Article
THE EXPERIMENTAL STUDY AND MATHEMATICAL MODEL OF THE EFFECT OF ALUMINA PARTICLES REINFORCEMENT ON MECHANICAL PROPERTIES OF EPOXY
دراسة عملية وموديل رياضي لتأثير التقوية بدقائق الالومينا على الخواص الميكانيكية للايبوكسي

Loading...
Loading...
Abstract

This article describes some mechanical properties of alumina-filled epoxy composites. In this work, the epoxy matrix was reinforced with increasing amount of alumina particles in the range of 0-40% by weight with different particle size (d≤8, 18≤d≤25, 33≤d≤45, 50≤d≤62)µm. From the flexural test results, it was observed that the flexural modulus increases with increasing α-alumina content from 10 to 40 wt%. At the same time, the results indicated that there are no much effect on the flexural modulus with change the particle size in the range of (d≤8, 18≤d≤25)µm. The highest value of flexural modulus was recorded with 40 wt% of α-alumina content and (d≤8)µm particle size. It was also found that the 40 wt% alumina content and (d≤8)µm particle size recorded the highest value of fracture toughness (Gc), fracture toughness (Kc), hardness (HB), and wear resistance which were improved by (253%, 282%, 230%, and 82%), respectively. Also, in this work a mathematical modeling is implemented and regression equations are obtained by using ( SPSS ) software to predict the properties of alumina filled epoxy composites. Comparing the predicted and measured values gives high prediction accuracy. The accuracy of prediction has been (90.13%, 85.95%, 90.28%, 89.76%, and 84.36%) for flexural modulus, toughness, fracture toughness, hardness, and wear rate respectively.

يصف هذا ألبحث بعض الخواص الميكانيكية لمتراكبات الايبوكسي المقواة بدقائق الالومينا. حيث تم في هذا البحث اضافة دقائق الالومينا لتقوية راتنجات الايبوكسي بنسب وزنية مختلفة (0-40)% مع احجام حبيبية مختلفة (d≤8, 18≤d≤25, 33≤d≤45, 50≤d≤62) مايكرومتر. بينت نتائج اختبار الانحناء زيادة قيمة معامل الانحناء بزيادة نسبة الالومينا. وفي نفس الوقت بينت النتائج عدم وجود تأثير كبير لتغيير الحجوم الحبيبية في حدود(d≤8, 18≤d≤25)مايكرومترعلى قيمة معامل الانحناء. أعلى قيمة لمعامل الانحناء تم الحصول عليها عند اضافة الالومينا بنسبة40 % من الوزن بحجم حبيبي (d≤8) مايكرومتر. من ناحية اخرى فقد وجد ايضا أن اعلى القيم للمتانة, متانة الكسر, الصلادة, ومقاومة البلى والتي تحسنت بمقدار( 253%، 282%، 230%، و82% ) على التوالي قد سجلت ايضا عند اضافة الالومينا بنسبة40 % وحجم حبيبي (d≤8) مايكرومتر. تم ايضا في هذا البحث استخدام موديل رياضي وتم الحصول على معادلات الانحدار باستخدام برنامج (SPSS) لغرض التنبؤ بخواص متراكبات الايبوكسي المقواة بالالومينا. بينت النتائج من خلال المقارنة بين القيم المتنبئة والحقيقية إن هذا البرنامج يعطي دقة تنبؤ عالية. فقد كانتدقة التنبؤ بمقدار (90.13%, 85.95%, 90.28%, 89.76%, 84.36%) لمعامل الانحناء، المتانة،ومتانة الكسر، الصلادة، ومعدل البلى على التوالي.


Article
THE FLEXURAL PROPERTIES OF IRAQI-BAUXITE FILLED EPOXY COMPOSITES
خواص الحني لمادة مركبة اساسها راتنج الايبوكسي المدعم بحبيبات البوكسايت العراقي

Author: Thaer Abdalwahab Shihab ثائر عبد الوهاب شهاب حمد
Journal: AL-TAQANI مجلة التقني ISSN: 1818653X Year: 2014 Volume: 27 Issue: 4 Pages: E51-E61
Publisher: Foundation of technical education هيئة التعليم التقني

Loading...
Loading...
Abstract

This study is focus on the mechanical properties of Iraqi bauxite filled epoxy composites. In this study, bauxite content was varied systematically to evaluate their effect on the properties of the composites. The composites were prepared using gravity molding technique. From the flexural test results, it was observed that the flexural modulus increases with increasing bauxite content from 1.25 to 40 wt% with 40 wt% of bauxite content recorded the highest value of flexural modulus (4.93 GPa). In contrast, the flexural strength of the composites decreases with rising bauxite content till 20% and then increases with bauxite content increase from 20 to 40%. It has also been demonstrated that the pattern of flexural stress-strain curve is also affected with addition of bauxite particles. The flexural strain at break and the toughness decreases with bauxite content increase.These types of composite materials are suitable for use in braking systems with moderate loads, but vehicle manufacturers are tending to design increasing number of vehicles with more braking power, also used in textile for heavy duty stores.

تتمحور هذه الدراسة على الخواص الميكانيكية للمواد المركبة من الأيبوكسي المدعم بالبوكسايت العراقي. تتغير نسبة البوكسايت في هذه الدراسة بشكل منتظم لتقييم تأثيرها على خواص المواد المركبة. تم تحضير المواد المركبة باستخدام تقنية الصب. أظهرت نتائج اختبار الحني أن معامل المرونة تزداد بأزياد النسبة الوزنية للبوكسايت من 1.25% الى 40% حيث سجلت أعلى قيمة لها عند نسبة 40% بوكسايت بقيمة مقدارها 4.93 GPa. بينما تقل مقاومة الانحناء للمواد المركبة بازدياد النسبة الوزنية للبوكسايت لغاية 20% وبعد ذلك تزداد بازدياد نسبة البوكسايت بين 20% و 40%. كما ظهر جلياً تأثير اضافة حبيبات البوكسايت على منحنيات الاجهاد-الانفعال للحني. ان انفعال الحني عند الكسر والمتانة تنخفض بأزدياد محتوى البوكسايت في المادة المركبة. هذا النوع من المواد المركبة مناسب جداً في أنظمة التوقف للمركبات للأحمال المعدلة وكذلك تستخدم في أرضيات المخازن الثقيلة.


Article
Analysing Some Mechanical Properties of Cinnamon Powder Reinforced with Polymeric Materials Used in Dental Application

Authors: Ahamed M. AlGhabban --- Reem A. Mohammed --- Jumaah R. Mahmood
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2019 Volume: 37 Issue: 3 Part (A) Engineering Pages: 96-105
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Abstract- In the dentures industry, materials must be chosen to have goodmechanical properties in order to resist the conditions that may occur in themouth. A study was conducted to assess tensile strength, elasticity coefficient,elongation, flexural strength, flexural modulus with impact properties of polymethyl methacrylate resin as matrix strengthened with cinnamon powder andalso analysing these mechanical properties by using (OriginLab) softwareprogram. The samples of Poly Methyl methacrylate bio composites whichcontaining 2%, 4%, 6%, and 8% weight fractions of cinnamon powder and anunfilled as control sample were fabricated using “hand lay up” method. Theresults indicate that the addition of 8% weight fraction cinnamon powder intoPoly Methyl methacrylate resin improved of ultimate tensile strength, moduluselasticity ,flexural strength, flexural modulus (62 MPa, 3.7 GPa, 96 MPa, 6.4GPa) respectively, compared with the values of pure Poly Methyl methacrylate(51 MPa, 1.5 GPa, 78MPa, 2.0 GPa) respectively. Also can be noted that theelongation at break values decreases with an increase in weight fractions offiller, where the sample (Poly Methyl methacrylate +2% cinnamon) has the bestvalue for elongation compared with samples reinforced (4%, 6% and 8% wt).The impact strength results observe the maximum value was present in thesample (Poly Methyl methacrylate+6% cinnamon). From the results,descriptive, One Way ANOVA statistical analysis and means comparison byused (Scheffe test and Tukey test) for all mechanical properties indicated, turnsout if Sig equals 1 shows that the variance in mean is significant at the level of0.05, whereas Sig is 0 designates that the mean variance is not significant at thelevel 0.05.


Article
COMPARATIVE STUDY THE FLEXURAL PROPERTIES AND IMPACT STRENGTH FOR PMMA REINFORCED BY PARTICLES AND FIBERS FOR PROSTHETIC COMPLETE DENTURE BASE
دراسة مقارنة حول خصائص الانحناء ومقاومة الصدمة للبولي مثيل ميثا اكريليت المقوى بالدقائق والألياف لمادة قاعدة طقم أسنان أصطناعي كامل

Loading...
Loading...
Abstract

In the present search, attempts are made to develop the properties of PMMA resin that used for upper and lower prosthesis complete denture, by addition two different types of particles, which included: nano-hydroxyapatite (nHA) particles and micro-zirconia (ZrO2) particles that added with different volume fractions of (1%, 2% and 3%) to poly methyl methacrylate (PMMA) cold cured resin as new fluid resin matrix. Also woven glass fiber kind (E-glass) and woven Kevlar fiber kind (49), it were added with a fixed volume fraction of (5%) to PMMA composites. In this work the composite prosthetic dentures specimens preparation was done by using (Hand Lay-Up) method as six groups which includes: the first group consists of PMMA resin reinforced by nHA particles, the second group consists of PMMA resin reinforced by ZrO2 particles, the third group consists of (PMMA-nHA) and glass fiber layer as laminated composite , the fourth group consists of (PMMA-ZrO2) and glass fiber layer, the fifth group consists of (PMMA-nHA) and Kevlar fiber layer and the sixth group consists of (PMMA-ZrO2) and Kevlar fiber layer.The experimental part of this study included performing many mechanical tests which, includes (Flexural, Maximum Shear Stress and Impact) tests. The result of this study showed the values of most properties increased with increasing of the volume fraction of (nHA and ZrO2) particles in polymer composite materials. While, the impact strength decreased. The ZrO2 particle and woven mat Kevlar fiber had shown greater values for the most composite materials properties for all groups’ specimens except the flexural strain.Also the results showed the maximum values for hybrid laminated composite properties (flexural modulus and impact strength) were obtained in hybrid laminated composite materials for sixth group specimens. While, the maximum value for properties (flexural strength and max shear stress) were obtained in hybrid laminated composite materials for fourth group specimens.

تم في هذا البحث أجراء عدة محاولات لغرض تطوير مواصفات راتنج البولي مثيل ميثا اكريليت المستخدم كطقم أسنان أصطناعي كامل علوي أو سفلي. وقد حضرت هذه المواد المتراكبة من البولي مثيل ميثا اكريليت على شكل راتنج سائل جديد معالج ذاتياً كمادة أساس وقد تم تقويتها بنوعين مختلفين من الدقائق تضمنت دقائق الهيدروكسي اباتايت النانوية ودقائق الزركونيا الميكروية اضيفت بكسور حجمية مختلفة هي (1%, 2% and 3%)، ونوعين مختلفين من الالياف الحصيرية الثنائية الاتجاه هي الياف الزجاج نوع (E-GLASS) والياف الكفلر نوع (49) وقد اضيفت الى المواد المتراكبة بكسر حجمي ثابت هو (%5). في هذا البحث حضرت عينات من أطقام الاسنان الأصطناعية المتراكبة بطريقة (الصب اليدوي) على شكل ستة مجاميع هي: المجموعة الاولى تضم راتنج البولي مثيل ميثا اكريليت ودقائق الهيدروكسي اباتايت النانوية، المجموعة الثانية تضم راتنج البولي مثيل ميثا اكريليت ودقائق الزركونيا، المجموعة الثالثة تضم راتنج البولي مثيل ميثا اكريليت والياف الزجاج مع دقائق الهيدروكسي اباتايت النانوية، المجموعة الرابعة تضم راتنج البولي مثيل ميثا اكريليت والياف الزجاج مع دقائق الزركونيا، المجموعة الخامسة تضم راتنج البولي مثيل ميثا اكريليت والياف الكفلر مع دقائق الهيدروكسي اباتايت النانوية، المجموعة السادسة تضم راتنج البولي مثيل ميثا اكريليت والياف الكفلر مع دقائق الزركونيا.يتضمن الجزء العملي من هذا البحث اجراء العديد من الاختبارات الميكانيكية والتي شملت فحوصات (الانحناء، اجهاد القص الأعظم والصدمة(. وقد بينت النتائج بان قيم اغلب الخواص ازدادت مع زيادة الكسر الحجمي لدقائق الهيدروكسي أباتايت النانوية ودقائق الزركونيا، بينما قلت مقاومة الصدمة. وان دقائق الزركونيا والياف الكفلر الحصيرية تعطي قيم أعلى لاغلب خواص المواد المتراكبة ولكافة مجاميع العينات ماعدا الانفعال الأنحنائي. كذلك أظهرت النتائج بان اعلى قيم لخصائص (معامل الانحناء ومقاومة الصدمة) وجدت في المواد المتراكبة الطبائقية الهجينية لعينات المجموعة السادسة. بينما اعلى قيم لخصائص (مقاومة الانحناء واجهاد القص الأقصى) وجدت في المواد المتراكبة الطبائقية الهجينية لعينات المجموعة الرابعة.

Listing 1 - 4 of 4
Sort by
Narrow your search

Resource type

article (4)