Article
The Effect of Adding Waste Plastic Fibers on some Engineering Properties of Roller Compacted Concrete
تاثير اضافة الياف الفضلات البلاستيكية على بعض الخواص الهندسية للخرسانة المحدولة بالرص

Loading...
Loading...
Abstract

This research includes producing compacted concrete by rolling method and the possibility for using in highway construction field with studying the influence of adding waste plastic fiber resulting from manual cutting for bottles used in the conservation gassy beverage on different characteristics of this type of concrete. For the purpose of selecting mix proportions appropriate for rolling compacted concrete (RCC). Approved design method for ACI-committee (5R-207 .1980) was selected for this research.Destroying plastic waste by volumetric rates ranging between (0.5%) to (2%) was approved. Reference mix was produced for comparison. Tests were conducted on the models produced from rolling compacted concrete like compressive strength, flexural strength and split tensile strength. The analysis of the results showed that the use of plastic waste fibers (1%) has led to improve the properties of each of the compressive strength and flexural strength and split tensile strength compared with reference concrete. Compressive strength in 28 days with fiber ratio (1%) is higher than (52.15%) from compressive strength in 28 days of reference concrete. It can be also observed that each of the flexural strength and split tensile strength increases by (17.86, 25.61)%, respectively, from flexural strength and split tensile strength for the reference mix

يتضمن هذا البحث انتاج الخرسانة المحدولة بالرص وإمكانية استخدامها في مجال انشاء الطرق مع دراسة تاثير اضافة الياف الفضلات البلاستيكية الناتجة عن التقطيع اليدوي للقناني المستخدمة في حفظ المشروبات الغازية على الخواص المختلفة لهذا النوع من الخرسانة لغرض اختيار نسب الخلط المناسبة للخرسانة المحدولة بالرص (RCC). تم اعتماد طريقة التصميم المعتمدة من قبل معهد الخرسانة الامريكي-اللجنة (5R-207 .1980). لقد تم اعتماد الياف الفضلات البلاستيكية بنسب حجمية تتراوح قيمتها بين (0.5%) الى (2%) . كما تم انتاج خرسانة مرجعية لغرض المقارنة. تم اجراء الفحوصات على النماذج المنتجة من الخرسانة المحدولة بالرص كفحوصات مقاومة الانضغاط , مقاومة الانثناء ,مقاومة الشد بالانشطار. لقد أظهر تحليل النتائج ان استخدام الياف الفضلات البلاستيكية بنسبة (1%) قد ادى الى تحسين خواص كل من مقاومة الانضغاط ومقاومة الانثناء ومقاومة الشد بالانشطار مقارنةَ بالخلطة المرجعية . مقاومة الانضغاط في 28 يوم عند استخدام نسبة الياف (1%) اعلى بمقدار (52.15 %) من مقاومة الانضغاط المرجعية كذلك يمكن ملاحظة بان كل من مقاومة الانثناء ومقاومة الشد بالانشطار تزداد بمقدار (17.86, 25.61)% على التوالي من مقاومة الانثناء ومقاومة الشد بالانشطار عن الخلطة المرجعية.


Article
Laboratory Investigation on Roller Compaction Technique in Concrete Construction

Authors: Ahmed S.Abdul Rahim --- Abeer A. Al-Rawi --- Saad I. Sarsam
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2012 Volume: 18 Issue: 4 Pages: 423-432
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Roller compacted concrete (RCC) is a concrete compacted by roller compaction. The concrete mixture in its unhardened state must support a roller while being compacted. The aim of this research work was to investigate the behavior and properties of roller compacted concrete when constructed in the laboratory using roller compactor manufactured in local market to simulate the field conditions. The roller compaction was conducts in three stages; each stage has different loading and number of passes of the roller. For the first stage, a load of (24) kg and (5) passes in each direction had been employed. For the second stage, a load of (104) kg and (10) passes in each direction were conducted. Finally, at the third stage, a load of (183) kg and (15) passes were adopted. Such procedure was in accordance to previous work conducted by the author. The effects of the type of coarse aggregate (crushed and rounded), fine aggregate (river and natural) and cement type (OPC and SRPC) on the mechanical properties of RCC were investigated. The effect of compaction method on compressive strength and indirect tensile strength was also discussed. A total of (26) roller compacted concrete slab samples of (380×380×100 mm) were prepared in the laboratory, Then, the slab specimens are taken out of the molds and immersed in the curing tank for (28) days. Core and Beam specimens were obtained from the slab samples for the determination of mechanical properties. Such properties include compressive, indirect tensile, flexural strengths using one point loading. It was concluded that the compressive strength of RCC using crushed aggregate is higher than that when using rounded aggregate in a range of (15-66) % for core specimens, while the compressive strength of RCC when using river sand is higher than that when using natural sand in a range of (9-26)% for core specimens. When river sand is implemented, RCC samples show higher indirect tensile strength than those with natural sand, such variation is within (7-8) %.

الخرسانة المرصوصة بالحدل تتمثل بكونها خرسانة ترص بالحادلات المدولبة حيث الخلطة الخرسانية في حالتها غيرالمتصلبة يجب ان تكون قادرة على تحمل حمل اسطوانة الحدل اثناء الرص. ان الغرض من هذا البحث هو التحري عن سلوك وخواص الخرسانة المرصوصة بالحدل تم تصنيعها مختبريا بأستخدام جهاز حدل صنع في الاسواق المحلية يشابه في هيكليته هيكلية الحادلة في الموقع من اجل ايجاد ظروف مشابه للظروف الطبيعية الموقعية. عملية الحدل تمثلت بثلاثة مراحل رئيسية كل مرحلة لها وزنها وعدد مرات مرور الحادله الخاصه بها حيث المرحلة الأولى كانت بوزن (٢٤) كغم وبعدد مرات مرور (٥) والمرحلة الثانية بوزن (١٠٤) كغم وبعدد مرات مرور (١٠) واما المرحله الأخيرة فكانت بوزن (١٨٣) كغم وبعدد مرات مرور (١٥). وقد كانت اتجاه الحدل بأتجاهين من اجل التخلص من المناطق الغير مرصوصة ولكل اتجاه ثلاثة مراحل رئيسية .تم اعتماد هذه الطريقة في الحدل استنادا لدراسة سابقة من قبل الباحث. تم دراسة تأثير نوع الركام الخشن (المكسر - المدور) ,نوع الركام الناعم (النهري- الطبيعي) ونوع السمنت المستخدم (العادي – المقاوم للكبريتات) على خواص الخرسانة المرصوصه بالحدل كما وتم اجراء مقارنة بين نتائج الخواص الميكانيكية (مقاومة الانضغاط ومقاومة الشد غيرالمباشر) لكل من النماذج التي تم رصها بواسطة المطرقه القياسيه وبين نماذج تم رصها بواسطة جهاز الحدل. تضمن الجزء العملي تهيئة (٢٦) بلاطة خرسانيه مرصوصه بالحدل بأبعاد (٣٨٠×٣٨٠×١٠٠ ملم) وتم استحصال النماذج والتي تتمثل (اللباب والاعتاب) من اجل اجراء الفحوص الخاصة بالخواص الميكانيكية. ان الخواص الفيزيائية للخرسانة المرصوصه بالحادلة المطلوبة في البحث هي مقاومة الانضغاط, مقاومة الشد غير مباشر (الأنشطار), مقاومة الأنثناء (بنقطة تحميل واحدة). تم الاستنتاج بان مقاومة الانضغاط للخرسانة المحدولة تون اعلى عند استخدام الركام المكسر عند مقارنتها بالركام المدور وبما يتراوح مابين (15-66)% لعينات اللباب, بينما ادى استخدام الرمل التهري الى ارتفاع مقاومة الانضغاط بمعدل (9-26)% للخرسانة المحدولة عن تلك التي استخدم فيها الرمل الطبيعي. عند استخدام الرمل النهري لوحظ ارتفاع في مقاومة الشد غير المباشر بمقدار (7-8)% للخرسانة المحدولة عن تلك المقاومة عند استخدام الرمل الطبيعي.


Article
Effect of Hydrated Lime on the Properties of Roller Compacted Concrete

Authors: Saad I. Sarsam --- Abeer A. Salih --- Suha Ghazi Abdullah
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2013 Volume: 19 Issue: 3 Pages: 377-387
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Roller compacted concrete (RCC) is a concrete of no slump, no reinforcement, no finishing, and compacted using vibratory roller. When compared with conventional concrete, it contains less water content when compared to traditional concrete. The RCC technique achieves significant time and cost savings during the construction of concrete. This study demonstrates the preparation of RCC slab of (38 ×38× 10) cm samples by using roller compactor which is manufactured in local markets. The Hydrated lime additive is used to study the mechanical and physical properties of that RCC slab samples. This investigation is divided into two main stages: The First stage consists of hammer compaction method with two gradation of aggregate, dense and gap graded aggregate, using five percentages of cement content (10, 12, 14, 16, and 18) as a percentage of the total aggregate content. This stage is carried out for selecting the maximum dry density, optimum moisture content, and optimum cement content which is utilized in RCC slab samples construction, a total of 49 cylinder samples sized (10 cm diameter and 11.6 cm high) are prepared.The Second stage is classified into two sub stages; the first one consists of constructing RCC slab samples using roller compaction, 12% cement as a percentage of total aggregate weight has been used according to the data obtained from first stage, this group presents reference mixes without additives. While the second sub stage presents RCC mix with hydrated lime additive and with the same gradation of mixes compact by hammer compaction method, hydrated lime was implemented as (5, 10, 12, and 15) percentage as a partial replacement of cement content. Both of physical and mechanical properties of RCC are studied using cores, sawed cubes, and sawed beams obtained from RCC slab samples. The properties studied were porosity, absorption, and compressive strength, splitting tensile strength and flexural strength by using third point loading method. The results show that hydrated lime improved the overall properties of RCC as compared to reference mix. Mixes with 5% lime give the optimum values for most of strength properties. Dense graded mixes with hydrated lime show superior properties as compared to gap graded mixes.

الخرسانه المرصوصه بالحدل هي خرسانه عديمة الهطول لاتحتاج الى حديد تسليح او عمليات انهاء وترص بأستخدام الحادلات الهزازه, عند مقارنتها بالخرسانه التقليديه فإنها تتميز بأن محتوى الماء قليل للحصول على خرسانه عديمة الهطول. هذا النوع من الخرسانه يقلل من فترة انجاز العمل وكلفة التنفيذ (معهد الخرسانة الاميركي, لجنة 211-3ر 1997). تعرض هذه الدراسه تنفيذ بلاطات من الخرسانه المرصوصه بالحدل بأبعاد (38×38×10) سم باستخدام جهاز حدل صنع محليا وباستخدام مضاف النوره المطفأه لغرض دراسة الخواص الفيزيائيه و الميكانيكيه لنماذج البلاطات هذه.يتضمن الجزء العملي مرحلتين أساسيتين هما:-المرحله الأولى تتضمن تصميم الخلطات باستخدام طريقه الرص بالمطرقة وباستخدام تدرجين من الركام هما العالي الكثافه والتدرج المنقطع التسلسل وباستعمال خمس نسب سمنت هي (10، 12، 14، 16و 18) كنسبه مئويه من الوزن الكلي للركام .هذه المرحله نفذت لاختيار الكثافه الجافه القصوى, محتوى الماء الامثل و محتوى السمنت الامثل والتي تستخدم في تنفيذ بلاطات الخرسانه المرصوصه بالحدل، حيث تم عمل 49 نموذج بأبعاد (10سم قطرا و11٫6 سم ارتفاعا) بأستخدام هذه الطريقه.المرحله الثانيه: قسمت هذه المرحله الى مجموعتين ثانويتين هما: المجموعه الأولى تشمل إنشاء بلاطات من الخرسانة المرصوصة بالحدل وترص بأستعمال الحادله لتشابه ظروف الموقع، في هذه المرحله تم اختيار نسبة السمنت المثاليه 12 كنسبه مئويه من الوزن الكلي للركام والتي تم الحصول عليها من المرحله الاولى ولنوعي التدرج السابقين لغرض دراسة سلوك وخواص الخرسانه المرصوصه بالحدل بدون إضافات تحت تأثير نسبة السمنت هذه.اما المجموعه الثانيه فتمثل تصميم خلطات الخرسانه المرصرصه بالحدل وبوجود مضاف النوره المطفأه كجزء مستبدل من وزن السمنت وبالاعتماد على نسبة سمنت 12٪ فقط ولنفس تدرجات الركام السابقه المستعملة في طريقة الرص بالمطرقه، تم استخدام المضاف كجزء من وزن السمنت وبنسب (5٪، 10٪، 12٪، 15٪). تم دراسة الخواص الفيزيائيه و الميكانيكية للخرسانة المرصوصة بالحدل باستعمال عينات من اللباب والمكعبات والاعتاب استخرجت من بلاطات الخرسانه المرصوصه بالحدل، و الخواص التي تم دراستها شملت المسامية، الامتصاص، مقاومة الانضغاط ، ومقاومة شد الانفلاق، ومقاومة الانثناء باستخدام ثلاث نقاط للتحميل.بينت النتائج إن مادة النوره المطفأة تحسن من خواص الخرسانه المرصوصه بالحدل, كما تبين إن افضل نتائج يمكن الحصول عليها عند نسبة نوره 5٪ من وزن السمنت. إن الخلطات ذات تدرج عالي الكثافه والحاويه على مضاف النوره تعطي نتائج جيده مقارنة بالخلطات ذات النواقص في التدرج.


Article
Evaluation of Mechanical Properties of Roller Compacted Concrete
تقييم الخواص الميكانيكية للخرسانة المرصوصة بالحدل والحاوية على مضافات

Authors: Mohamed Abdul-Razzaq Ahmed --- Hisham K.Ahmed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 2 Part (A) Engineering Pages: 551-572
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The main aim of this research is to study the effect of using the additive materials (hydrated lime and metakaolin) on the behavior of roller compacted concrete. The experimental work includes several trial mixes to choose the most suitable roller compacted concrete mix in terms of physical concrete properties. The first step is to specify the optimum cement and water content which is designed in laboratory using 300 kg/m3 of cement and 0.5 W/C ratio while the second step the only variation is using the optimum sand content of 700 kg/m3 and the third step the variation is using the optimum percentage of the additive materials (metakaolin and hydrated lime) at percentages (5%, 10%, 15%, 20% and 25%) as a partial replacement by weight of cement, the optimum percentage of 15% of (HL and MK) as a partial replacement of cement at different ages. The research also includes studying the physical properties (compressive strength, splitting tensile strength and flexural strength) of specimens with additive materials and without additive materials. Also the results of RCC specimens with additive materials (MK and HL) show improvement in compressive strength, splittingtensile andflexural strength (modulus of rupture) compared with the specimen without additive materials.

ان الغرض الرئيسي من هذا البحث هو دراسة تأثير أستعمال المواد المضافة (الميتاكاؤلين والجير المتميأ) على سلوك البلاطات الخرسانية المرصوصة بالحدل.تضمن الجزء العملي عمل عدد من الخلطات التجريبية لاختيار الخلطة للخرسانة المرصوصة بالحدل من حيث الخواص الفيزيائية للكونكريت التي أنجزت على عدة مراحل المرحلة الاولى هي تحديد المحتوى الامثل من السمنت والماء حيث صممت مختبريا على اساس أستعمال وزن 300 كغم/م3 من الاسمنت، 0.5 نسبة الماء الى الاسمنت بينما المرحلة الثانية تضمنت الحصول على المحتوى الامثل من الرمل وهو 700 كغم/م3 والمرحلة الثالثة تضمنت الحصول على النسبة المثلى من المواد المضافة (الميتاكاؤلين والجير المتميأ)والمستخدمة بنسب مختلفة (5%، 10%، 15%، 20%، 25%) كبديل لجزء من محتوى الاسمنت، من خلال النتائج كانت النسبة المثلى 15% من (الميتاكؤلين والجير المتميأ) كبديل لجزء من محتوى الاسمنت وبأعمار مختلفةكما شمل البحث دراسة الخواص الفيزيائية (مقاومة الانضغاط ، مقاومة شد الانشطار و مقاومة الانثناء) للنماذج الخرسانية الحاوية على المواد المضافة وكذلك الغير حاوية على المواد المضافةوكذلك بينت النتائج بأن النماذج الخرسانية المرصوصة بالحدل والحاوية على المواد المضافة (الميتاكاؤلين والجير المتميأ) أظهرت تحسنا في خاصية مقاومة الانضغاطومقاومةشد الانشطار ومقاومةالانثناء (معامل التصدع) مقارنة مع النماذج الخالية من المواد المضافة.


Article
Assessing Durability of Roller Compacted Concrete
تقييم ديمومة الخرسانة المرصوصة بالحدل

Authors: Saad Issa Sarsam سعد عيسى سرسم --- Abeer Abdulqader Salih عبير عبد القادر صالح --- Sura Dheyaa Tawfee سرى ضياء توفيق
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2014 Volume: 20 Issue: 7 Pages: 1-14
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Roller Compacted Concrete (RCC) is a technology characterized mainly by the use of rollers for compaction; this technology achieves significant time and cost savings in the construction of dams and roads. The primary scope of this research is to study the durability and performance of roller compacted concrete that was constructed in the laboratory using roller compactor manufactured in local market. A total of (60) slab specimen of (38×38×10) cm was constructed using the roller device, cured for 28 days, then 180 sawed cubes and 180 beams are obtained from RCC slab. Then, the specimens are subjected to 60 cycles of freezing and thawing, sulfate attack test and wetting and drying. The degree of effect of the type of coarse aggregate (crushed and rounded), cement type (OPC and SRPC) and cement content on the durability of RCC were investigated. The results indicated that RCC that contain SRPC has beneficial effects on properties of RCC as compared to RCC that contain OPC after durability testing. Based on the testing results, it was concluded that the resistance of RCC specimens to freezing and thawing, wetting and drying and sulfate attack test increase as cement content increase. The results also indicate that using RCC that contain crushed aggregate has a positive effect on the overall properties of RCC, as compared with RCC that contain rounded aggregate after durability testing.

تعتبر الخرسانة المرصوصة بالحدل من التقنيات التي تعتمد بالدرجة الأكبر خاصية إستعمال الحادلات لرص الخرسانة،هذه التقنية توفر وتحفظ الوقت المهم والكلفة في إنشاء السدود و الطرق. ان الهدف الرئيسي من هذا البحث هو دراسة ديمومة واداء الخرسانة المرصوصة بالحدل التي تم تصنيعها مختبريا بأستخدام جهاز حدل صنع في الاسواق المحلية. 0يتضمن الجزء العملي تحضير (60) بلاطة خرسانية مرصوصة بالحادلة بأبعاد (٣٨×٣٨×١٠) سم،بعد ذلك انضجت لمدة 28 يوم، ثم تم تقطيع هذه البلاطات الى (180) مكعب و (180)عتبة. تم تعريض النماذج الى 30و60 دوره من الانجماد والذوبان , فحص تأثير الكبريتات و الترطيب والتجفيف. تم دراسة نوع السمنت ( السمنت البورتلاندي الاعتيادي و السمنت المقاوم للكبريتات) وتأثير محتوى السمنت على ديمومة الخرسانة المرصوصة بالحادلة. من خلال النتائج التي تم الحصول عليها وجد ان مقاومة النماذج الحاويةعلى السمنت المقاوم للكبريتات له تأثير ايجابي على خواص الخرسانة المرصوصة بالحدل مقارنة مع النماذج الحاويةعلى السمنت البورتلاندي الاعتيادي بعد تعريض لنماذج الى فحوصات الديمومة. اعتمادا على نتائج الفحوصات تم الاستنتاج ايضا بأن مقاومة نماذج الخرسانة المرصوصة بالحدل لدورات الانجماد والذوبان , الترطيب و التجفيف و فحص مقاومة تأثير الكبريتات تزداد بزيادة محتوى السمنت .


Article
Effect of Compaction Methods on the Properties of Roller Compacted Concrete
تأثير طرق الرص المختلفة على خواص الخرسانة المرصوصة بالحدل

Authors: Hisham Khalid Ahmed --- Azal Thair Abdulrazzak
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 10 Part (A) Engineering Pages: 2454-2464
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Roller compacted concrete (RCC) is a technology characterized mainly use of roller for compaction. This construction method permits considerable reduction in costs and construction time of dams and roads. The main aim of this work is to investigate the influence of compaction methods on the properties of RCC. the experimental program included preparing cylindrical specimens with (diameter of 150 mm by height of 300 mm) for measuring the compressive strength, splitting tensile strength and absorption. And it also includes prism specimens with (100*100*400) mm for measuring the modulus of rupture. These specimens were compacted by using different compaction methods, dynamicly (modified proctor hammer compaction (CBR test), vibrator table, and vibrator table with CBR test) and statically (compacting pressure (compacting pressure 10 MPa, 15 MPa and 20 MPa).Results show that the compaction methods have a noticeable effect on the properties of RCC. The results also indicated that using vibrator table with CBR show an increase in the compressive strength, splitting tensile strength and modulus of rupture by 23%, 14% and 13%, respectively as compared with compacted by vibrator table only. The results also show that using compacting pressure 20 MPa show an increase in the compressive strength, splitting tensile strength and modulus of rupture by 31%, 27%, and 39%, respectively as compared with that made by compacting pressure 10 MPa.

تعتبر الخرسانة المرصوصة بالحدل من التقنيات التي تمتلك بالدرجة الاكبر خاصية استعمال الحادلات لرص الخرسانة, ان استعمال هذه الخرسانة يوفر الوقت و الكلفة في إنشاء السدود و الطرق. إن الهدف الرئيسي من هذا البحث هو دراسة تأثير طرق الرص المختلفة على خواص الخرسانة المرصوصة بالحدل. تضمن المنهاج العملي تحضير نماذج فحص اسطوانية بابعاد (قطر 150 ملم و ارتفاع 300 ملم) لغرض قياس مقاومة الانضغاط و مقاومة شد الانشطار و الامتصاص و استخدام مواشير ذات ابعاد ( 100* 100* 400)ملم لغرض فحص معامل التصدع. و قد تم استعمال طرق مختلفة لرص النماذج الخرانية بصورة ديناميكية (الرص بالمطرقة, المنضدة الهزازة, المنضدة الهزازة ثم الرص بالمطرقة معاً) و بصورة ستاتيكية (بتسليط ضغط بمقدار 10 ميكاباسكال, 15 ميكاباسكال, 20 ميكاباسكال). و قد بينت النتائج بان لطرق الرص المختلفة تأثير ملحوظ على خواص الخرسانة المرصوصة بالحدل, كما اشارت النتائج بان استعمال طريقة المنضدة الهزازة مع الرص بالمطرقة يؤدي الى زيادةفي مقاومة الأنضغاط, الأنشطارومعامل التصدع بمقدار 23%, 14%, 13% على التوالي مقارنة بتلك التي تم رصها بواسطة المنضدة الهزازة وكذلك بينت النتائج ان استعمال طريقة تسليط الضغط بمقدار 20 ميكاباسكال يؤدي الى زيادة في مقاومة الانضغاط, الانشطار, ومعامل التصدع بمقدار 31%, 27%, 39% على التوالي مقارنة بتلك التي تم رصها بتسليط ضغط 10 ميكاباسكال وطريقة تسليط ضغط 20 ميكاباسكال لرص النماذج تعطي تحسن جيد في الخواص الميكانيكية للخرسانة المرصوصة بالحدل.


Article
Effect of Practical Curing Methods on the Properties of Roller Compacted Concrete
تأثير الطرق العملية للمعالجة على خواص الخرسانة المرصوصة بالحدل

Authors: Hisham K. Ahmed --- Intesar Kadhim Gata
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 2 Part (A) Engineering Pages: 500-511
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Roller Compacted Concrete (RCC) is a technology characterized mainly by the use of rollers for compaction. This construction method permits considerable reduction in costs and construction time of dams and roads. It is necessary to study the curing of RCC especially in hot weather because RCC has no slump and has low W/C ratio. Therefore the primary scope of this research is to study the effect of various curing methods (continuous watering, wet burlap, nylon, sprinkling, curing cycles, and curing compound) after 24 hrs from casting on the physical properties of roller compacted concrete. The mix proportion which was used in this investigation, was designed and laboratory tried on the basis of using 250 kg/m³ of Ordinary Portland Cement. This work involves preparing cylindrical specimens with (diameter of 150 mm and height of 300 mm) for measuring the compressive strength, splitting-tensile strength, and static modulus of elasticity. And it also includes prism specimens with (100×100×400 mm) for measuring the modulus of rupture (flexural strength). Results show that the curing of RCC with continuous watering clearly improved the RCC properties. The results also indicate that the RCC specimens without curing (left in air) suffered from permanent loss of strengths ranging between 20 to 25 % when compared with continuous watering at age of 28 days.

تعتبر الخرسانة المرصوصة بالحدل من التقنيات التي تملك بالدرجة الأكبر خاصية إستعمال الحادلات لرص الخرسانة إن إستعمال هذه الخرسانة يوفر الوقت والكلفة في إنشاء السدود والطرق. وبالنظر لكون الخرسانة المرصوصة بالحدل هي خرسانة بلا هطول، وذات محتوى مائي قليل ،ولإهمية المعالجة لهذا النوع من الخرسانة فإن من الضروري الإهتمام بدراسة طرق المعالجة للخرسانة المرصوصة بالحدل وخاصة في الأجواء الحارة، لذلك فإن الهدف الرئيسي من هذا البحث هو دراسة تأثير الأنواع المختلفة من المعالجة (المعالجة بصورة مستمرة بالماء، تغطية الخرسانة بالجنفاص المرطب، تغطيتها بالنايلون، الرش، تعريض الخرسانة لدورات متعاقبة من الترطيب والتجفيف و إستعمال مركبات المعالجة) بعد 24 ساعة من البدء بعملية الصب على الخواص الفيزيائية وتضمن المنهاج العملي استعمال نسبة خلط والتي صممت مختبرياً على أساس إستخدام 250 كغم/م‎3 من السمنت وتحضير نماذج فحص أسطوانية بإبعاد (قطر 150 ملم وطول 300 ملم) لغرض قياس مقاومة الإنضغاط ومقاومة الشد ومعامل المرونة الستاتيكي وفحص الإمتصاص،وإستخدام مواشير ذات أبعاد (100 ×100×400 ملم) لغرض فحص معامل التصدع (مقاومة الإنثناء). وقد بينت النتائج بأن معالجة الخرسانة بصورة مستمرة بالماء يحسن من خواص الخرسانة المرصوصة بالحدل بشكل ملحوظ، كما أشارت النتائج إلى إن عدم معالجة الخرسانة المرصوصة بالحدل يؤدي إلى إنخفاض ملموس في مقاومة الإنضغاط ومقاومة الشد ومعامل التصدع يتراوح ما بين 20% إلى 25% مقارنة مع تلك الخرسانة المعالجة بصورة مستمرة بالماء وبعمر 28 يوم.


Article
Assessing the Effect of Using Porcelanite on Compressive Strength of Roller Compacted Concrete
تقييم تأثير اضافة مادة البورسيلنايت على مقاومة الانضغاط للخرسانة المرصوصة بالحدل.

Authors: Abeer Abdulqader Salih Abeer Abdulqader Salih عبـير عبد القادر صالح --- Ziyad Majeed Abed زيــاد مجــيــد عــبــد
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2014 Volume: 20 Issue: 10 Pages: 16-28
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Roller-Compacted Concrete (RCC) is a zero-slump concrete, with no forms, no reinforcing steel, no finishing and is wet enough to support compaction by vibratory rollers. Because the effectiveness of curing on properties and durability, the primary scope of this research is to study the effect of various curing methods (air curing, emulsified asphalt(flan coat) curing, 7 days water curing and permanent water curing) and different porcelanite (local material used as an Internal Curing agent) replacement percentages (volumetric replacement) of fine aggregate on some properties of RCC and to explore the possibility of introducing more practical RCC for road pavement with minimum requirement of curing. Cubes specimens were sawed from the slabs of (38*38*10) cm for determination of compressive strength. The results show that using (5) % porcelanite improved the compressive strength of RCC (with air curing) as compared with reference RCC (with permanent curing) by percentage ranging from(-2.9 to 6)%.

الخرسانة المرصوصة بالحدل هي الخرسانة العديمة الهطول والتي لا يتم فيها أستعمال القوالب أوحديد التسليح ولا تحتاج الى عمل الانهاءات ،ويجب ان تكون ذات رطوبة كافية لتحمّل الحدل بواسطة الحادلة الهزازة.بسبب تأثير الانضاج على خصائص وديمومة لذا فإن الهدف الرئيسي من هذا البحث هو دراسة تأثير طرق الانضاج المختلفة (الانضاج بالهواء،الانضاج بالمستحلب الاسفلتي (الفلنكوت) ،الانضاج 7 ايام بالماء،الانضاج الدائمي بالماء ) وبأستخدام البورسيلنايت (مادة محلية تستعمل كعامل أنضاج داخلي) وبنسب استبدال مختلفة (استبدال حجمي من الركام الناعم) على بعض خواص الخرسانة المرصوصة بالحدل واستكشاف مدى امكانية انتاج هذه الخرسانة لرصف الطرق لتكون اكثر عملية وبأستعمال الحد الادنى من متطلبات عملية الانضاج.يتم نشر الواح خرسانة بأبعاد (38*38*10) سم لتشكيل مكعبات لفحص مقاومة الانضغاط.تظهر النتائج ان استعمال (5%) بورسيلنايت يقوم بتحسين مقاومة الانضغاط للخرسانة المرصوصة بالحدل (بأستعمال الانضاج بالهواء) مقارنة مع الخرسانة المرصوصة بالحدل المرجعية (بأستعمال الانضاج الدائمي) بنسبة تتراوح بين (6 – 2.9 - )%.


Article
Effect of Using Porcelanite as Partial Replacement of Fine Aggregate on Roller Compacted Concrete with Different Curing Methods
تأثير أستعمال مادة البورسيلنايت كأستبدال جزئي من الركام الناعم على الخرسانة المرصوصة بالحدل وبطرق انضاج مختلفة.

Authors: Abeer Abdulqader Salih عبـير عبد القادر صالح --- Ziyad Majeed Abed زيــاد مجــيــد عــبــد
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2016 Volume: 22 Issue: 9 Pages: 21-35
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Roller-Compacted Concrete is a no-slump concrete, with no reinforcing steel, no forms, no finishing and wet enough to support compaction by vibratory rollers. Due to the effect of curing on properties and durability of concrete, the main purpose of this research is to study the effect of various curing methods (air curing, 7 days water curing, and permanent water curing) and porcelanite (local material used as an Internal Curing agent) with different replacement percentages of fine aggregate (volumetric replacement) on some properties of Roller-Compacted Concrete and to explore the possibility of introducing practical Roller-Compacted Concrete for road pavement with minimum requirement of curing. Specimens were sawed from slabs of (380*380*100) mm for determination of Ultrasonic Pulse Velocity (UPV) and Voids volume. Results show that using (5) % porcelanite improved the results of UPV and Voids volume of Roller-Compacted Concrete (with air curing) as compared with reference Roller-Compacted Concrete (with permanent water curing) by percentages ranging from(3.6 to 28.9)% and (-8 to -15.5)% respectively.

الخرسانة المرصوصة بالحدل هي الخرسانة عديمة الهطول والتي لا يتم فيها أستعمال حديد التسليح أو القوالب ولا تحتاج الى عملية الانهاء وكذلك يجب ان تكون ذات رطوبة كافية لتحمّل الحدل بواسطة الحادلات الهزازة.نتيجة لتأثير الانضاج على خصائص وديمومة الخرسانة لذا فإن الهدف الاساسي من البحث هو دراسة تأثير طرق مختلفة من الانضاج (الانضاج بالهواء ،الانضاج 7 ايام بالماء، الانضاج الدائمي بالماء) وبأستخدام البورسيلنايت (مادة محلية تستعمل كعامل أنضاج داخلي) وبنسب استبدال مختلفة من الركام الناعم (استبدال حجمي) على بعض خواص الخرسانة المرصوصة بالحدل وتحري مدى امكانية انتاج هذه الخرسانة لرصف الطرق لتكون اكثر عملية وبأستعمال الحد الادنى من متطلبات عملية الانضاج .يتم نشر الواح خرسانة بأبعاد (380*380*100) مم لعمل نماذج لفحوص الامواج فوق الصوتية والمسامية.تظهر النتائج ان استعمال (5%) بورسيلنايت يقوم بتحسين نتائج فحوص الامواج فوق الصوتية والمسامية للخرسانة المرصوصة بالحدل (بأستعمال الانضاج بالهواء) بالمقارنة مع الخرسانة المرصوصة بالحدل المرجعية (بأستعمال الانضاج الدائمي بالماء) بنسب تتراوح بين (3.6 to 28.9)% و(-8 to -15.5) % على التوالي .

Listing 1 - 9 of 9
Sort by
Narrow your search

Resource type

article (9)


Language

English (7)

Arabic and English (2)


Year
From To Submit

2016 (2)

2015 (1)

2014 (4)

2013 (1)

2012 (1)