Corrosion Inhibition of Galvanic Couple Copper Alloy/Mild Steel in Cooling Water System

Loading...
Loading...
Abstract

The driving idea for the present work was to combine the effect of polyvinyl alcohol (PVA) as corrosion inhibitor with the distance between the anodic and cathodic elements of the galvanic cell, beside their area ratio, in scope of synergistic suppression of galvanic corrosion on Cu/Fe model couple, using weight loss method. The performance affecting galvanic corrosion process has been tested for three major factors affect the process:1.Four PVA inhibitor concentrations were selected to be (0, 1000, 4000 and 7000 ppm) in simulated cooling water.2.Two cathode: anode area ratios as 1:1 and 2.4:1.3.Two distances apart cathode – anode as 3 and 7 cm. Maximum corrosion inhibition achieved was 86% which indicates that increasing inhibitor concentration leads to decrease dissolution process followed hydrogen evaluation Cu electrode as cathode element in galvanic cell.


Article
Galvanic Corrosion of Copper / Nickel-Chrome Alloy in an Agitated Sulfuric Acid Solution
التاكل الكلفاني لسبیكة النیكل كروم و النحاس في محلول حامض الكبریتیك تحت تاثیر الجریان

Authors: Naseer A. Al-Haboubi نصیرعبود الحبوبي --- Basim O. Hasan باسم عبید حسن --- Samar S. Hussein سمر سعدي حسین
Journal: AL-NAHRAIN JOURNAL FOR ENGINEERING SCIENCES مجلة النهرين للعلوم الهندسية ISSN: 25219154 / eISSN 25219162 Year: 2018 Volume: 21 Issue: 1 Pages: 133-140
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

AbstractGalvanic corrosion of Nickel-Chrome alloy (Ni-Cr alloy) and Copper (Cu) coupled in 5% sulfuric acid solution was investigated. The effects of agitation velocity, temperature, and time on the galvanic corrosion current and the weight loss of both metals in both free corrosion and galvanic corrosion were investigated. The trends of open circuit potential (OCP) of each metal and galvanic potential (Eg) of the couple were also determined. The results showed that Cu was cathodic relative to Ni-Cr alloy in galvanic couple and the corrosion potential of the couple (Ni- Cr alloy /Cu) was between the values of the two single components because the OCP of copper shifted to positive with the increase in velocity. Under stagnant conditions initially the galvanic current was more negative then shifted to the positive with time. The corrosion of Ni-Cr alloy decreased with time because the passivation layer was formed on the surface. Under flow conditions, the galvanic current sharply shifted to the negative direction (increase galvanic current from Ni-Cr alloy (anode) to Cu (cathode) during the first few minutes.


Article
Galvanic Corrosion of Carbon Steel -Stainless Steel Couple in Sulfuric Acid under Flow Conditions
التاكل الكلفاني للحديد الكاربوني والحديد المقاوم للصدأ في حامض الكبريتيك تحت تاثير الجريان

Authors: Samar Saadi Hussien سمر سعدي حسين --- Naseer Abood Al-habubi نصير عبود الحبوبي --- Basim Obed Hasan باسم عبيد حسن
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2016 Volume: 22 Issue: 8 Pages: 158-174
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Galvanic corrosion of stainless steel 316 (SS316) and carbon steel (CS) coupled in 5% wt/v sulfuric acid solution at agitation velocity was investigated. The galvanic behavior of coupled metals was also studies using zero resistance ammeter (ZRA) method. The effects of agitation velocity, temperature, and time on galvanic corrosion current and loss in weight of both metals in both free corrosion and galvanic corrosion were investigated. The trends of open circuit potential (OCP) of each metal and galvanic potential (Eg) of the couple were, also, determined. Results showed that SS316 was cathodic relative to CS in galvanic couple and its OCP was much more positive than that of CS for all investigated ranges of operating conditions. A sharp increase in galvanic current from CS to SS316 in the first 20 min and then decrease with time. Increasing the agitation velocity led to increase in galvanic corrosion rate. The decrease in galvanic current is attributed to metal passivation due to the formation of a protective film which grows with time. The minus sign in galvanic current means that the current is flow from CS (anode) to SS316 (Cathode). The galvanic current of CS-SS316 couple shifts to the negative direction with increase agitation velocity.

تم دراسة التاكل الكلفاني للحديد الكاربوني والحديد المقاوم للصدأ بوجود سرع في5% wt/v) ) حامض الكبريتيك. السلوك الكلفاني للمعدنين ايضا درس باستعمال مقياس التيار الكهربائي ذو المقاومة صفر (ZRA) . تاثير السرعة ودرجة الحرارة والزمن على تيارات التاكل الكلفاني والوزن المفقود للمعدنين في حالة التاكل الحر والتاكل الكلفاني. حساب جهود المعادن في الحالة الحرة والربط الكلفاني. من النتائج نلاحظ انه الحديد المقاوم للصدأ هو كاثود الحديد الكاربوني هو انود في حالة الربط الكلفاني .الجهد الحر للحديد المقاوم للصدأ في جميع الظروف المدروسة كان اكثر خمولا من الحديد الكاربوني. زيادة حادة في التيار الكلفاني من الحديد الكاربوني الى الحديد المقاوم للصدأ في اول عشرين دقيقة ثم يقل مع الزمن وهذا يزداد مع زيادة السرعة .نقصان معدل التاكل الكلفاني وكذلك معدل التاكل الحر للحديد المقاوم وذلك بسبب تاثير طبقة الحماية على سطح المعدن التي تنمو مع الزمن. الاشارة السالبة في التيارالكلفاني تعني اتجاه التيار من الحديد الكاربوني الى الحديد المقاوم.تزداد قيمة التيار الكلفاني للمعدنين معا باتجاه السالب (وذلك يعني الحديد الكاربوني انود والحديد المقاوم للصدأ هو كاثود) مع زيادة السرعه.


Article
Corrosion of Carbon Steel in Oxygen and NaCl Concentration Cells: the Influence of Solution Temperature and Aeration
تاكل الفولاذ الكاربوني في خلايا تركيز الاوكسجين وكلوريد الصوديوم :تاثير درجة حرارة المحلول والتهوية

Loading...
Loading...
Abstract

Corrosion rate tests were carried out on carbon steel under concentration cells conditions of oxygen and sodium chloride. The effect of aeration in one compartment on the corrosion rate of both coupled metals was determined. In addition, the effects of time and temperatures on the corrosion rate of both coupled metals and galvanic currents between them were investigated. Corrosion potentials for the whole range of operating conditions under concentration cell conditions were also studied. The results showed that under aeration condition, the formation of concentration cell caused a considerable corrosion rate of the Carbon steel specimens coupled in different concentrations of O2 and NaCl due to the galvanic effect. Aerating one compartment caused a noticeable increase in the corrosion rate of the coupled specimen in the other compartment due to the galvanic effect. Increasing temperature caused unstable trends in the free and galvanic corrosion potentials. Increasing the temperature led to an increase in the corrosion rate for both metals.

اجريت عملية قياس معدل التاكل للحديد الفولاذي تحت ظروف خلايا التركيز للاوكسجين وملح كلوريد الصوديوم. وتم دراسة تاثير عامل التهوية لاحد اجزاء الخلية على معدل التاكل لكلا المعدنين المربوطين بالاضافة الى ذلك تم دراسة تاثير الوقت ودرجات الحرارة على معدل التاكل لكلا المعدنين المربوطين وايضا تم قياس التيارات الكلفانية بينهما .تم قياس ودراسة جهود التاكل للمدى الكلي للظروف التشغيلية لظروف خلية التركيز.اظهرت النتائج انه في حالة استخدام التهوية فان تَكُون خلية التركيز يسبب زيادة معدل التاكل للعينات المربوطة وفي تراكيز مختلفة للاوكسجين وملح كلوريد الصوديوم بسبب التاثير الكلفاني. استخدام التهوية لاحد اجزاء الخلية يسبب زيادة ملحوظة في معدل التاكل للعينة المربوطة في الطرف الاخر من الخلية نتيجة التاثير الكلفاني. زيادة درجة الحرارة يؤدي الى اتجاه غير مستقر في جهود التاكل الكلفانية والحرة وان زيادة درجة الحرارة يؤدي الى زيادة معدل التاكل الكلي للمعدنين .