Article
Effect of Nanocomposites TiO2 addition on the Dielectric Properties of Epoxy resin
تأثير متراكبات النانو بإضافة TiO2¬ على خواص العزل لراتنج الأيبوكسي

Loading...
Loading...
Abstract

Sheets of Epoxy (EP) resin with addition of TiO2 of grain size (1.5μm, and 50nm) and weight percentage (1%, 3%, and 5%) were prepared. Discs of 20mm diameter and 3mm thickness were cut for dielectric measurements. Dielectric properties (dielectric constant, dispassion factor and electrical conductivity) over the frequency range 102 -106 Hz were measured.Comparison was made between the effect of micro and nano particles of TiO2 on the dielectric properties of EP composites with different weight percentage. Epoxy composites with micro sized particles of TiO2 were observed to have the better values of dielectric properties.

في هذا البحث تم تحضير صفائح راتنج الايبوكسي Ep باضافة ثنائي اوكسيد التيتانيوم TiO2 بمقاس حبيبي ((1.5μm, 50nm وبنسب وزنية مئوية مختلفة (1%, 3%, 5%). تم قطع اقراص بقطر 20mm وسمك 3mm من المادة المحضرة ولذلك لغرض القياسات العزلية. الخواص العزلية (ثابت العزل وعامل الفقد والتوصيلية الكهربائية) اجرت القياسات لمدى من الترددات بين 102 -106 Hz.تم كذلك مقارنة تأثير الجسيمات TiO2 من ابعاد النانومتر والمايكرمتر على الخصائص العزلية من متراكبات الايبوكسي وبنسب وزنية مختلفة. وتبين من النتائج ان الجسيمات TiO2 بابعاد المايكرو متر ذات خصائص عزلية افضل


Article
Effect of triammonium orthophosphate on fire retardationof Epoxy resin reinforced with wood flour
تأثير ثلاثي أمونيوم أورثو فوسفات على مقاومة الاحتراق لراتنج الايبوكسي المسلح بنشارة الخشب

Authors: Mohammed. H. Mokhilif محمد هلول مخيلف --- Harith. I. Jaffer حارث ابراهيم جعفر
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2011 Volume: 8 Issue: 2عدد خاص بمؤتمر الفيزياء Pages: 671-675
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Epoxy resin reinforced by 30% of wood flour was prepared as a composite . Triammonium orthophosphate as a flame retardant was added to composite at weight percentages of ( 0 , 2 , 3 , 5 , 7 , and 10 ) % . Hand lay-up technique was used to prepare sheets from that composite. The results indicated that the rate of burning decreases with increasing the weight percentage of that flame retardant. And the limiting oxygen Index (LOI ) increases with increasing concentration of that flame retardant .

تم دراسة تأثير اضافة ثلاثي أمونيوم اورثو فوسفات على لهوبية راتنج الايبوكسي المسلح بـ 30% من نشارة الخشب . استخدم المضاف بنسب مئوية ( 0 , 2 , 3 , 5 , 7 , 10 ) % . ثم حضر صفائح من المتراكب بالطريقة اليدوية لصب مكبوسات . قد اظهرت النتائج ان معدل احتراق العينات يتناقض مع زيادة النسب المئوية للمضاف وان معامل الاوكسجين المحدد (LOI ) يزداد مع زيادة تركيز المضاف .


Article
Fatigue Behavior Of Chopped Carbon Fiber Reinforced Epoxy Composites
سلوك الكلل لمتراكب الايبوكسي المدعم بألياف الكاربون المقطعة

Authors: Ekram .A.AL-Ajaj أكرام عطا العجاج --- Mohammed Hussein B. Hassan محمد حسين بشار
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2010 Volume: 8 Issue: 11 Pages: 110-117
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Hand-lay up method was used to prepare the samples made of epoxy (EP) as a matrix reinforced with chopped carbon fibers (CCF). The fatigue behavior of epoxy resin /chopped carbon fiber composites was studied with different weight percentage of chopped carbon fibers (2.5%,5%,7.5%,10%,12.5%). The fatigue test was carried out under alternate bending method, which was made by applying sinusoidal wave with constant displacement (15mm), stress ratio R=-1,and loading frequency 10Hz, which is believed to give a negligible temperature rise during the test. The results of the maximum stress, fatigue strength, fatigue limit and fatigue life of the tested composites are calculated from stress(S)-number of cycles(N) (S-N) curves.
It was shown that increasing weight percentage of chopped carbon fibers increase the values of maximum stress for all composites, while the values of fatigue strength, fatigue limit and fatigue life increasing for all composites except the composite with reinforcing weight 12.5%, which was subjected to rapid failure (fracture). This failure could be due to the debonding of the chopped carbon fibers from the matrix epoxy.

حضرت العينات للفحص بطريقة التشكيل اليدوي من مادة الايبوكسي كمادة أساس ودعمت بألياف الكاربون المقطعة ( chopped carbon fiber(CCF.تمت دراسة سلوك الكلل لمادة الايبوكسي ومتراكباتها المدعمة بأليـاف الكـاربون المقطعة وبنسب وزنية مختلفة هي 10%, 7.5%, 5%, 2.5% و%12.5 بطريقة الثني المتناوب. أجري فحص الكلل بطريقة الثني المتناوب وبتسليط حمل جيبي بإزاحة بقيمة ثابتة مقدارها 15mm وبنسبة أجهاد R=-1 وبتردد 10Hzوالتي يعتقد بأنها تمنع أي زيادة في درجة الحرارة. وتم حساب أعظم جهد, مقاومة الكلل, حد الكلل وعمر الكلل لكل المتراكبات من منحنيات الإجهادS)) مع عدد الدورات N)) وأظهرت نتائج الفحص تأثير زيادة نسبة التدعيم على سلوك الكلل للعينات وذالك بزيادة قيمة أعظم جهد لجميع المتراكبات وكذلك بزيادة قيم مقاومة الكلل,حد الكلل وعمر الكلل لجميع العينات باستثناء العينة ذات النسبة الوزنية 12.5% والتي تتعرض للفشل السريع(الكسر) ويحدث الكسر بسبب عدم الترابط القوي بين ألياف الكاربون ومادة الأساس الايبوكسي.


Article
Mathematical Model of Autoclave Curing of Epoxy Resin Based Composite Materials
الموديل الرياضي لعملية إنضاج متراكبات الأيبوكسي في جهاز الاوتوكليف

Authors: Adnan A. Abdul Razak --- Najat J. Salah --- Hassen Sh. Majdi
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2007 Volume: 25 Issue: 7 Pages: 828-835
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Polymer matrix composites using thermosetting resins as the matrix areincreasingly finding use in several applications. Process modelingdescribing the governing curing has played an important role, inimproving the fundamental understanding and development ofcomposite fabrication techniques. In present work, the thermokineticinvolved in the autoclave curing of fiber-reinforced epoxy has beenstudied by means of a computer program, using the transient heatconduction equation coupled with kinetic equation, and the initial andboundary conditions. In the analysis the cure assembly is assumed toconsist of a tool plate, composite laminate. The temperature distributionand the degree of reaction are obtained as a function of position andtime.

يشهد استخدام المواد المتراكبة الايبوكسية تطورا كبير ا. ويلعب الموديل الرياضي لعمليةالإنضاج دورا كبيرا في فهم هذه العملية وتحسينها وتطويرها .تم أيجاد مود يل رياضي يقوم بحساب درج ات الحرارة و درجة الإنضاج كدالة من الزمن( un steady state energy و الموضع ويشمل هذا الموديل على حل معادلة الطاقةنتيجة ( generated heat ) مع إضافة حدود تمثل الحرارة المتولدة equation )تصلب الايبوكسي . ويعتمد الموديل الرئيسي على موديل ديناميكية التفاعل الأيبوكسيوالذي تم دراسته باستخدام جهاز المسح التفاضلي


Article
Comparative Differential Thermal Analysis of Epoxy Resin blends with Amic Acid-Copper Complexes
التحليل الحراري التفاضلي المقارن لسبائك راتنج الايبوكسي مع حوامض الاميك ومعقداتها النحاسية

Author: Akram A. Mohamed أكرم عزيز محمد
Journal: Tikrit Journal of Pure Science مجلة تكريت للعلوم الصرفة ISSN: 18131662 Year: 2008 Volume: 13 Issue: 1 Pages: 197-200
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

This work deals with the thermal behaviour of epoxy resin blended with eleven mono-and dibasic maleamic acids and their copper complexes. DTA thermograms of all blands show two distinct exotherms (T2 and T4) at high temperatures if compared with those of epoxy alone. Values of T1 and T4 in copper containing blends are higher than their isomers in mono amic acids, while the inverse was observed in copper-diamic acid blends. The presence of copper in the blend shifts the position of the oxidation exotherm (T4) to relatively higher temperatures.

يشتمل البحث على دراسة حرارية تفاضلية مقارنة لمجموعة من سبائك راتنج الايبوكسي مع أحد عشر نوعاً من حوامض الاميك الأحادية والثنائية المجموعة الكاربوكسيلية وكذلك مع معقداتها مع النحاس. أشارت الدراسة أن معظم السبائك أعطت انبعاثين حراريين كبيرين T2 و T4 في درجات حرارية أعلى مما هي في حالة راتنج الايبوكسي منفرداً. كما لوحظ أن قيم T1 و T4 في السبائك الحاوية على فلز النحاس مع حامض أحادي أعلى من نظائرها المحتوية على الفلز مع حامض ثنائي المجموعة. كما أشارت الدراسة أن وجود النحاس في السبائك يحرف قيم T4، والتي تمثل انبعاث الأكسدة، إلى درجات حرارية عالية نسبياً


Article
The Rheological Properties of Isothermal Curing of DGEBA/ TETA Epoxy System
دراسة الخواص الريولوجية بثبوت درجة الحرارة لعملية تقسية راتنج الايبوكسي بأستخدم مادة تراي اثلين تترا امين

Authors: Adnan A. Abdul Razak --- Najat j. Saleh --- Maryem Emad
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 5 Part (A) Engineering Pages: 1095-1112
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this study viscosity (η) of diglycidyl ether of bisphenol A / triethylenetetramine (DGEBA/TETA) system were measured through curing using a Brookfield viscometer at four different temperatures (30, 45, 60 and 80) °C. The measurements were carried out for two hardener/resin ratios (13 and 20) phr. The gel time was calculated for each hardener/resin ratio formulation; from the viscosity experimental data. The results showed that the gel time decrease with increasing curing temperature for each hardener/resin ratio formulation. Viscosity profiles were described by a model based on the Boltzmann function. The fitted results agreed well with the experimental values.

في هذا البحث تم قياس اللزوجة لنظام مكون من (DGEBA/TETA ) خلال عملية الانضاج بأستخدام مقياس اللزوجة من نوع Brookfieldفي اربع درجات مختلفة (30,45,60,80) م0 . تم أخذ القياسات باستخدام نسبتين للراتنج / المصلد وهما (13) و(20) جزء من المائة .تم حساب زمن التصلب gel time)) لكل نسبة من الراتنج/ المصلد من قياسات اللزوجة . أظهرت النتائج بان زمن التصلد يزداد مع زيادة درجة الانضاج لكل نسبة من نسب الراتنج/ المصلد . تم وصف منحنى اللزوجة بموديل يعتمد على موديل (Boltzman) وتم مطابقة النتائج المستخلصة من الموديل مع النتائج المختبرية وظهر تطابق كبير بينهما .

Keywords

Epoxy Resin --- Curing --- Rheology --- Hardener


Article
Structure dependence of gamma ray irradiation effects on polyurethane and epoxy resin studied by PAL technique
دراسة تأثير اشعة كاما على البنية التركيبية لبولي يوراثين وراتنج الايبوكس باستخدام تقنية عمر فناء البوزترون

Author: Hayder S. Hussain حيدر سليم حسين
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2015 Volume: 13 Issue: 27 Pages: 157-163
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Positron annihilation lifetime (PAL) technique has been employed to study the microstructural changes of polyurethane (PU), EUXIT 101 and epoxy risen (EP), EUXIT 60 by Gamma-ray irradiation with the dose range (95.76 - 957.6) kGy. The size of the free volume hole and their fraction in PU and EP were determined from ortho-positronium lifetime component and its intensity in the measured lifetime spectra. The results show that the irradiation causes significant changes in the free volume hole size (Vh) and the fractional free volume (Fh), and thereby the microstructure of PU and EP. The results indicate that the γ-dose increases the crystallinity in the amorphous regions of PU and increase the cross-linking of EP.

استخدمت تقانة عمر فناء البوزترون لدراسة التغيرات في البنية المجهرية الناتجة من تعرض البولي يوراثين(EUXIT 101) و راتنج الايبوكسي (EUXIT 60) الى جرع من اشعة كاما ضمن المدى (95.76- 957.6) كيلوكري. تم حساب حجم الفجوات الحرة و نسبة الفجوات الحرة في البولي يوراثين والايبوكسي من خلال مركبة عمر البوزترونيوم وشدته في طيف عمرالفناء.بينت النتائج بان معدل الاشعاع يسبب تغيرات بليغة في مقدار حجم الفجوات الحرة و نسبة الفجوات الحرة، وبالتالي التغيرات في البنية المجهرية. تظهر النتائج انه بزيادة جرع اشعة كاما يزداد تبلور مادة البولي يوراثين ويزداد تشابك اواصر الايبوكسي.


Article
A Study of Wear Rate Epoxy Resin filled with SiO2 particle and Glass fibers
دراسة معدل البلى لراتنج الايبوكسي المضاف اليه دقائق السليكا والياف الزجاج

Authors: Nadia A. Ali نادية عباس علي --- Sinaa I.Husaen سيناء ابراهيم حسين --- Harith I. Jaffer حارث ابراهيم جعفر
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2011 Volume: 8 Issue: 2عدد خاص بمؤتمر الفيزياء Pages: 689-693
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This research is devoted to study the effect of different in weight percentage of Sio2 particles and glass fibers (5, 10, 15, 20) wt. % on the wear rate epoxy resin.The results show that the value of hardness increase with the increase for the weight percentage of reinforcing particles and fibers, while the wear rate decrease with the increase the load level of the reinforcing particles and fibers . The largest value of the hardness, and the lowest value of the wear rate for epoxy reinforced with 20% of SiO2, the wear rate increase in general with increasing the applied load.

يهدف البحث الى دراسة اضافة دقائق السليكا والياف الزجاج بنسب وزنية (5و10و15و20)% معدل البلى لراتنج الايبوكسي بينت النتائج بان الصلادة تزداد بزيادة نسب اضافة مواد التقوية بينما معدل البلى يقل مع زيادة نسب اضافة مواد التقوية ,حيث اعلى قيمة للصلادة واقل قيمة لمعدل البلى كانت لمتراكب الايبوكسي المقوى بنسبة 20% من السليكا وان معدل البلى بصورة عامة يزداد بزيادة الحمل المسلط

Keywords

epoxy resin --- glass fibers --- sio2 --- wear rate


Article
Evaluation of some physical properties of the copolymerized temporary crown and bridge auto–cured acrylic resin (Reinforcement)

Authors: Akram A Mohammad --- Nadiaa H Hasan --- Lamia T Rejab
Journal: Al-Rafidain Dental Journal مجلة الرافدين لطب الأسنان ISSN: 18121217 Year: 2007 Volume: 7 Issue: 2 Pages: 160-165
Publisher: Mosul University جامعة الموصل

Loading...
Loading...
Abstract

Aims: To evaluate some of the physical properties which are transverse strength, tensile strength,surface hardness, water sorption and solubility of the auto–cured acrylic resin when copolymerizedwith epoxy resin at two different ratios 10% and 20% of its weight and then compared with that ofauto–cured alone and heat–cured acrylic resin alone. materials and methods: The tested samples weredivided into four groups according to the materials to be used and the samples of each group weresubdivided according to the test to be done. The samples were prepared according to ADASpecification No. 12. Statistically analysis of the physical properties was with (ANOVA) and Duncan'smultiple range test to determine significant different at (p ≤ 0.05 ) level of significance, and the meanvalue of the water sorption and solubility ratios compared with accepted limit of ADA SpecificationNo. 12. Results: The transverse strength, tensile strength and surface hardness in this study showed thatthere was a highly significant difference between the four tested groups. The result appeared improvingof the mechanical properties and decreasing the ratio of water sorption and solubility of the auto–curedacrylic resin and the resin was reinforced when copolymerized at 10%, but the values still not reachedthat of the heat–cured acrylic resin and they became worse when copolymerized at 20%.


Article
Study the Effect of Some Solutions on Epoxy Resin & Calculate Diffusion Coefficient of Solution.
دراسة تأثير بعض المحاليل على راتنج الايبوكسي وحساب معاملات الانتشار لهذه المحاليل.

Author: Khalil T. Hassan خليل ثابت حسان
Journal: Journal of university of Anbar for Pure science مجلة جامعة الانبار للعلوم الصرفة ISSN: ISSN: 19918941 Year: 2010 Volume: 4 Issue: 1 Pages: 65-71
Publisher: University of Anbar جامعة الانبار

Loading...
Loading...
Abstract


Abstract: Specimen of Epoxy resin have surface area (1cm*1cm) immersed in several individual solvent (0.5% NaoH), (1% NaOH),(2.5% H2SO4), (5%H2SO4),(2.5%HCl), (5% HCl). For long time (three years). The specimen's masses were measured before and after immersion in solutions. Diffusivity and diffusion coefficient of solutions in epoxy resin measured from the relation of the change of specimen weight and the square rout of time.Photograph of the specimen surface have taken by using optical microscope and digital camera. Shoor Hardness test was used to obtain the change of Hardness properties after pot in solvent. The result obtained illustrate the different effect of these solution in the surface of specimen that effect in hardness and diffusion coefficient.

الخلاصة:-في هذا البحث تم غمر عینات مصنوعة من ا رتنج الایبوكسي ذات أبعاد مساحة مقطع ( ١سم* ١سم) في محالیل مختلفةكل على حدة وبت ا ركیز مختلفة وهي( ٠.٥ % هیدروكسید الصودیوم)و( ١% هیدروكسید الصودیوم)و ( ٢.٥ %وحامضالكبریتیك)و( ٥%وحامض الكبریتیك) و( ٢.٥ %حامض الهیدوكلوریك)و( ٥%حامض الهیدوكلوریك) لفترة زمنیة طویلة ( ثلاث سنوات)وتم وزن النماذج قبل وبعد الغمر بفت ا رت زمنیة مختلفة .تم إیجاد الانتشاریة للمحالیل وحساب معامل الانتشار لها من خلال رسم العلاقةبین التغیر في وزن العینات والجذر ألتربیعي للزمن .تم التقاط صور لأسطح العینات باستخدام المجهر الضوئي والكامی ا ر الالكترونیة.لقدأظهرت النتائج التأثیر المختلف للمحالیل على العینات هذا التأثیر ظهر بشكل واضح عل سطوح العینات وعلى قیم معامل الانتشارلهذه المحالیل.

Listing 1 - 10 of 66 << page
of 7
>>
Sort by
Narrow your search

Resource type

article (66)


Language

English (52)

Arabic (7)

Arabic and English (4)


Year
From To Submit

2019 (5)

2018 (7)

2017 (6)

2016 (4)

2015 (8)

More...