Article
Effect of Ageing Time on Adhesive Wear of AL Alloy AA6061-T6

Author: Malik Niama Hawas
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2013 Volume: 11 Issue: 4 Pages: 145-152
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

In this study the effect of artificial aging time on adhesive wear of AA(6061-T6) aluminum alloy was investigated for the specimens groups (A , B , C and D)which manufactured in the dimensions of ( 20*10)mm according to ASTM, heat treatment was implemented to specimens groups( B , C and D) which include solution zing at temperature of 5000 C for (1 hour) then quenching in water and artificial aging for (1,3,5 ,hr.) at 1800C The resulting phases after each heat treatment was tested by x –ray diffraction and microstructure was also examined to understand the nature of structure then hardness test was implementedAdhesive wear test have been conducted on aluminum alloy AA 6061 T6 at variable (time ,loads, and sliding speed ) using pin on disc method. The results showed that increasing of aging time increases hardness then decreasing wear rate.

يهدف البحث الى دراسة تاثير زمن التعتيق الصناعي على مقاومة البلى الالتصاقي لسبيكة المنيومAA 6061- T6 حيث تم تصنيع عينات اسطوانية الشكل بالابعاد (20*10) mm وفق المواصفة القياسية ASTM ثم تم تصنيفها الى مجاميع ( A,B ,C ,D) بعدها اجريت معاملة حرارية على هذه المجاميع حيث تضمنت تسخين المعدن الى درجة حرارة 500 درجة مئوية لمدة ساعة ثم التبريد السريع بالماء بعدها اجريت عملية تعتيق صناعي بتسخينها الى 180 درجة مئوية لفترات (1,3,5) ساعة على التوالي ثم تم تصوير البنية المجهرية لمعرفة التركيب المجهري لكافة العينات وكذلك اجري اختبار حيود الاشعة السينية لمعرفة الاطوار المترسبة بعد المعاملات الحرارية, اجري اختبار الصلادة بطريقة Vickers لبيان تاثير المعاملات على الصلادة وكذلك اجري اختبار البلى الالتصاقي عند زمن وحمل وسرعة متغييرين با ستخدام طريقة pin on discلمعرفة تاثير المعاملات الحرارية على مقاومة البلى الالتصاقي ومن النتائج التي تم الحصول عليها وجد ان الصلادة ومقاومة البلى الالتصاقي تزداد بزيادة زمن التعتيق


Article
Evaluation the Mechanical Properties of Shot Peened TIG Welded Aluminum Sheets
تقييم الخواص الميكانيكية لصفائح الالمنيوم الملحومة بطريقة قطب التنكستن المحمي بالغاز الخامل والمعاملة بطريقة القذف بالكرات

Loading...
Loading...
Abstract

A tungsten inert gas (TIG) welding is one of the most popular kinds of welding used to join metals mainly for aluminum alloys. However, many challenges may be met with this kind of joining process; these challenges arise from decay of mechanical properties of welded materials. In the present study, an attempt was made to enhancing the mechanical properties of TIG weld joint of 6061-T6 aluminum alloy by hardening the surfaces using shoot peening technique. To optimize the shoot peening process three times of exposure (5, 10, and 15) min. was used. All peened and unpeened, and welded and unwelded samples were characterized by metallographic test to indicate the phase transformation and modification in microstructure occurring during welding process. Tensile test and Vickers micro-hardness measurements were performed for all samples to investigate the effect of shoot peening on mechanical properties of welded aluminum. The results indicated a significant improvement in properties for peened welded and unwelded samples compared with those unpeened one. Also, the results showed that the tensile and micro-hardness properties were increased with increasing the time of exposure to 15 min. due to generation of compressive residual stresses at surface.

تعتبر عملية اللحام بقطب التنكستن المحمي بالغاز الخامل (TIG) من اكثر انواع اللحام انتشارا والمستخدمة لربط المعادن وخصوصا سبائك الالمنيوم. رغم هذا فهناك العديد من التحديات والتي ممكن مواجهتها عند استخدام هذا النوع من عمليات الربط. هذه التحديات ناشئة من انخفاض الخواص الميكانيكية للمواد الملحومة. في الدراسة الحالية تم عمل محاولة لتحسين الخواص الميكانيكية لوصلة من سبائك الالمنيوم (6061-T6) ملحومة بطريقة اللحام بقطب التنكستن المحمي بالغاز الخامل (TIG) من خلال تصليد السطح باستخدام تقنية القذف بالكرات. وللوصول الى الاسلوب الامثل في عملية القذف بالكرات تم استخدام ثلاث ازمان للتعرض (5,10,15) دقيقة. تم توصيف جميع العينات المعاملة بالقذف بالكرات وغير المعاملة، الملحومة وغير الملحومة من خلال فحص سطح المعدن لبيان التحولات الطورية والتغيرات الحاصلة خلال عملية اللحام. تم اجراء فحص الشد وقياس صلادة فيكرز المجهرية لجميع العينات لدراسة تاثير القذف بالكرات على الخواص الميكانيكية لملحومات الالمنيوم. بينت النتائج تحسن ملموس في خواص العينات المعاملة بالقذف بالكرات الملحومة وغير الملحومة مقارنة بالعينات الغير معاملة. بينت النتائج ايضا ان خواص الشد والصلادة المجهرية قد ازدادت مع زيادة زمن التعرض الى 15 دقيقة نتيجة لتوليد مستويات اعلى من اجهادات الضغط المتبيقية عند السطح.