Carbon nanotubes with different shapes have been prepared using water assisted chemical vapor deposition technique (WA-CVD). Different thicknesses of nickel layers were sputtered on alumina substrate. These were treated under high temperature (700 °C) at hydrogen gas to grow nickel nanoparticles (Ni-NPs). Tube furnace (single type), argon and acetylene gases were used for Carbon Nanotubes (CNTs) growth. The FESEM, TEM, HRTEM, Raman spectroscopy, and XRD were used for characterization of the carbon product. The results show that Water Assisted CVD produces CNTs with no trace of amorphous carbon. Nickel catalyst thicknesses (0.5,1,3,3.45,6.8,100 nm) offer different shapes of carbon nanotubes (single walled carbon nanotube, plain MWCNT, helical carbon nanotube, carbon nanofiber).

تم تحضير انابيب الكاربون النانوية باشكال مختلفة باستخدام طريقة ترسيب البخار الكيميائي بمساعدة الماء. حيث تم ترسيب طبقات مختلفة السمك من النيكل بطريقة التذرية على اساس من الالومينا. وقد تمت معاملتها بالهيدروجين وعند درجة حرارة عالية (700 °C). حيث تم استخدام فرن انبوبي احادي و غاز الاستيلين وغاز الاركون لتنمية انابيب الكاربون النانوية. وتم استخدام المجهر الالكتروني الماسح عالي الدقة والمجهر الالكتروني النافذ والمجهر الالكتروني النافذ عالي الدقة ومطياف رامان والاشعة السينية المنحادة لتشخيص الكاربون الناتج. بينت النتائج بان استخدام الترسيب البخار الكيميائي بمساعدة الماء ينتج انابيب كاربون بدون وجود اثر للكاربون غير المتبلور.وان اختلاف سمك طبقة المادة المساعدة (0.5,1,3,3.45,6.8,100 nm)اعطت اشكال مختلفة من انابيب الكاربون النانوية وهي انابيب الكاربون احادية الجدران ومتعددة الجدران المستوية والحلزونية، والياف الكاربون النانوية.

Carbon nanotube --- Water assisted CVD --- Ni catalyst