Article
PREPARATION AND CHARACTERIZATION OF PHASE-PURE ANATASE NANOPARTICLES

Author: Dr Imad Ali Disher Al-Hydary
Journal: Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد ISSN: 20761819 Year: 2014 Volume: 14 Issue: 1 Pages: 98-106
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

The anatase phase of titania has great potential to be used in various applications. Thus; the synthesis of phase-pure nanocrystalline anatase has attained great importance in the past decade. In the present work, the sol-gel method was used to prepare such nanoparticles. It has been found that the sol-gel method can, with the help of long aging time, produce phase-pure anatase nanoparticles that have polygonal shape with edges’ length in the range of (~30-70nm). The firing temperature should be kept higher than 500°C to get fully crystalline nanoparticles and lower than 800°C to avoid the phase transformation to rutile phase

يمتلك طور الاناتيس لثنائي اوكسيد التيتانيوم الاهلية للاستخدامات العديدة في التطبيقات المختلفة، لذلك اكتسب تحضيره بشكل متبلور نانوي نقي-الطور اهمية كبيرة في العقد المنصرم. في العمل الحالي استعملت طريقة (المحلول-الجلاتين) في تحضير هذه المادة بالوصف المذكور. لقد وجد ان طريقة (المحلول-الجلاتين) يمكن ان تنتج هذه المادة بمساعدة التعتيق لفترة زمنية طويلة. تمتلك الحبيبات النانوية المحضرة شكلا متعدد الاظلاع تتراوح ابعاد اضلاعه بين (~30 – 70 نانومتر). يجب ان تتم عملية حرق الجلاتين في درجة حرارة اعلى من (500°م) للحصول على الحبيبات النانوية المتبلورة وبدرجة اقل من (800°م) لتفادي تكون طور الروتايل.


Article
Modeling and Evaluation of Queuing Systems Use of ArtificialNeural Net work for Estimation of the Dissolved of Rutile Ore
نمذجة وتقييم الشبكات العصبيه لتقدير اذابة خام الروتايل

Author: Ahmed Falh
Journal: Diyala Journal For Pure Science مجلة ديالى للعلوم الصرفة ISSN: 83732222 25189255 Year: 2011 Volume: 7 Issue: 2 Pages: 13-28
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

This paper use artificial neural net work for state the fractional of dissolution rutile ore (TiO2)
with different condition ( Reaction temperature and acid concentration ,HCl) at different leaching
time ,tow neural net wok was proposed each one contain 20 samples (in put data) for training the
net work then 5 samples use to test the net work after training at different condition .
The results show the net work NO.1 give perfect estimation ,but the network No.2 was failed
to estimate the result ,also correlation factor is the most important factor in ANN(Artificial Neural
Net work) to give estimation for matching between experimental and target data.

تهدف الدراسة الحالية إلى استخدام الشبكات العصبية لغرض تحديد إذابة خام الروتايل ( ثنائي وكسيد التيتانيوم ) بظروف مختلفة من درجة حرارة وتركيز حامض الهيدروكلوريك عند أزمان نض مختلفة , تم تحضير شبكتان عصبيتان كل واحدة تحتوي على 20 مدخل لغرض تدريب الشبكة ثم استخدام 5 نماذج لغرض اختبار الشبكة عند ظروف مختلفة .ومن النتائج تبين أن الشبكة الأولى التي درست تأثير تركيز حامض الهيدروكلوريك كانت مثالية في تخمين النتائج أما الشبكة التي درست درجة حرارة التفاعل فقط أخفقت في الاختبار , وكذلك بينت الدراسة أن معامل الارتباط مهم جدا" في تدريب واختبار الشبكات العصبية لكي يتم استخدامها مستقبلا بظروف مقاربة للدراسة .


Article
Study The Molarity Influence on the structural properties of titanium oxide (TiO2) Prepared with (Sol_Gel)
دراسة التأثير المولاري على الخصائص التركيبية لأوكسيد التيتانيوم TiO2 المحضر بطريقة Sol _ Gel

Authors: Riyadh sami رياض سامي عنتر --- Rafea A. Munef رافع عبد الله منيف --- Fares Saleh Atallah فارس صالح عطاالله
Journal: Tikrit Journal of Pure Science مجلة تكريت للعلوم الصرفة ISSN: 18131662 Year: 2016 Volume: 21 Issue: 2 Pages: 162-170
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

This report was conducted to study the molar effect on structural characteristics of Titanium dioxide TiO2 ,the deposition of films on glass substrates was done by using sol gel solution with Spin-Coting method (speed =3000 rpm) during 30 sec of the deposition where the solution have been prepared using Titanium hydroxyl Material Ti[O(CH2)3(CH3)]4 and C4H11NO2 as Fixative and Ethanol as a solvent. we have prepared different concentrations of solution (0.05, 0.10 , 0.15, 0.20, 0.30) M ,the films have been annealing with temperature (500 °C), we have investigated the Structural characteristics using (XRD,AFM and SEM) analyses. The (XRD) results have shown that the Anatase phase is the prevalent phase when the concentrations (0.05 and 0.10)M and after increase the concentration start changes gradually from Anatase phase to Rutile phase when the concentration (0.2)M. The SEM analyses have approved that the film has good topography. The granules had a rhombus form then its shape became cluster with the increasing of concentration . The (AFM) have shown that the membranes had nano- thickness,and they are soft with good coating

تم في هذا البحث دراسة التأثير المولاري على الخصائص التركيبية لثنائي أوكسيد التيتانيوم TiO2 حيث رسبت الاغشية على ارضيات من الزجاج باستخدام محلول (Sol_Gel) وبتقنية Spin_Coting وبسرعة RPM 3000 خلال زمن ترسيب قدره 30sec وتم تحضير المحلول باستخدام مادة اوكسيد التيتانيوم المائي Ti[O(CH2)3CH3]4 و [C4H11NO2] كمثبت والايثانول كمذيب (C3H8O2) وحضر المحلول بمولاريات مختلفة منM (0.05,0.1,0.15,0.2,0.3) ويتم تلدين الأغشية بدرجة حرارة 500℃ ,وتم دراسة الخصائص التركيبة من خلال فحوصات (XRD & AFM,SEM). حيث تبين من النتائج XRD)) ان طور الانتاس هو الطور السائد عند التركيزM 0.05)& (0.1 وبعد زيادة التركيز يبدا التحول التدريجي بالطور حيث يتحول من الانتاس الى الروتايل عند تركيز 0.2M, وبينت فحوصات SEM)) ان الغشاء ذو طبوغرافية جيدة ,وان شكل الحبيبات يكون معيني ثم يتحول بزيادة التركيز الى عناقيد زهرية الشكل, ومن خلال فحوصات(AFM) تبين ان الاغشية ذات سمك نانوي وناعمة وذات اكساء جيد .


Article
Growth, Single-Crystalline Rutile TiO2 Nanorod Thin Film By Hydrothermal Technique
تطوير تقنية الأنماء للأغشية الرقيقة ذات القضبان النانوية أحادية التبلور لمركب ثنائي أوكسيد التيتانيوم تركيب الروتايل

Authors: Zuhair H. Nasser زهير هشام ناصر --- Sattar J. Kasim ستار جبار قاسم --- Whidad S. Hanoosh وداد صالح حنوش
Journal: Journal of Kufa - physics مجلة الكوفة للفيزياء ISSN: 20775830 Year: 2018 Volume: 10 Issue: 2 Pages: 39-47
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

A facile, hydrothermal technique was developed to growth, single-crystalline rutile TiO2 nanorod thin films on transparent conductive fluorine-doped tin oxide (FTO) substrates. In this study, the deferent periods(6, 9, 12, 15, and 18 hour) were selective with constant temperature at 160 oC to growth this films and growth in deferent temperature (130, 150,170,190, and 210 oC) with constant period of deposition at 6h. SEM image showed all the films were nanorodand the EDX measurement was given the portion of element that contribution in rutile TiO2 nanorod thin films. The diameter, length, and density of the nanorods could be varied by changingthe growth parameters. The XRD to determine the structure properties, and optical properties were measured of these rutile TiO2 nanorod thin films and obtained the absorbance and energy gap. http://dx.doi.org/10.31257/2018/JKP/100206

لقد تم تطوير تقنية الأنماء للأغشية الرقيقة ذات القضبان النانوية أحادية التبلور لمركب ثنائي أوكسيد التيتانيوم تركيب الروتايل على قواعد زجاجية مطلية بـطبقة شفافة و موصلة من(FTO) .و ذلك بانتفاء فترات ترسيب مختلفة ((6, 9, 12, 15, and 18 hour بثبوت درجة الحرارة عند 160oC ودرجات حرارية مختلفة (130, 150,170,190, 210 oC)بثبوت فترة الترسيب 6h. تم قياس الخواص التركيبية عن طريق الصور الملتقطة بواسطة جهاز المجهر الإلكتروني الماسح وقياسات (EDX) أضافة الى قياسات (XRD)وأظهرت أن الأغشية الرقيقة تعود الى TiO2` ذات قضبان بقياسات نانوية . وقد تم حساب أقطار وكثافة القضبان النانوية. كما أجريت القياسات على الأغشية لتحديد خواصها البصرية ييث تم تحديد حافة و معامل الامتصاص أضافة الى فجوة الطاقة البصرية.

Listing 1 - 4 of 4
Sort by
Narrow your search

Resource type

article (4)


Language

English (3)

Arabic (1)


Year
From To Submit

2018 (1)

2016 (1)

2014 (1)

2011 (1)