PREPARED THIXOFOROMED ALUMINUM ALLOYS BY HIGH-PRESSURE CAST AND STUDY THEIR WEAR PROPERTIE
تحضير سبائك ثايكسوفورميد الألمنيوم بواسطة سباكة الضغط العالي ودراسة خواص البلى لها

Author: Aqeel Ali Kadhim AL-Attar عقيل علي كاظم
Journal: DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية ISSN: 19998716/26166909 Year: 2010 Volume: 3 Issue: 2 Pages: 25-38
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

Hypereutectic Al-Si casting alloys are attractive candidates for connecting rod applications in compressors. Several hypo- and hypereutectic Al-Si alloys were produced by pressure die casting and thixoforming in this search. Hypereutectic Al—Si alloys were less than the near-eutectic and hypoeutectic alloys under the sever were conditions encountered in compressors, confirming the impact of Si on were resistance. Cu also improves were properties. The thixoformed alloys were at comparable rates with pressure die cast alloys at lower Si levels, implying that the lower Si content of the former is compensated for by the thixoforming processing route. Hypereutectic composition, uniform dispersion of fine Si particles and thixoforming as the production route are all good for a superior wear performance, However, does not translate into a sizable improvement in wear resistance of the thixoformed alloys.

تعتبر سبيكة الألمنيوم-سيليكون المسبوكة من السبائك ذات التطبيقات الواسعة وخصوصاً في أنظمة الضاغطات. ولهذا السبب تم إنتاج العديد من سبائك Al-Si بطرق الضغط أو العصر أو بالطريقة الهلامية (العجينة) ودراسة تأثير البلى على هذه السبيكة ومعرفة مدى تأثير السيليكون على مقاومة البلى وكذلك معرفة مدى تحسين مقاومة البلى من خلال طريقة التصنيع بالحالة الهلامية، ومن خلال هذا البحث تم التوصل إلى زيادة البلى عن طريق التصنيع بالطريقة الهلامية .

Listing 1 - 1 of 1
Sort by
Narrow your search

Resource type

article (1)


Language

English (1)


Year
From To Submit

2010 (1)