Article
Effect of Admixture Type on Compressive Strength and Modulus of Elasticity of Rubber- Tire - Waste Concrete
تاثير نوع المضاف على مقاومة الانضغاط ومعامل المرونة لخرسانة الاطارات المطاطية المستهلكة

Author: Khalid Battal Najim خالد بتال نجم
Journal: Anbar Journal of Engineering Sciences مجلة الأنبار للعلوم الهندسية ISSN: 19979428 Year: 2007 Volume: 1 Issue: 1 Pages: 88-103
Publisher: University of Anbar جامعة الانبار

Loading...
Loading...
Abstract

The presented work investigates the effect of addition admixtures (superplasticizer and polymer) to Chopped Worn-Out Tire concrete as a partial replacement of cement weight. Superpasticizer was addition by 4% and polymer (SBR) by 15%. The Chopped Worn-Out Tire (Ch.W.T.) addition to reference concrete with the three proportions as a Partial Replacement Ratio (PRR) of (25,25),(20,30),and (30,20) by volume of (sand and gravel) respectively. Three mixes were selected with above PRR for each type of admixture in additional to three mixes for Ch.W.T. concrete without admixtures and three reference mixes with admixtures without Ch.W.T. Thus, twelve mixes could be used in this investigation. Compressive strength and modulus of elasticity (static and dynamic) were tested. The test results indicated that the use of admixture led to significant improvement in concrete properties in general. Superplasticizer gave best results comparative with polymer, for example at 28 day the compressive strength of superplasticizer Ch.W.T. concrete Csp25,25 was 32.5 MPa, while compressive strength of polymer modified Ch.W.T. concrete CB25,25 was 28 MPa and compressive strength of Ch.W.T. concrete C25,25 was 21.2 MPa.

يدرس هذا البحث تأثير إضافة بعض أنواع المضافات (الملدن المتفوق والبوليمر) إلى خرسانة الإطارات المطاطية المستهلكة. حيث تم إضافة الملدن المتفوق بنسبة 4% والبوليمر بنسبة 15% من وزن الاسمنت. تم إضافة مفروم الإطارات المطاطية المستهلكة إلى الخلطات الخرسانية كجزء مستبدل من حجم الركام الخشن والناعم بثلاث نسب استبدال هي (25, 25), (20, 30) و (30, 20) (ركام خشن وناعم على التوالي). تم اختيار ثلاث خلطات بنسب الاستبدال أعلاه لكل مضاف إضافة إلى ثلاث خلطات بدون مضافات وثلاث خلطات مصدرية مع المضافات وبدون مفروم الإطارات وبذلك يكون مجموع الخلطات اثنا عشر خلطة. تم إجراء فحص مقاومة الانضغاط ومعامل المرونة ( الساكن والديناميكي), وقد أظهرت نتائج الفحص تحسن ملحوظ لخواص الخرسانة عند إضافة المضافات وكانت الأفضلية باستخدام الملدن المتفوق بشكل عام.فعلى سبيل المثال بعمر 28 يوم كانت مقاومة الانضغاط لخرسانة الإطارات الحاوية على الملدن المتفوق Csp25,25 32.5MPa بينما كانت مقاومة الانضغاط لخرسانة الإطارات المطورة بالبوليمر CB25, 25 هي 28 MPa وكانت مقاومة الانضغاط لخرسانة الإطارات بدون مضافات C25, 25 هي 21.2 MPa.


Article
EXPERIMENTAL STUDY FOR BEHAVIOR OF (WASTE CONCRETE FILLED STEEL TUBULER) COLUMNS SUBJECTED TO A STATIC AXIAL LOADS

Author: Zaid Ali Kadhim Alzaidi
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2017 Volume: 10 Issue: 3 Pages: 291-298
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

In this study, composite columns have been tested under axial load. The steel tubes were filled with waste concrete to perform the composite action. The specimens divided into two groups; square and circular columns. The diameter of the circular hallow columns was 7.5 cm with 2mm thickness, while the dimension of the square hallow columns was (7.5 cm × 7.5 cm) with 2mm thickness. For each group a column without waste concrete filled steel tubular (W.C.F.S.T) was tested to act as a reference column. Load-deflection curves were constructed for all specimens. The results indicate that the waste concrete filled steel tube has more capacity due to the composite action. The pattern of failure in circular sections was different from the failure pattern of the square ones.


Article
Re-using The By-product of Cement Industry (Cement Kiln Dust) To Produce The Concrete
(إعادة استخدام مخلف صناعة الاسمنت غبار الاسمنت) لإنتاج الخرسانة

Authors: Aseel Medulla Mohammad أسيل مدا لله محمد --- Nahla Naji Hilal نهلة ناجي هلال
Journal: Anbar Journal of Engineering Sciences مجلة الأنبار للعلوم الهندسية ISSN: 19979428 Year: 2010 Volume: 3 Issue: 2 Pages: 1-14
Publisher: University of Anbar جامعة الانبار

Loading...
Loading...
Abstract

The presented work investigates the effect of addition admixture (cement kiln dust) to concrete as a partial replacement of cement weight. Cement kiln dust was added by (10,30,50)% of cement weight.Four mixes were selected, three of them contain cement kiln dust (CKD) and one reference mix without any admixture for ages (7,28,90) days. Compressive strength ,flexural strength, ultra-sound velocity (UPV), slump, splitting tensile strength and static modulus of elasticity were tested.The test results indicated that the use of (CKD) led to significant decreasing in concrete strength in general and this decreasing increases with the increasing of (CKD), for example at 28 day the compressive strength of reference concrete (A) was 35 MPa, while the compressive strength of (B,C,D) contain (10,30,50)%CKD were (28,25,22) MPa respectively.

يدرس هذا البحث تأثير إضافة غبار الاسمنت إلى الخرسانة. حيث تم إضافة غبار الاسمنت بنسب (10, 30, 50) % من وزن الاسمنت. تم اختيار أربع خلطات واحدة منها بدون مضاف وثلاث منها مع المضاف . تم إجراء فحص مقاومة الانضغاط , مقاومة الانثناء, مقاومة الشد غير المباشر (الانفلاق), سرعة الموجات فوق الصوتية, الهطول ومعامل المرونة الاستاتيكي وقد أظهرت نتائج الفحص تناقصا ملحوظا لخواص الخرسانة عند إضافة المضاف وكان التناقص يزداد مع ازدياد نسبة المضاف بشكل عام. فعلى سبيل المثال بعمر 28 يوم كانت مقاومة الانضغاط للخرسانة الحاوية على غبار الاسمنت بنسب(10, 30, 50) % كالأتي ( 28, 25 , 22 ) ميكا باسكال وكانت مقاومة الانضغاط للخرسانة المرجعية بدون إضافات (35) ميكا باسكال


Article
Mechanical Properties of High Strength Mortars Made with Fine Waste Concrete Aggregates and Ground Granulated Blast Furnace Slag

Author: Ali Hassoon Nahhab
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2018 Volume: 26 Issue: 2 Pages: 338-355
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

The mechanical properties of high strength mortars produced with fine waste concrete aggregate (FWCA) and GGBFS were investigated. The natural sand was replaced by FWCA with different levels, namely 0, 25, 50, 75, and 100%. The ordinary Portland cement (OPC) was substituted by GGBFS with 0, 30, and 60% by weight. To satisfy the requirements of high strength, all the mortar mixes were made with a 0.25 w/b ratio. The hardened mortars were tested for compressive strength, splitting tension, and fracture parameters at different ages. The experimental findings showed that the mixtures with FWCA showed lower strength, fracture energy and toughness compared to the corresponding reference mixes at a given age and GGBFS content. The 30% replacement of OPC by GGBFS improved the strengths of all mixes at 28 and 90 days. Moreover, the use of 30% GGBFS counterbalanced the strength decrement due to the use of the FWCA such that the mixtures with FWCA and GGBFS showed strengths comparable to or even exceeded the strengths of the mixtures made with natural sand only.

تم خلال هذا البحث دراسة الخواص الميكانيكية للمونة عالية المقاومة المنتجة من ركام مخلفات الخرسانة ومطحون خبث الفرن النفاخ. استبدل الركام الناعم الطبيعي بركام مخلفات الخرسانة بنسب مختلفة هي 0، 0.25، 0.5،0.75 و 100%. استبدل السمنت البورتلاندي الاعتيادي بنسب مختلفة من مطحون الخبث هي 0،30 و60%. كانت نسبة الماء الى المادة الرابطة هي 0.25 لتحقيق متطلبات المقاومة العالية. تم اجراء فحوصات مقاومة الانضغاط والشد الانشطاري ومعاملات الكسر على المونة المتصلبة باعمار مختلفة. بينت النتائج المختبرية بان الخلطات الحاوية على ركام مخلفات الخرسانة قد ابدت مقاومة وطاقة كسر وصلادة اقل من الخلطات المرجعية عند تثبيت نسبة مطحون الخبث. كما ان استخدام مطحون الخبث بنسبة 30% قد حسن المقاومة لجميع الخلطات في الاعمار 28 و 90 يوم. بالإضافة الى ذلك فان استعمال تلك النسبة من مطحون الخبث قد قلل من او ازال تماما التأثير السلبي لركام مخلفات الخرسانة بحيث ان الخلطات الحاوية على مطحون الخبث وركام مخلفات الخرسانة قد ابدت مقاومة مماثلة او حتى اعلى من تلك الحاوية على الركام الطبيعي فقط.

Listing 1 - 4 of 4
Sort by
Narrow your search

Resource type

article (4)


Language

English (3)

Arabic and English (1)


Year
From To Submit

2018 (1)

2017 (1)

2010 (1)

2007 (1)