Article
Retarding of Precipitation Hardening of Al-Cu Alloy by Cadimium Addition
تأخیر عملیة التصلید بالترسیب لسبیكة (ألمنیوم – نحاس) بواسطة إضافة ألكادمیوم

Authors: Sabreen Ali --- Alaa A. Atiyah --- Amin D. Thamir
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 16 Part (A) Engineering Pages: 2997-3006
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The aim of the present work is to prepare a set of Al-Cu alloys with slowprecipitation hardening by aging. Present work results can be utilized during theimporting or exporting of such alloys at solution treatment conditions. In order toestablish this aim, a set of Al-4%Cu alloys have been prepared in the laboratory toinvestigate the effect of Cd-addition with the percentage varied from (0.1, 0.3 and0.5) weight percentage. The prepared alloys with different Cd additions weresubjected to a natural aging up to 60 days after solution treatment. As a result, thealloys showed an obvious retarding in the aging kinetics as the percentage of Cdadditionsincreasing. This retarding was found to be due to the trapping of thevacancies that resulted during the quenching step that resulted in delays of Gunier-Preston zones precipitation. SEM has been used in monitoring of microstructure aswell as optical microscopy


Article
The Influence of Quenching Media and Aging Time on Microstructure and Mechanical Behavior of 6061 Aluminum Alloy
تأثير أوساط الاخماد وزمن التعتيق على التركيب المجهري والسلوك الميكانيكي لسبائك المنيوم 6061

Author: Naser Korde Zedin
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 8 Part (A) Engineering Pages: 1757-1770
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Aluminum-magnesium-silicon (Al-Mg-Si) alloys are medium strength, excellent formability, good corrosion resistance and widely used in extruded products and automotive body materials. The influence of quenching media with different aging time on microstructure and mechanical properties of 6061 aluminum alloy was investigated. The results show formation of (Mg2Si) and (CuAl2) phaseswhensolution treatmentwas applied (at 520°C for 2h,followed by quenching in water and oil at room temperature then aging (at 175°C for 2, 4and6h)) which resultimprovingof both the strength, hardness and decreases elongation. It can be noted that, the grains of samples which are quenching in water is finer than the structure of samples which are quenching in oil. The values of yield stress and ultimate tensile strength decrease respectively with increasing aging time to 6h as (258MPa) and (264MPa) for water quenching and (199MPa) and (235MPa) for oil quenching. In this piper were measured and discussedthe variation of the yield stress, ultimate tensile strength and elongation with different solution quenching and aging time.

تمتاز سبائك (Al-Mg-Si) بمقاومتها المتوسطة وقابليتها العالية للتشكيل ومقاومتها الجيده للتاكل مما جعلها واسعة الانتشار في صناعة المبثوقات وهياكل وسائط النقل. في هذا البحث تم دراسة تأثير اختلاف أوساط الاخماد و زمن تعتيق على البنية المجهرية و الخواص الميكانيكية لسبائك المنيوم 6061. بينت النتائج تكون طوري Mg2Si و CuAl2عند اجراء المعالجة المحلولية (بدرجة حرارة 520مͦلمدة(2ساعة) والمتبوعة بالاخماد (مرة بالماء و مرة بالزيت) عند درجة حرارة الغرفة ثم التعتيق عند درجة حرارية 175 مͦلمدة (6,4,2ساعة) مما ينتج تحسين في كلاً من المقاومة و الصلادة وتنخفض المطيلية. كذلك نلاحظ ان البنية المجهرية للعينات التي يتم اخمادها بالماء اصغر من البنية المجهرية للعينات التي يتم اخمادها بالزيت. قيم اجهاد الخضوع ومقاومة الشد القصوى التي تم الحصول عليها تقل بزيادة زمن التعتيق الى 6 ساعة ,القيم بالتتابع (258 ميكا باسكال) و(264 ميكا باسكال) للاخماد بالماء و (199 ميكا باسكال) و(235 ميكا باسكال) للاخماد بالزيت. في هذا البحثتم قياس و دراسة التغيرات التي تحدث على المعادن بواسطة دراسة مقاومة الخضوع ومقاومة الشد والمطيلية مع اختلاف محاليل الاخماد و زمن التعتيق.


Article
Studying the dry sliding wear behavior of Al-4%Cu/ SiC Metal Matrix Composite with heat treatment
دراسة سلوك الانزلاق الجاف للمادة المركبة Al-4%Cu/ SiC والمعاملة حراريا

Loading...
Loading...
Abstract

In This study metal matrix composite (MMCs) was produced by using aluminum as base metal matrix reinforced with the SiC particulates using conventional casting technique, macro structural studies showed that uniform distribution of SiC particulates. The density of MMCs decreased with the increase in SiC wt%. The Hardness of MMCs increased with the increase in SiC wt%, composites exhibit a significant acceleration in kinetics of preciptation in compare with the unreinforced matrix alloy. A pin on disc wear testing machine was used to evaluated the wear loss of composites. The results showed that wear rates of composites are lower than of the matrix alloy and further decrease with increase in SiC particulate content.

في هذه الدراسة تم أستعمال معدن الالمنيوم كمادة أساس وحبيبات كاربيد السلكون كمادة تقوية وذلك بأستخدام تقنياتَ الصب التقليديةِ في انتاج المادة الاساس والمادة المدعمة، أظهرت نتائج الفحص العياني للتركيب بأنّ التوزيعِ الحبيبي لمادة التقوية وهي حبيبات كاربيد السلكون كانت منتظة أما كثافة المادة المدعمة فقد أنخفضت بزيادةِ نسبة حبيبات كاربيد السلكون المضافة. وبالنسبة للصلادة فهي زادت للمادة المركبة بزيادةِ نسبة حبيبات كاربيد السلكون ألمضافة، وحصل زيادة في سرعة الترسيب للمادة المدعمة بحبيبات كاربيد السلكون بالمقارنةِ مع سبيكةِ المادة الاساس غير المدعمةِ. أستخدمت تقنية الدبّوس على ماكنةِ أختبار البلى والتي تستعمل القرصِ الدوار لمعرفة خسارةِ البلى للمادة الاساس والمادة المدعمة. أظهرت النَتائِجَ بأنّ نِسَبِة خسارة البلى للمادة المدعمة أوطأ مِنْها بالنسبة لسبيكةِ المادة المتراكبة الاساس ويزداد النقصانَ بزيادةِ المحتوى من حبيبات كاربيد السلكون.


Article
Low Cycle Fatigue of Precipitation Hardened Aluminum Alloy
كلال الدورات المنخفضة في سبيكة المنيوم قابلة للتصليد بالترسيب

Authors: Dhafir S. Al-Fattal --- Saif Khalid Mahmood
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 9 Part (A) Engineering Pages: 2146-2158
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this work, the influence of different heat treatments on the mechanical properties and fatigue life under low cycles of wrought 7075 aluminum alloy was experimentally investigated. The heat treatments included peak ageing (T6), over ageing (T73) and annealing (O).The flat fatigue specimens were subjected to constant reverse bending load. The tests were performed at the laboratory environment with a frequency of 23.6 Hz andat a stress ratio (R) of -1.For each temper, strain-life graphs were obtained for specimens with notches in the form of central cylindrical holes made by drilling. The fatigue resistance of specimens with notches was comparedto the results for notch-free specimens. It was observed that the presence of a stress raiser, such as a drilled hole, lowers the fatigue life for all tempers. However, the notch sensitivity of the fatigue life was different for each temper. The fatigue crack growth rate of T73 and annealed temper was investigated; the results showed that T73 treated sample exhibits higher crack growth resistance. Paris` equation was derived for each temper.

في هذا البحث، تم التحقق عمليا من تاثير معاملات حرارية مختلفة على الخواص الميكانيكية وعلى عمر الكلال تحت دورات منخفضة لسبيكة الالمنيوم 7075 . تضمنت المعاملات الحرارية : التعتيق لاقصى صلادة (T6) والتعتيق المفرط (Overageing,T73) والتخمير(O). تعرضت عينة الكلال المسطحة الى حمل انحناء متعاكس ثابت السعة. تم اجراء الاختبار في جو المختبر مع تردد 23.6 Hz و نسبة اجهاد -1 .لكل معاملة حرارية ، تم ايجاد منحنيات الانفعال- العمر لعينات ذات حزوز بشكل ثقوب اسطوانية مركزية صنعت بعملية التثقيب . تم مقارنة مقاومة الكلال للعينات المحززة مع نتائج مقاومة الكلال لعينات غير محززة . لوحظ ان وجود رافعات الاجهاد، كما الحال في الثقوب، تخفض عمر الكلال لكل المعاملات، ولكن كان تأثير حساسية الحز علىعمر الكلال مختلف لكل معاملة. تم التحقق من معدل نمو الشق لمعاملة التخمير و معاملة T73 و اظهرت النتائج ان معاملة T73 لها مقاومة اعلى لنموالشق . تم ايجاد معادلة باريس لكل معاملة.