Article
Calculation the mass attenuation coefficient of beta-particles through Polyvinyl chloride
حساب معامل التوهين الكتلي لجسيمات بيتا خلال بولي كلوريد الفاينيل

Authors: Harith I. Jaafer حارث ابراهيم جعفر --- Ban M. Alshabander بان مازن مزاحم الشابندر
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2010 Volume: 8 Issue: 12 Pages: 50-53
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The mass attenuation coefficient for beta particles through pure Polyvinyl chloride (PVC) and flax fibers- reinforced PVC composite were investigated as a function of the absorber thickness and the absorber to source distance. The beta particles mass attenuation coefficients were obtained using a NaI(Tl) energy selective scintillation counter with 90Sr/ 90Y beta source having an energy range from (0.546-2.275) MeV. Pure PVC polymer samples were prepared by compacting the PVC powder in a mould at high pressure (10bar) and temperature about 140°C for 30 minutes. A hot press system was used for this process. The experimentally obtained values of mass attenuation coefficients for 90Sr and 90Y were found to be 7.72 cm2.g-1and 0.842 cm2.g-1 respectively, and the measured mass attenuation coefficients values decrease with increase of the absorber to source distance .

تمت دراسه معامل التوهين الكتلي لجسيمات بيتا خلال عينات من مادة بولي كلوريد الفاينيل (PVC) ومتراكب الياف الكتان المدعمة بــ (PVC) كدالة لسمك المادة الماصة وللمسافة بين المادة الماصة والمصدر المشع. تم قياس معامل التوهين الكتلي لجسيمات بيتا باستخدام منظومة الكاشف الوميضي NaI(Tl) مع مصدر أشعة بيتا 90Sr/90Y بمدى طاقة تتراوح بين (0.546-2.75) ميكا الكترون فولت. حضرت عينات (PVC) النقي عن طريق كبس مسحوق الـ (PVC) في قالب معدني تحت ضغط عالي مقداره 10 بار وبدرجة حرارة 140 درجة مئوية ولمدة 30 دقيقة ولقد استخدمت منظومه الكبس الحراري لهذا الغرض. وجد ان القيم العملية المستحصلة لمعامل التوهـين الكتلي لـ 90Sr و 90Y هي 7.72 cm-2.g-1 و 0.842 cm-2.g-1 على التوالي. وان قيم معاملات التوهين الكتلي تتناقص مع زيادة المسافة بين المادة الماصة والمصدر.


Article
The mechanical behavior of thermoplastic and thermosetting polymers in different aqueous environments
السلوك الميكانيكي لبوليمر مطاوع وآخر متصلد حراريا في بيئات مائية مختلفة

Author: Awham M. Hameed
Journal: Journal of College of Education مجلة كلية التربية ISSN: 18120380 Year: 2012 Issue: 1 Pages: 483-497
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

The current investigation is interested by study the effect of some types of water (sea, river and rain) on the mechanical behavior for two polymeric materials (Epoxy resin (EP) and Polyvinyl Chloride (PVC) type U(Un plasticized PVC), the prepared specimens of two materials were tested under impact and bending loads at room temperature. The results showed that U-PVC has the higher impact strength comparing with (EP) resin before and after the immersion into three types of water for 4 weeks. The bending test results showed that the maximum deflection exhibits for both materials at the first stage of immersion except (U-PVC) sample which immersed in rain water, the maximum deflection exhibits in it after 2 weeks of immersion.The Young's modulus values vary (increase and decrease) for both materials under work depending on the nature of water, immersion time, the penetration amount of it into the structure of material as well as the plasticization case which causes it.

اهتم بحثنا الحالي بدراسة تأثير بعض انواع المياه التي شملت (ماء البحر, ماء النهر , ماء المطر) على السلوك الميكانيكي لمادتين بوليمريتين احدهما مطاوعة للحرارة وهي بولي كلوريد الفاينيل PVC نوع (U والاخرى متصلدة حراريا وهي (راتنج الايبوكسي EP) وبعد تحضير النماذج لكلا المادتين, جرى اختبارهما تحت تأثير حملي (الصدمة والانحناء) قبل وبعد غمرهما في المياه المذكورة اعلاه وقد تم ذلك عند درجة حرارة الغرفة.اظهرت النتائج ان مادة ((U-PVC لها مقاومة صدمة اعلى مقارنة براتنج الايبوكسي(Epoxy resin) وذلك في حالتي قبل وبعد الغمر في انواع المياه الثلاثة ولمدة اربعة اسابيع.اما نتائج اختبار الانحناء فقد بينت بان اقصى انحراف (maximum deflection) يظهر لكلا المادتين بعد الفترة الاولى من الغمر ((1week ما عدا نموذج ((U-PVC المغمور في ماء المطر الذي يحدث فيه اقصى انحراف بعد مدة اسبوعين من الغمر.اما قيم معامل المرونة (معامل يونك) فتتغير صعودا ونزولا لكلا المادتين قيد الدراسة وذلك حسب طبيعة الماء وفترة الغمرفيه ومقدار تغلغله الى داخل تركيب المادة علاوة على حالة التلدن التي يسببها للبوليمر.


Article
PREPARATION OF PVC HOLLOW FIBER MEMBRANE USING (DMAC/ACETONE)

Loading...
Loading...
Abstract

Membrane manufacturing system was operated using dry/wet phase inversion process. A sample of hollow fiber membrane was prepared using (17% wt PVC) polyvinyl chloride as membrane material and N, N Dimethylacetamide (DMAC) as solvent in the first run and the second run was made using (DMAC/Acetone) of ratio 3.4 w/w. Scanning electron microscope (SEM) was used to predict the structure and dimensions of hollow fiber membranes prepared. The ultrafiltration experiments were performed using soluble polymeric solute poly ethylene glycol (PEG) of molecular weight (20000 Dalton) 800 ppm solution 25 °C temperature and 1 bar pressure. The experimental results show that pure water permeation increased from 25.7 to 32.2 (L/m2.h.bar) by adding acetone to the dope solution, while rejection decreased from 91.8 to 63.2%.


Article
Optical Properties of Polymer polyvinyl chloride (PVC) doped with DCM Laser-Dye and Tio2 Thin Film

Authors: Shatha Raheem Helal Alhimidi --- Thill A. Kadhum Al-musawi
Journal: Journal of Education for Pure Science مجلة التربية للعلوم الصرفة ISSN: 20736592 Year: 2018 Volume: 8 Issue: 1 Pages: 197-206
Publisher: Thi-Qar University جامعة ذي قار

Loading...
Loading...
Abstract

Abstract:polyvinyl chlorideis blended with DCM laser dye co-doped with TiO2 nanoparticle. The thin filmswere prepared by using casting method.The optical properties such as absorbance, absorptioncoefficient, refraction index and the optical conductivity of the prepared thin film have been studiedat (30oC).It has been shown from the results that allowed direct electronic transitions energy gapis(1.7eV),while allowed indirect electronic transition energy gap is(1.6 eV).

الخلاصة:اللیزریة ومع جسیمات ثاني اوكسید التیتانیوم (DCM) مع صبغة (PVC ) في ھذه الدراسة تم مزج بولیمر بولي كلورید الفینیلالنانویة، وحضّرت الاغشیة باستعمال طریقة الصب. درست الخواص البصریة كالامتصاصیة، ومعامل الامتصاص، (TiO2)300 ). تبیّن من النتائج ان قیمة فجوة C ومعامل الانكسار، والتوصیلیة البصریة للأغشیة الرقیقة المحضرة عند درجة حرارة ( 0.(1.6 eV) 1.7 )، بینما فجوة الطاقة غیر المباشرة فتساوي eV) الطاقة المسموحة المباشرة ھي


Article
The Effect of Shear on the Properties of Rigid PVC
تأثير قوى القص على خواص مادة متعدد (كلورايد الفاينيل) الصلب

Author: Sawsan D. A. Shubbar سوسن ضياء احمد شبر
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2011 Volume: 17 Issue: 6 Pages: 1567-1575
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The rheological and fusion behavior of polyvinyl chloride (PVC) compounds plays a dominant role in the processing operations and in the development of physical properties in the processed material. A comprehensive study was made in this work to evaluate the effect of shear and thermal history on stability, mechanical and rheological properties of rigid PVC compounds. Different samples of Rigid Poly vinyl chloride including dry blend powder, granules, and bottles molded from both were examined. A study was also made on recycled RPVC where 25% of reclaimed material was continuously blended with fresh dry blend and processed for 15 cycles. Results showed that compaction of the PVC material took place in the brabender plastograph at constant temperature and shear stress. Correlations were given to explain results concerning residual stability and rheological behavior. Furthermore, it was seen that elongation and tensile impact are dependent on shear history

حيث ان لخواص الانصهار والانسياب لبوليمرات متعدد ( كلورايد الفاينيل) الصلب دورا حيويا في عمليات التصنيع وفي عمليات تطوير الخواص الفيزياوية للمنتج النهائي ؛ تمت اجراء دراسة شامله تناولت تاثير قوى القص والاجهاد الحراري المسبق على كل من الثبوتية وخواص الانسياب والخواص الميكانيكية لهذا البوليمر. شملت الدراسة اربع انواع من متعدد ( كلورايد الفاينيل) الصلب هي : مسحوق البوليمر الجاف ، حبيبات مصنعة من نفس المسحوق، وقناني مصنعه من كلا الفقرتين السابقتين. كذلك تمت دراسة تاثير رفع نسبة (المثروم البلاستيكي للقناني : نسبة المسحوق الجاف) الى 25% وذلك باعادة تدويره 15 دورة متتالية .اظهرت النتائج ان عملية الرص والانصهار للبوليمر حصلت في جهاز البرابندر بدرجة حراره واجهاد قص ثابتين. وكذلك تم اعطاء ارتباطات لتوضيح النتائج التي تتعلق بالاستقرارية وخواص الانسياب. علاوة على ذلك ، تبين ان الاستطالة والصدم تعتمد على قوى القص المسبقة.


Article
POLYVINYL ALCOHOL/POLYVINYL CHLORIDE (PVA/PVC) HOLLOW FIBER COMPOSITE NANOFILTRATION MEMBRANES FOR WATER TREATMENT

Authors: Sufyan Algebory --- A. Figoli --- Qusay Alsalhy --- Ghanim M. Alwan --- et al.
Journal: Iraqi Journal of Chemical and Petroleum Engineering المجلة العراقية للهندسة الكيمياوية وهندسة النفط ISSN: 19974884/E26180707 Year: 2010 Volume: 11 Issue: 4 Pages: 23-32
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Two different polyvinyl alcohol/polyvinyl chloride (PVA/PVC) hollow fiber composite nanofiltration membranes were prepared after PVC hollow fiber membranes were coated using dip-coating method with PVA aqueous solution, which was composed of PVA, fatty alcohol polyoxyethylene ether (AEO9), and water [PVA/AEO9/water (4:0.5:95.5) wt%]. Effect of two different PVC hollow fiber immersion times in coating solution were studied. Cross-section, internal and external surfaces of the PVC hollow fibers and PVA/PVC composite nanofiltration membranes structures were characterized by scanning electron microscopy (SEM), pure water permeation flux and solutes rejection. It was found that, the coating layer thickness on the outer surface of the 19 wt% PVC hollow fiber was thin and about (6µm), while the coating solution penetrates through the outer edge of the PVC hollow fiber and it looks like sponge-like structure with increase of the dip-coating time from 20 to 30 sec. Besides, the pure water permeation flux decreases and solutes rejection increases with an increase of the coating time from 20 to 30 sec for the two PVA/PVC composite nanofiltration membranes.Molecular weight cut-off (MWCO) of the PVA/PVC composite nanofiltration membranes were in the range of NF (i.e. 200-3000 Mw).

تم تحضير نوعين من اغشية الالياف المجوفة والنانوية المكونة من PVA/PVC بواسطة طريقة الاكساء بالتغطيس في محلول PVA المائي المكون من بولي فنيل الكحول PVA, الماء و(AEO9) Fatty Alcohol Polyoxyethylene Ether وبنسب وزنية مئوية(0.5, 95.5, 4) على التوالي.تم دراسة تاثير وقتين مختلفين لزمن اكساء اغشية الالياف المجوفة على التركيب الداخلي والخارجي لاغشية الياف PVA/PVC المركبة والنانوية باستخدام جهاز المجهر الالكتروني الماسح (SEM) وايضا على اداء الاغشية في فصل المذابات وانتاج الماء النقي. وجد ان سمك طبقة الاكساء للالياف المحضرة من19% PVC كان رقيقا وبسمك µm6بينما يدخل محلول الاكساء خلال السطح الخارجي ويسد التراكيب الاصبعية الشكل عندما يزداد زمن الاكساء من 20-30 ثانية. بالاضافة الى ذلك, تقل نفاذية الماء النقي ويزداد فصل المذابات بزيادة زمن الاكساء من 20-30 ثانية لكلا نوعي الالياف المجوفة النانوية. ان الوزن الجزيئي للمذابات المفصولة(MWCO) لاغشية اليافPVA/PVC المجوفة النانوية كان ضمن مدى اغشية الفصل النانوية (200- 3000Da ).


Article
The Effect of Gamma radiation on polyvinyl chloride
تأثير أشعة كاما على بولي فينيل كلورايد ونترات السليلوز

Author: H. A. Hussain and A. H. M. Al-Hashimi حسين علي حسين و علي حسين محمد الهاشمي
Journal: Journal of Basrah Researches (Sciences) مجلة ابحاث البصرة ( العلميات) ISSN: 18172695 Year: 2013 Volume: 39 Issue: 1A Pages: 112-124
Publisher: Basrah University جامعة البصرة

Loading...
Loading...
Abstract

Gamma rays effect has been worked out on polyvinyl chloride and CN-85, this effect has been found out and compared together, by using optical density technique, this work for this polyvinyl chloride, has been done for the first time.Polyvinyl chloride used in this work shows more response and more linearity than CN-85, in response to gamma photons within the dose range between 679mGy and 13582mGy.

تم قياس تأثير أشعة كاما على ( بولي فينيل كلورا يدPVC ، نترات السليلوز CN-85 ) تمت دراسة هذا التأثير ومقارنته باستخدام تقنية الكثافة الضوئية . قد تم استخدام هذا العمل لـ ( بولي فينيل كلورا يد ) لأول مرة .اظهر بولي فينيل كلورا يد المستخدم في هذا العمل ، أكثر استجابة وكان أكثر خطيا من نترات السليلوز، نتيجة التأثير فوتونات كاما المستخدمة في مدى الجرعات (679mGY-13582mGY ) .


Article
Studying the Electrical Conductivity of Different Carbon Fillers Reinforced Polyvinyl Chloride Composite Materials
دراسة التوصيلية الكهربائية للمواد المتراكبة البولي فينايل كلورايد المدعم بانواع مختلفة من حشوات الكاربون الموصلة

Authors: Nirvana A. Abed Al ameer نيرفانا عباس عبد الامير --- Walla W. Jameel ولاء وديع جميل
Journal: AL-NAHRAIN JOURNAL FOR ENGINEERING SCIENCES مجلة النهرين للعلوم الهندسية ISSN: 25219154 / eISSN 25219162 Year: 2013 Volume: 16 Issue: 2 Pages: 260-268
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

The aim of this study is development the electrical conductivity of composite materials which used three fillers of carbon reinforced PVC at different weight fractions. The experimental results showed that carbon black was more effective than carbon fiber and synthetic graphite at low weight fractions, it reached (0.229 S/cm) whereas it was (0.109 S/cm) and (0.104 S/cm) of each carbon fiber and synthetic graphite respectively. At (40%) weight fraction the electrical conductivity was increased to (0.216 S/cm) and (0.226 S/cm) of each carbon fiber and synthetic graphite while it was inattentive with carbon black. Hybrid composites were investigated also; the result appears that maximum value of the electrical conductivity at combination of (20%) weight fraction of fillers, it was (0.592 S/cm).

الهدف من الدراسة هو تطوير التوصيلية الكهربائية للمواد المتراكبة البولي فينايل كلورايد المدعم بحشوات مختلفة من الكاربون. النتائج المختبرية اظهرت ان الكاربون الاسود كان اكثر فعالية من الانواع الاخرى عند النسب الوزنيةالواطئة حيث وصلت الى(0.229S/cm) في حين كانت (0.109 S/cm) و(0.104S/cm) لكل من الياف الكاربون والكرافيت على التوالي. اما عند الكسور الوزنية العالية (40%) فان التوصيلية الكهربائية ازدادت الى (0.216S/cm) و (0.226S/cm) لكل من الياف الكاربون والكرافيت بينما كانت ضئيلة للكاربون الاسود. كذلك تم دراسة المواد المتراكبة الهجينة حيث اظهرت النتائج اعلى قيم لها عند دمج الحشوات بنفس الكسور الوزنية (20%) لكل حشوة , كانت (0.592S/cm) .


Article
Using the plastic wastes in fabrication of composite materials for different applications
استخدام النفايات البلاستيكية في تصنيع مواد متراكبة متعددة التطبيقات

Authors: Awham M. Hameed اوهام محمد حميد --- Ahmed Ali Talib احمد علي طالب
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2018 Volume: 16 Issue: 36 Pages: 123-133
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This study suggests using the recycled plastic waste to prepare the polymer matrix composite (PMCs) to use in different applications. Composite materials were prepared by mixing the polyester resin (UP) with plastic waste, two types of plastic waste were used in this work included polyethylene-terephthalate (PET) and Polyvinyl chloride (PVC) with varies weight fractions (0, 5, 10, 15, 20 and 25 %) added as a filler in flakes form. Charpy impact test was performed on the prepared samples to calculate the values of impact strength (I.S). Flexural and hardness tests were carried out to calculate the values of flexural strength and hardness. Acoustic insulation and optical microscope tests were carried out. In general, it is found that UP/PVC composite exhibit the optimum values compared to UP/PET composite in all properties under test. From the experimental results, it can be concluded that the prepared composites from the waste could be utilized as precast or partitions inside the buildings with improved mechanical properties.

يقترح هذا البحث اعادة التدوير للمخلفات البلاستيكية لغرض استعمالها في تصنيع متراكبات ذات اساسات بوليمرية (PMCs) من الممكن استخدامها في تطبيقات متعددة. حضرت المواد المتراكبة بخلط راتنج البولي استر غير المشبع مع المخلفات البلاستيكية وقد استخدم نوعين من المخلفات اضيفت كحشوة بشكل قشور في هذه الدراسة شملت البولي اثيلين ترفثاليت (PET) والبولي كلوريد الفاينيل ((PVC وبكسوروزنية مختلفة (0، 5، 10،15 ، 20 و (25%. نفذ اختبار صلادة نوع جاربي على النماذج المحضرة لتحديد قيم مقاومة الصدمة لها. كما اجري اختباري الانحناء والصلادة لتحديد قيم مقاومة الانحناء والصلادة. اختبار العزل الصوتي والفحص بالمجهر البصري تمت على النماذج القياسية. بشكل عام، وجد ان المتراكب المدعم بمخلفات الPVC يظهرقيم مثلى مقارنة بالمتراكب المدعم بمخلفات الPET في جميع الخواص قيد الدراسة. ومن النتائج التجريبية يمكن الاستنتاج بان المتراكبات المحضرة من التدعيم بالمخلفات يمكن استخدامها كمصبوبات اولية جاهزة أو كقوطع داخل المباني وبخواص ميكانيكية محسنة.


Article
Investigation of the External Loads Applied on the PVC and PE Pressurized Pipes
التحقيق في الأحمال الخارجية المسلطة على أنابيب البولي فينيل كلورايد والبولي ايثيلين المضغوط

Author: Humam Mohammed Salih همام محمد صالح
Journal: Al-Rafidain University College For Sciences مجلة كلية الرافدين الجامعة للعلوم ISSN: 16816870 Year: 2017 Issue: 39 Pages: 406-426
Publisher: Rafidain University College كلية الرافدين الجامعة

Loading...
Loading...
Abstract

The irrigation systems, water supply system, sewage water system ….etc. Dealing with many types of pipes and fittings depending on the applications. The current study was concert on test the polyethylene (PE) and polyvinyl chloride (PVC) pipes experimentally and theoretically under external loads and internal pressure to simulate the application conditions of pipes which are buried under ground used to transit the fluid under pressure such as drink water, sewage water or any other purpose and find out the deformation, stress and strain due to this loads. The tested was carried out for two size (actual and standard) of the two pipes (PE and PVC). The external load represented by a force in range (10-50KN), and the internal loads represented in pressure in range (5-20 bar). In the experiment a hydraulic press was used to supply the external load and hydraulic pump to supply the internal pressure with two adapter on the two end of tested pipe. The results showed that the deformation, stress and strain increase with increase in internal and external loads and the peak values of that were in the maximum internal and external loads (20 bar internal pressure and 50KN external force), also the experimental tests match the numerical calculation for both actual and standard size.

ركزت الدراسة الحالية على اختبار أنابيب البولي إثيلين (PE) والبولي فينيل كلورايد (PVC) عمليا ونظريا" تحت الأحمال الخارجية والضغوط الداخلية لمحاكاة ظروف تطبيق الأنابيب التي دفنت تحت الأرض المستخدمةلنقل السائل تحت الضغط مثل مياه الشرب، مياه الصرف الصحي أو لأي غرض آخر, ومعرفة التشوه، الاجهادواالانفعال بسبب هذه الأحمال. وأجريت الاختبار لحجمين (الحقيقي والقياسي) لنوعين من الأنابيب (PE وPVC). الحمل الخارجي ممثلة بقوة على مدى (10-50 كيلونيوتن)، والأحمال الداخلية ممثلة في الضغط على مدى (5-20 بار). الاختبار العملي كان باستخدام كابس يستخدم لتزويد الحمل الخارجي ومضخة هيدروليكية لتجهيز الضغط الداخلي مع اثنين من السدادات على نهايتي انبوب الاختبار. وأظهرت النتائج أن التشوه، الاجهاد والانفعال يزداد مع الزيادة في الأحمال الداخلية والخارجية و وبلغت القيم ذروتها عند أقصى حمل داخلي وخارجي (الضغط الداخلي 20 بار و القوة الخارجية 50كيلو نيوتن). وكان هنالك تقارب بين االاختبارات العملية والنظرية وكذلك بين الحجم الحقيقي والقياسي لنفس الانبوب

Listing 1 - 10 of 12 << page
of 2
>>
Sort by
Narrow your search

Resource type

article (12)


Language

English (11)

Arabic and English (1)


Year
From To Submit

2018 (3)

2017 (2)

2014 (1)

2013 (2)

2012 (1)