الانتشاري هما الطلاء بالالمنيوم والطلاء بالالمنيوم المدعم باليتريوم باستخدام تقنية الطلاء الانتشاري بالسمنتة.جرت اختبارات التاكسد بشكل دوري للعينات المطلية في وسط الهواء عند الضغط الجوي وعند درجات الحرارة 700 م˚ و 800 م˚ لمدة 100 ساعة وبمعدل 10 ساعة للدورة الواحدة.تم استخدام المجهر الضوئي وجهاز حيود الاشعة السينية (XRD)، لدراسة سطح العينات وتحديد الاطوار بعد الطلاء والاكسدة الدورية.وقد اثبتت النتائج بان طلاء الالمنيوم المدعم باليتريوم للصلب الاوستنايتي له مقاومة عالية للاكسدة الدورية مقارنة بطلاء الالمنيوم لوحده.


Article
Oxidation Properties of Steel-T22 Alloy Coated by Simultaneous Ge-Doped 699 Chromizing-Siliconizing Process

Author: Ahmed A. Moosa
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2008 Volume: 26 Issue: 6 Pages: 699-709
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Diffusion coating was carried out at 1050 oC for 6 h under argon atmosphere bysimultaneous Ge-doped chromizing-siliconizing process on low alloy steel type-T22.Cyclic oxidation tests were conducted for the uncoated and for the chromizing –Siliconizing coated steel-T22 alloy at 800 oC . For the Ge-dopded chromizingsiliconizingcoated steel, the cyclic oxidation was carried out in the temperature range600-800 oC in air for 100 h at 5 h cycle. The results showed that the oxidation kineticsfor uncoated steel-T22 alloy in air at 800 oC follow a breakaway oxidation and thephases present are FeO (Wustite), Fe3O4 (Magnetite) and Fe2O3 (Haematite).The oxidation kinetics for chromizing –Siliconizing coated system in air at 800 oCwas found to be parabolic. Oxide phases that formed on coated system are SiO2 andCr2O3. The oxidation kinetics Ge-doped chromizing –Siliconizing coated system in air inthe temperature range 600-800 oC was found to be parabolic .Oxide phases that formedon coated system are SiO2 and Cr2O3. The Ge addition improves the oxidation resistanceof low alloy steel.

1050 ولمدة 6 ساعة في جو من oC في هذا البحث تم اجراء الطلاء الانتشاري في درجة حرارةغاز الاركون بااستخدام نظام الجرمانيوم –الكروم –السليكون لسبيكة الفولاذ المنخفض السبائكية نوععلى سبيكة الفولاذ (Cyclic Oxidation ) اجريت اختبارات الاكسدة بشكل دوري . T22وانظمة الطلاء النوع الاول سبيكة الفولاذ المنخفض السبائكية نوع T المنخفض السبائكية نوع 22ونظام الطلاء النوع الثاني سبيكة ( chromizing –Siliconizing) سليكون- كروم / T22(Ge-doped chromizing –. سليكون- كروم – جرمانيوم / T الفولاذ المنخفض السبائكية 22600-800 لمدة 100 ساعة بمعدل 5 ساعة للدوره oC في الهواء بدرجة حرارة Siliconizing)الواحدة.بدون طلاء يتبع T اظهرت النتائج ان سلوك التاكسد لنظام سبيكة الفولاذ المنخفض السبائكية نوع 22وان الاطوار المتكونة هي : (breakaway oxidation ) التاكسد الانفصاليFeO, Fe3O4 and Fe2O3.سليكون- كروم / T ان سلوك التاكسد لنظام النوع الاول سبيكة الفولاذ المنخفض السبائكية نوع 22ونظام الطلاء النوع الثاني سبيكة الفولاذ المنخفض السبائكية ( chromizing –Siliconizing)هو قطع (Ge-doped chromizing –Siliconizing) . سليكون- كروم – جرمانيوم / T22. SiO2 and Cr2O 600- في الهواء وان الاطوار المتكونه هي 3 800 oC المكافيء في درجة حرارة. T ان اضافة الجرمانيوم يؤدي الى تحسين سلوك التاكسد لسبيكة الفولاذ المنخفض السبائكية 22


Article
Isothermal Oxidation of Simple and Pt-Modified Diffusion Coating on Inconel Alloy 600 In Water Vapor
اكسدة سبائك الانكونيل – بلاتينيوم – الالمنيوم تحت ظروف بخار الماء

Authors: Al- Hatab, Khalil --- Al- Alqawie, Hussein --- Moosa, Ahmed Ali
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 2 Pages: 288-299
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this work the oxidation behavior of both inconel alloy 600 and coated system(Pt-modified aluminide coating) was investigated in pure water vapor H2O in thetemperature range 700 - 900 ºC. The platinum was deposited by electrochemicalmethod. Pt-modified aluminide coating was applied to inconel alloy 600 by using singlestephigh activity pack cementation method. The weight gain measurements indicatethat the oxidation kinetic is parabolic for uncoated and coated alloy. At temperaturesbelow 900 ºC the inconel alloy 600 is less aggravated in water vapor environmentsbecause it is a chromia former alloy. At 700 ºC, water vapor does not have a significanteffect on the spalling of oxide scales. At 900 ºC, water vapor causes spalling of theoxide scales during isothermal oxidation of inconel alloy 600. Therefore, it is concludedthat this alloy should not be used above 900 ºC in water vapor environments. Largevoids were found at the oxide scales-substrate interface and at grains or at grainboundaries due to the chromium outward diffusion toward the oxide scales.At 900 ºC, the parabolic rate constant (kp) of the coated system was one order ofmagnitude lower than that for the uncoated alloy. It was concluded that, water vaporexhibit little effect on the Pt-modified aluminide coating. Oxide phases that formed oncoated system are: Al2O3, NiAl2O4, Cr2O3, and NiFe2O4.

ذات (inconel سبيكة انكونل 600 ) Superalloys تم دراسة سلوك الأكسدة للسبائك الفائقة المؤلف من Coating System بالاضافة الى سلوك التأكسد لنظام الطلاء Ni الأساس من النيكل تم ترسيبها بتقنية Pt –Layer و طبقة من البلاتين substrate سبيكة الانكونل 600 كأساس ثم عوملت بالانتشار الحراري ليتم أخيرا ترسيب الألومنيوم Electrochemical الطلاء الكهروكيميائي تم دراسة سلوك الأكسدة . Pack Cementation Technique عليها باستخدام تقنية الطلاء بالسمنتةتشير نتائج .º 700 م - عند درجات حرارة هي 900 ، H2O للأنظمة أعلاه في وسط و بخار الماء الدراسة الحالية الى أن السلوك الكيناتيكي العام للتأكسد لسبيكة الانكونل 600 (الغير المطلية والمطلية) وجد أن بخار الماء ليس ،º عند درجة حرارة 700 م . Parabolic kP يتبع تقريبا قانون القطع المكافئيشير ذلك الى صعوبة استخدام هذه º له تأثير يذكر على تشظية الأكاسيد . عند درجة حرارة 900 م .º السبيكة في هذه الأوساط في درجة حرارة أعلى من 900 مللسبيكة المطلية اقل بمرتبة عشرية واحدة º عند درجة حرارة 900 م kp أن قيمة ثابت معدل التأكسد للسبيكة غير المطلية . تشير النتائج الى تكون فجوات كبيرة عند kp من قيمة ثابت معدل التأكسد طبقة ألاوكسيد/ الارضية وذلك بسبب عملية الانتشار لعناصر السبيكة كالكروم. تشير نتائج التحليلبالأشعة السينية للسبيكة المطلية ظهور أكاسيد الكروم و النيكل اضافة الى أكسيد الألومنيوم كما يلي .NiAl2O4, Cr2O3 , Al2O3 ,NiFe2O4


Article
Effect of Pack Cementation Coating on Hot Corrosion Resistance of Low Alloy Steel
تأثيرالطلاء بالسمتنة على مقاومة التأكل الحار لفولاذ منخفض السبائكية

Authors: Jawad Badr Gatea --- Muna khedier Abbass
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 2 Pages: 332-346
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Two technique of coatings were performed by applying pack cementationtechnology, the first one was aluminizing diffusion coated low alloy steel substratewhereas the second one was single step simultaneous Co-deposition silicon- aluminumdiffusion coated low alloy steel substrate. The pack mixture used for producing bothcoating systems in pack cementation process was composed of (30% Al, 2% NH4Cl andthe filler 68% Al2O3) , (30% Al , 5% Si , 2% NH4Cl and 63% Al2O3 ) respectively. Thepack temperature was 1000◦C and the diffusion time was 3 hr. XRD exhibits the phasesformed on both coated systems are Fe2Al5 , FeAl3 and FeSi . Uncoated low alloy steelsubstrate and the both two coating systems were subjected to exposure environmentdeposit salts mixture of (50%Na2SO4 and 50%NaCl) with weight (2mg /cm2), usingcyclic oxidation method in the experiments at temperature of 750◦C for 100hr eachcycle of 5hr. It was found that the oxidation kinetic for uncoated low alloy steel will giveevidence that the oxides formed on this alloy are non – protective. The XRD analysisexhibited the phases are Fe2O3 , Fe3O4. It was found they followed linear rate law, andspalling was observed. After these hot corrosion tests were undertaken, It was found thatthe oxidation kinetics for both coated systems in environment consist of salt mixture(50% NaCl +50% Na2SO4) followed parabolic law (protective oxidation behavior). XRDexhibits the oxides formed on both coated systems are Al2O3, SiO2.

تم تنفيذ نظامين طلاء الأول طلأء الألمنة الأنتشاري والنظام الثاني طلأء الأ لمنة - السلكنةالأنتشلري في خطوة واحدة وهو عبارة عن ترسيب الألمنيوم والسيلكون على سطح الفولاذ في زمن68% Al2O3 , 2% NH4Cl , 30% Al, ) واحد. وتم أستعمال خليط مسحوق السمنتة من المواد63% ) عند ترسيب الألمنيوم , الألمنيوم Al2O3 , 2% NH4Cl , 5% Si , 30% Al ) ) و والسيلكون على ا لتوالي, وأجريت عملية الطلاء في أجواء معزولة عن الهواء ( غاز الاركون ) في ( XRD ) لمدة زمنية 3 ساعة . وكانت نتائج الفحص بحيود الأشعة السينية ◦ درجة حرارة 1000 م في كلا نظامي الطلاء. و تم أجراء أختبارات Fe2Al5 , FeAl3 , FeSi تشير الى نكون الأطوار التأكل الحار الدوري لسبيكة الفولاذ منخفض السبائكية الغير المطلية والمطلية . وتم أكسدة العينات الغير ( 50% ) بوزن ( 2 ملغم / سم 2 Na2SO4 +50%NaCl ) المطلية و المطلية بطبقة ملحية من خليط لفترة ◦ في درجة حرارة 750 مزمنية 100 ساعة وبمعدل 5 ساعة لكل دورة. وكانت نتائج أختبارات الأكسدة على العينات الغير Fe2O3 , Fe3O المطلية هي تكون أكاسيد غير واقية على سطح الفولاذ . وان الأكاسيد السائدة هي 4 وقد أظهرت النتائج بأن العينات الغير .( XRD ) كما اثبتتها نتائج الفحص بحيود الأشعة السينية المطلية ذات سلوك كاينتيكي يتبع القانون الخطي ويحصل تقشر في الأكاسيد . اما أختبارات التأكل الحار على العينات المطلية في ك لا نظامي الطلاء فقد أظهرت النتائج ان السلوك الكاين تيكي العام يخضع الى . Al2O3, SiO قانون القطع المكافئ ( سلوك الأكسدة الواقية ). وأن الأكاسيد المتكونة هي 2


Article
Taguchi Approach to Optimize Pack Aluminization Parameters in Carbon Steel Using MINITAB13
استخدام طریقة تاكوجي لتحدید العوامل المثلى في عملیة الطلاء بالألمنة في الفولاذ الكاربوني بواسطة MINITAB 13

Author: Abbas Khammas Hussein
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 11 Pages: 2259-2272
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Pack aluminization has been rapidly developed and widely used in many fieldsdue to its superior properties of coating. Surface is the only part of the componentwhich has to coexist with external environment. Majority of engineering failuresoriginate from the surfaces and components degrade in service leading to failures suchas fatigue, wear, corrosion and oxidation. The present study deals with the surfacemodification of steel base through diffusion of aluminium by aluminium packcementation for improving wear and corrosion resistance. The material chosen forstudy is medium carbon steel. Effect of varying weight percentage (wt.%) of halideactivator (NH4Cl) at different diffusion temperatures and times on the microstructureand microhardness of aluminized specimens was studied. Taguchi robust designtechnique using MINITAB13 was used to rank several factors that may affect themicrohardness and microstructure in order to formulate the optimum conditions. TheTaguchi orthogonal array L9 (33) was used for experimental design with three level ofconsideration for each factor. The respone (Microhardness) was analyzed based on theTaguchi’s signal-to-noise ratio. The use of 4%wt. of (NH4Cl) at 5hr and diffusiontemperature of 700oC seems to be the optimum condition, where the surface hardnesscould be increased to 1000Hv when aluminized. X-Ray diffraction studies have beenconfirmed the presence of aluminides in the surface layer, which could be instrumentalin the significant increase in the surface hardness.

ان طريقة الطلاء بالألمنة قد تطورت بشكل سريع و استخدمت بصورة واسعة في العديد من المجالات نتيجة خواص الطلاء الفائقة. و يعتبر السطح الجزء الوحيد من المنتج الذي يتعرض بشكل مباشر الى الوسط الخارجي. ان أغلب حالات الفشل الهندسي تنشأ من السطح و تؤدي الى فشل الجزء الهندسي في التطبيق مثل الفشل بالكلال ، البلى، التآكل و الأكسدة. يتضمن هذا البحث، تحوير سطح الفولاذ من خلال انتشار الألمنيوم بواسطة التغليف بالسمنتة للألمنيوم و ذلك لتحسين مقاومةالبلى و التآكل. ان المادة التي تم اختيارها في هذه الدراسة هي الفولاذ المتوسط الكاربون. وقد تم في عند درجات (NH4Cl) هذا البحث دراسة تأثير النسب المئوية الوزنية المختلفة لهاليد المادة الفعالة حرارية و أوقات مختلفة على التركيب المجهري و الصلادة المجهرية للعينات الخاضعة لعمليةلتحديد العوامل التي يمكن أن MINITAB الألمنة. تم استخدام طريقة التصميم لتاكوجي بواسطة 13 تؤّثر على الصلادة المجهرية و التركيب المجهري و من ثم تحديد الظروف المثلى. مصفوفة تاكوجي قد تم اعتمادها في تصميم التجارب نظرا لاستخدام ثلاث مستويات لكل عامل تحت L9( من نوع ( 33 الدراسة. كما تم تحليل الاستجابة ( الصلادة المجهرية) من خلال الاعتماد على نسبة عند زمن مقداره 5 NH4Cl 4% من wt. الاشارة/الاستجابة لتاكوجي. أظهرت النتائج أن استخدام700 يؤدي الى الحصول على الحالة المثلى ضمن مجموعة oC ساعة و درجة حرارة مقدارها 1000Hv الظروف التي أُستخدمت في هذا البحث حيث أن الصلادة السطحسية يمكن أن تزداد الى عندما يخصع الفولاذ الى الألمنة. أظهرت دراسات حيود الأشعة السينية وجود مركبات في السطح و التي يمكن أن تلعب دورا فعالا في الزيادة الكبيرة في الصلادة السطحية. Aluminides

Listing 1 - 10 of 15 << page
of 2
>>
Sort by
Narrow your search

Resource type

article (15)


Language

English (12)

Arabic and English (2)

Arabic (1)


Year
From To Submit

2015 (1)

2014 (1)

2013 (2)

2012 (1)

2009 (6)

More...