Article
Fabrication of Tio2 and V2o5 Thin Films by Powder Coating Technique
تصنیع اغشیة رقیقة من اوكسید التیتانیوم و اوكسید الفنادیوم بتقنیة مساحیق الطلاء

Authors: Mohammed S. Hamza --- Alaa Aladdin --- Shatha Kazem
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 16 Part (A) Engineering Pages: 3194-3202
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Titanium dioxide (TiO2) and vanadium oxide (V2O5) in different mixing percentage(100, 50, 0)% from them powders as thin film on substrate of glass .the coatingthickness was ( 0.37 ±0.03 μm ).Thin films were inspection by microphotographs with scanning electron microscopy(SEM) and x-ray diffraction (XRD).The results showed that thin films was prepared crystalline and also the compound(tio2, v2o5), and the structure was regular and smooth.

Keywords

TiO2 --- V2O5 --- THIN film --- SEM --- XRD


Article
The Influence of RF power, pressure and substrate temperature on optical properties of RF Sputtered vanadium pentoxide thin films
تاثير الطاقة والضغط ودرجة حرارة الركيزة على الخصائص البصرية للاغشية الرقيقة لخامس اوكسيد الفاناديوم باستخدام الترذيذ بالترددات الراديوية

Authors: Ibrahim K. salman إبراهيم خلف سلمان --- N.K. Hassan نديم خالد حسن --- Mohammed K. Khalaf محمد خماس خلف
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2018 Volume: 16 Issue: 39 Pages: 42-47
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The V2O5 films were deposited on glass substrates which produce using "radio frequency (RF)"power supply and Argon gas technique. The optical properties were investigated by, UV spectroscopy at "radio frequency" (RF) power ranging from 75 - 150 Watt and gas pressure, (0.03, 0.05 and 0.007 Torr), and substrate temperature (359, 373,473 and 573) K. The UV-Visible analysis shows that the average transmittance of all films in the range 40-65 %. When the thickness has been increased the transhumance was decreased from (65-40) %. The values of energy band gap were lowered from (3.02-2.9 eV) with the increase of thickness the films in relation to an increase in power, The energy gap decreased (2.8 - 2.7) eV with an increase in the pressure and substrate temperature respectively.

تم ترسيب أغشية رقيقة من خامس اكسيد الفاناديوم على ركائز زجاجية التي تنتج باستخدام طاقة التردد الراديوي وتقنية غاز الأرجون، وتم بحث الخواص البصرية بواسطة دراسة مطيافية مرئية فوق بنفسجية عند قدرة التردد الراديوي من 75 - 150 واط وضغط الغاز 0.03 تور، .050 تور و 0.007 تور، ودرجة حرارة الركيزة (359، 373، 473 و 573) كلفن. أظهر التحليل الطيفي المرئي و للأشعة فوق البنفسجية أن متوسط نفاذ جميع الأغشية يكمن في نطاق 40-65 ٪ و عندما زاد السمك انخفضت نسبة الانتقال مـــن (65 -40) %. و انخفضت فجوة النطاق الضوئي للغشاء من 3.02 إلى 2.9 الكترون فولت, مع زيادة سماكة الأغشية مقارنة بالزيادة في القدرة، من ناحية أخرى انخفضت فجوة النطاق من 2.8 إلى 2.7 الكترون فولت, مع زيادة الضغط ودرجة حرارة الركيزة على التوالي.


Article
Structural and Optical properties of Polymers(PVA / PVP ) doped with V2O5 composites films

Author: Ghuzlan S. Ahmed
Journal: Ibn Al-Haitham Journal For Pure And Applied Science مجلة ابن الهيثم للعلوم الصرفة والتطبيقية ISSN: 16094042/ 25213407 Year: 2017 Volume: 30 Issue: 2 Pages: 16-24
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Study the effect of doping V2O5 on polymers poly vinyl alcohol ( PVA), poly vinyl pyrrolidone (PVP) on the optical and structural properties for film prepared by using Casting method at thickness( 300±20)nm ,All the materials dissolved in distilled water by magnetic mixer for one hour .The optical parameters measured by using UV-VIS spectrometer ,and the structural parameters measured by X-ray diffraction .when measured the energy gap found that the value was decreases from 4.6 eV to 2.98 eV with doping .The refractive index ,extinction coefficient ,absorption coefficient ,real and imaginary dielectric constants of (PVA/PVP) are increasing with doping by V2O5 and with increase the ratio of dop


Article
Fabrication Of TiO2 , V2O5 Thin Film (Super Hydrophobic Surface )By Powder Coating Technique
تصنيع أغشية رقيقة من TiO2 , V2O5 (سطح فائق الرفض للماء) بتقنية طلاء المسحوق

Authors: Mohammed S. Hamza محمد صلاب حمزة --- Alaa Aladdin ألاء علاء الدين --- Shatha K. Mohammed شذا كاظم محمد
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2016 Volume: 22 Issue: 2 Pages: 128-136
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this research, deposition of titanium oxide (TiO2) and vanadium oxide (V2O5) thin film in different mixing percentage (0, 25 ,50, 75 and100)% on the substrate of glass .The coating thickness was ( 50 nm ).In this research contact angle was measured and the effect of weather conditions. Results showed that the value of the contact angle of the prepared films reached its highest value at 50% (TiO2+V2O5) was 160º.The results showed that the optical transmittance of TiO2 and V2O5 thin film decrease with increasing the deposition angle and decrease with increasing V2O5 proportion.

في هذا البحث، تم ترسيب أوكسيد التيتانيوم (TiO2) وأكسيد الفناديوم (V2O5) بشكل غشاء رقيق عند نسبة خلط مختلفة ( 0و25 و 50 و 75 و 100)% منها على قاعدة من الزجاج. وبسمك طلاء (50 نانومتر).في هذا البحث تم قياس زاوية الاتصال وتأثير الظروف الجوية. وأظهرت النتائج أن قيمة زاوية الاتصال من الأفلام المعدة بلغت أعلى قيمة لها عند نسبة خلط 50٪( TiO2، V2O5 ) و كانت (160 ̊ ) . وقد تم فحص النفاذية البصرية؛ وأظهرت النتائج أن النفاذية الغشاء الرقيق لكل من TiO2 وV2O5 انخفضت مع زيادة زاوية الترسب ومع زيادة نسبة V2O5 في الخليط.


Article
HOT CORROSION OF CERIA-YTTRIA STABILIZED ZIRCONIA PLASMA SPRAYED THERMAL BARRIER COATING BY EUTECTIC VANDIUMPENTAOXIDE-SODIUM SULFATE
التاكل الساخن لطبقات الرش بالبلازما للحواجز الحرارية للسيريا-ياتريا المثبتة للزركونيا بالاويتكتيك لخماسي اوكسيد-الفناديوم- كبريتات الصوديوم

Loading...
Loading...
Abstract

The high temperature corrosion behavior of thermal barrier coating (TBC) system consisting of IN-738 LC superalloy substrate, air plasma sprayed Ni24.5Cr6Al0.4Y (wt%) bond coat and air plasma sprayed ZrO2-20 wt% ceria-3.6 wt% yttria (CYSZ) ceramic coat were characterized. The upper surfaces of CYSZ covered with 30 mg/cm2 , mixed 45 wt% Na2SO4-55 wt% V2O5 salt were exposed at different temperatures from 800 to 1000 oC and interaction times from 1 up to 8 h. The upper surface plan view of the coatings were identified for topography, roughness, chemical composition, phases and reaction products using scanning electron microscopy, energy dispersive spectroscopy, talysurf, and X-ray diffraction. XRD analyses of the plasma sprayed coatings after hot corrosion confirmed the phase transformation of nontransformable tetragonal (t') into monoclinic phase, presence of YVO4 and CeVO4 products. Analysis of the hot corrosion CYSZ coating confirmed the formation of high volume fraction of YVO4, with low volume fractions of CeOV4 and CeO2. The formation of these compounds were combined with formation of monoclinic phase (m) from transformation of nontransformable tetragonal phase (t').

تم تقييم التاكل الكيميائي بدرجة الحرارة العالية لطلاءات الحواجز الحراية المنتجة بالرش بالبلازما للزركونيا الحاوية على 20 wt% سيريا و 3.6 wt% ياتريا والمطلية على طبقة طلاء وسطية من Ni24.5Cr6Al0.4Y (wt%). ان طبقات الطلاء السيراميكية والوسطية المنتجة بالرش بالبلازما تم طلائها على سبيكة فائقة من .IN-738 LC طبقات الرش بالبلاما السيراميكية التي تم تغطيتها بمزيج ملحي من 45 wt% Na2SO4-55 wt% V2O5 وبمعدل تغطية 30 mg/cm2 تم اختبارها بدرجة حرارة من 800 الى oC 1000 ولفترات زمنية 1 و 8 ساعات. طوبوغرافية الاسطح والخشونة والتركيب الكيمائي والاطوار ونواتج التاكل للاسطح العلوية لطبقات الرش تم تحديدها باستخدام المجهر الالكتروني الماسح ومطياف مفرق الطاقة و جهاز قياس الخشونة وحيود الاشعة السينية. اثبتت نتائج حيود الاشعة السينية لطبقات الرش بعد التاكل الكيميائي تحول الطور السداسي الغير متحول t') ) الى الطور احادي الميل m)) و الاطوار YVO4 و CeVO4. اوضح تحليل طبقات الرش بالبلازما بعد التاكل بان الطور السائد بكسر حجمي كبير هو YVO4 وكمية قليلة من الاطوار CeOV4 و .CeO2 أن تكزن هذه الاطوارمصاحب لتكوين الطور الاحادي الميل m)) الناتج من تحول الطور السداسي الغير متحول (t') .


Article
Plasma Spectroscopy Diagnostics of V2O5 at a Variable of Operating Power and Pressure With Radio Frequency Magnetron Sputtering.
التشخيص الطيفي للبلازما لمادة خامس اوكسيد الفاناديوم في الترذيذ الماكنتروني بالترددات الراديوية مع تغير طاقة التشغيل والضغط

Authors: Ibrahim K. salman إبراهيم خلف سلمان --- Mohammed K. Khalaf محمد خماس خلف --- N. K. Hassan نديم خالد حسن --- Hanaa Eesa Jasim هناء عيسى جاسم
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2019 Volume: 16 Issue: 1 Supplement Pages: 209-214
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this paper, we investigate the basic characteristics of "magnetron sputtering plasma" using the target V2O5. The "magnetron sputtering plasma" is produced using "radio frequency (RF)" power supply and Argon gas. The intensity of the light emission from atoms and radicals in the plasma measured by using "optical emission spectrophotometer", and the appeared peaks in all patterns match the standard lines from NIST database and employed are to estimate the plasma parameters, of computes electron temperature and the electrons density. The characteristics of V2O5 sputtering plasma at multiple discharge provisos are studied at the "radio frequency" (RF) power ranging from 75 - 150 Watt and gas pressure (0.03, 0.05 and 0.007) torr. One can observe that the intensity of the emission lines increases with increasing the sputtering power. We find that the electron temperature excess drastically from 0.95 eV to 1.11eV when the emptying gas pressure excess from 0.03 to 0.05 Torr. On other hand excess electron temperature from 0.9 to 1.01 eV with increasing sputtering power from 100 to 125 Watt, while the electron density decrease from 5.9×1014 to 4.5×1014 cm-3 with increasing sputtering power. and electron density decrease with increasing of pressure from 4.25×1014 to 2.80×1014 cm-3, But the electron density maximum values 5.9×1014 at pressure 0.03 Torr.

في هذا البجث، تم التحقق من الخصائص الأساسية لبلازما الترذيذ الماكنتروني باستخدام الهدف V2O5. تم إنتاج البلازما باستخدام الترذيذ الماكنتروني ببمجهز طاقة بالترددات الراديوية وغاز الاركون. تم قياس شدة الانبعاث الضوئي من الذرات والجذور في البلازما باستخدام مقياس الطيف الضوئي البصري، وكانت القمم التي ظهرت في جميع الأنماط متطابقة مع خطوط معيارية من قاعدة بيانات( NIST ) وتستخدم لتقدير معلمات البلازما لحساب كثافة الإلكترونات و درجة حرارة الإلكترون. تمت دراسة خصائص البلازما في ظروف التفريغ المختلفة. طاقة الترددات الراديوية تتراوح من 75 إلى 150 واط وضغط الغاز( 0.03 ، 0.05 و 0.007) تور. وجدنا أن كثافة خطوط الانبعاثات تزداد مع زيادة طاقة الترذيذ . و أن درجة حرارة الإلكترون زادت من )0.95 إلى 1.11) الكترون فولت عندما زاد ضغط غاز التفريغ من 0.03 إلى 0.05 تور.من جهة أخرى زادت درجة حرارة الإلكترون من ( 0.9 إلى 1.01 ) الكترون فولت مع زيادة طاقة الترذيذ من 100 إلى 125 واط ، بينما تنخفض كثافة الإلكترون من(5.4 – 4.5) x1014 cm-3 مع زيادة طاقة الترذيذ. ايظا كثافة الإلكترون تنخفض من x1014 cm-3(2.80 - 4.25) مع زيادة الضغط ، ولكن اقصى قيمة لكثافة الإلكترون كانت 3 cm- x1014 5.9 عند ضغط 0.03 تور .

Listing 1 - 6 of 6
Sort by
Narrow your search

Resource type

article (6)


Language

English (6)


Year
From To Submit

2019 (1)

2018 (2)

2017 (1)

2016 (1)

2013 (1)