Thin films of vanadium oxide nanoparticles doped with different concentrations of europium oxide (2, 4, 6, and 8) wt % are deposited on glass and Si substrates with orientation (111) utilizing by pulsed laser deposition technique using Nd:YAG laser that has a wavelength of 1064 nm, average frequency of 6 Hz and pulse duration of 10 ns. The films were annealed in air at 300 °C for two hours, then the structural, morphological and optical properties are characterized using x-ray diffraction (XRD),Field emission scanning electron microscopy (FESEM) and UV-Vis spectroscopy respectively. The X-ray diffraction results of V2O5:Eu2O3 exhibit that the film has apolycrystalline monoclinic V2O5 and triclinic V4O7 phases. The FESEM image shows a homogeneous pattern and confirms the formation of uniform nanostructures on the glasssubstrate. The type of the particle foundnanoparticles with different doping concentrations of Eu2O3. The optical energy gap increases with the increase of doping concentration and it varies from 2.67 eV to 2.71 eV. The prepared thin films are used to fabricate sensor against nitrogen dioxide gas. The dependence of sensitivity and response time on doping ratio and operation temperature of gas sensors has been studied, the maximum sensitivity was about 100%, the response time is equal to 24s and recovery time 16s for V2O5 doped 2% Eu2O3 at 50 °C.

تم في هذا البحث استخدام طريقة الترسيب بالليزر النبضي بواسطة ليزر Nd:YAG ذي الطول الموجي nm1064λ= وبمعدل تكرار Hz6 وفترة نبضة ns10 لترسيب أغشية رقيقة بنوعية عالية لاوكسيد الفناديوم النقية و المشوبه بأوكسيد اليوربيوم وبنسب مختلفة (0, 2, 4, 6, 8) wt. % على قواعد زجاجية ورقائق السليكون من النوع (111) وتم تلدين الغشاء بدرجة حرارة 300 درجة مئوية لمدة ساعتين. تم دراسة الخصائص التركيبية باستخدام حيود الاشعة السينية والمجهر الالكتروني والطوبوغرافية للسطح والخصائص البصرية باستخدام طيف الامتصاص للكيف المرئي والفق البنفسجية. بينت دراسة طيف حيود الاشعة السينية لأغشية V2O5 ذات التركيب النانوي وبتراكيزEu2O3مختلفة (0% -8 %) والتي تم تحضيرها باستخدام الترسيب بالليزر النبضي ان جميع الاغشيه المحضره كانت ذات تركيب متعدد التبلور وتبين أيضا ان الطور الذي ظهر في غشاءEu2O3كان أحادي الميل مع ظهور طور ثانوي و انقلاب في الطور الى V4O7. بينت صور المجهر الالكتروني ا شكال نانوية منتظمة الترسيب مع تغير النوع مع تغير نسبة التشويب. فجوة الطاقة البصريةتزداد بزيادة نسبة التشويب من 2.67 الى 2.71 الكترون فولت. تم استخدام الاغشية المحضرة لتصنيع متحسس لغاز اوكسيد النتروجين. تم دراسة تاثير تغيير النسبة ودرجة الحرارة على كل من التحسسية وزمن التحسس و زمن الرجوع. وجد ان اعظم تحسسية 100% وزمن تحسس 24 ثانية وزمن الرجوع 16 ثانية للعينة بنسبة 2% Eu2O3 وبدرجة حرارة 50 درجة مئوية.

Vanadium oxide --- gas sensor --- nanoparticles.

Decolorization of blue azo dye (Cibacron Blue FN-R) from simulated wastewater has been investigated as a function of solar photocatalysis process. The photocatalysis activity using different catalysis was compared. Different parameters affected the removal efficiency, including initial concentration of dye, pH of the solution, catalysis dosage, and H2O2 concentration, were evaluated to find out the optimum operation conditions. The results proved that, the optimal pH value for TiO2, V2O5 and ZnO were 2, 2, and 8 respectively and the best catalysis dosage was 500mg/L for TiO2, V2O5 and ZnO. In addition, the most efficient H2O2 concentration was 300,100, 100 mg/L for TiO2, V2O5 and ZnO respectively. The theoretical relationships described the photocatalysis process have been predicted for the three catalysis. It can be concluded, from these experiments, that the using of ZnO as a photocatalysis was found to be more efficient than TiO2 and V2O5 to remove blue azo dye from aqueous solution.

تم دراسة عملية ازالة اللون لصبغة الازو الزرقاء (Cibacron Blue FN-R) من مياه مخلفات مصنعة في المختبر باستخدام عملية التحفيز الضوئي الشمسي. تمت مقارنة كفاءة انواع مختلفة من عوامل التحفيز ومن ثم تقييم تأثير عدة عوامل مثل تركيز الصبغة الاولي، قيمة الاس الحامضي للمحلول، جرعة العامل المساعد المستخدم وتركيز بيروكسيد الهيدروجين المضاف وذلك لإيجاد أفضل قيم لهذه العوامل المؤثرة على نسبة الازالة. لقد تم التوصل الى ان أفضل قيمة للاس الحامضي للمحلول باستخدام اوكسيد التيتانيوم، اوكسيد الفناديوم واوكسيد الخارصين هي 2, 2, 8 على التوالي وأفضل جرعة للعامل المساعد المستخدم كانت 500ملغم/لتر لكل من اوكسيد التيتانيوم، اوكسيد الفناديوم واوكسيد الخارصين. أفضل تركيز لبيروكسيد الهيدروجين المضاف كانت 100,300 ,100 ملغم/لتر لهيدروكسيد التيتانيوم، اوكسيد الفناديوم واوكسيد الخارصين على التوالي. تم ايضا" ايجاد العلاقة النظرية الخاصة بوصف عملية التحفيز الضوئي لكل نوع من انواع العوامل المساعدة. من التجارب العملية يمكن استنتاج ان استخدام اوكسيد الخارصين كعامل مساعد لعملية التحفيز الضوئي هو الاكثر كفاءة" من اوكسيد التيتانيوم واوكسيد الفناديوم في ازالة صبغة الازو الزرقاء من المحلول المائي.

photocatalysis --- zinc oxide --- titanium oxide --- vanadium oxide --- azo dye