Effect of Wax Burn-Out Heating Temperature on The Compressive Strength of Casting Dental Alloy Investment

Author: Lamia T Rejab
Journal: Al-Rafidain Dental Journal مجلة الرافدين لطب الأسنان ISSN: 18121217 Year: 2008 Volume: 8 Issue: 2 Pages: 197-204
Publisher: Mosul University جامعة الموصل

Loading...
Loading...
Abstract

Aims: To evaluate the effect of the burn-out heating on the compressive strength of investment materials.Materials and Methods: Three commercial investment materials were used in this study. Seventy two cylindrical shape specimens were prepared to evaluate the compressive strength of the investment materials at room temperature (cold strength) and at two different burn-out heating temperatures : 700 oC and 1000 oC (hot strength). Three groups were prepared according to tested investment materials, The specimens were then subdivided into three subgroups according to burn-out heating temperatures,eight specimens for each subgroup. The compressive strength (kg /cm2) was evaluated by using Instron testing machine. Mean values were compared statistically with one way analysis of variance (ANOVA),Duncan , s multiple range test and t-test to determine the significant difference among the tested groups at (p<0.05) level of significance .Results: The results showed that there is a significant difference of the means value of the compressive strength among the three tested investment materials. The compressivestrength value significantly decreased with increasing burn-out heating temperature. Conclusion:The result of this study showed that the increase of burn-out heating had a significant decrease the compressive strength of the investment materials, and cold compressive strength gives an indicationof the hot strength .

Listing 1 - 1 of 1
Sort by
Narrow your search

Resource type

article (1)


Language

English (1)


Year
From To Submit

2008 (1)