EFFECT OF FIBER ORIENTATION ANGLES ON MECHANICAL BEHAVIOR OF CAR BUMPER COMPOSITE
تأثير زوايا توجيه الألياف على السلوك الميكانيكي لدعامة سيارة من المواد المتراكبة

Authors: Nabel Kadum Abd-Ali نبيل كاظم عبد علي --- Ahmed Raee Madeh احمد راعي مديح
Journal: KUFA JOURNAL OF ENGINEERING مجلة الكوفة الهندسية ISSN: 25230018 Year: 2016 Volume: 7 Issue: 3 Pages: 27-37
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

The present work focused on the effect of glass fiber orientation that reinforced polymeric matrix in car bumper composite to understand the mechanical behavior of these materials during work conditions. Tensile test and bending test were performed and discussed for (0o, 30 o, 45 o, 60 o, and 90 o) angles of fibers orientation. The finite element method by program (ANSYS V.13 software) was used to study the behavior of these compounds. The results showed that the extension and deflection values were higher at (0o) and decreased with increasing fiber angle orientation until reached to a lower value at perpendicular state between fibers and applied loads. The study used to improve the mechanical properties of the composite materials depending on the fiber orientation angle.

ركزت الدراسة الحالية على تأثير زاوية توجيه الألياف الزجاجية التي تعزز ارضية البوليمر في دعامة السيارة والمصنعة من مواد متراكبة لفهم السلوك الميكانيكي لهذه المواد خلال ظروف العمل. أجري خلال الدراسة اختبار الشد واختبار الانحناء ومناقشة تاثير زاوية انتظام الياف التسليح للزوايا (0، 30، 45، 60 و 90) . تم الاستعانة بطريقة العناصر المحددة و برنامج ANSYS V.13 لدراسة سلوك هذه المركبات. أظهرت النتائج أن قيم التشوه والانحراف كانت أعلى عند الزاوية (0) وتتناقص وصولا إلى أقل قيمة في حالة التعامد بين الألياف والأحمال المطبقة. استخدمت الدراسة لتحسين الخواص الميكانيكية للمواد المتراكبة اعتمادا على زاوية اتجاه الألياف.


Article
Study of Compression Behaviour of a Cu-13Al-4Ni-xCr Shape Memory Alloys Prepared by powder metallurgy process

Authors: Abdul Raheem K. Abid Ali --- Aseel Safee hamza
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2017 Volume: 25 Issue: 1 Pages: 145-156
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

In this study (Cu-13Al-4Ni-xCr) shape memory alloys have been prepared by using Powder metallurgy technique with added Cr element (x=0.3,0.6,0.9) . After compacted , sintering process has been done in vacuum pressure (10-4torr) at ( 550oC for 120 minute) and ( 900oC for 60 minute) then cooling inside furnace.Quenching heat treatment carry out at (850oC for 60 minute) then cooling in cold water to (3-4oC) . The microstructure has been studied by optical microscope and scanning electron microscope (SEM) , porosity , compression behavior(stress-strain) for quenched specimens also have been studied .The results have been approached that the hardness increases with percent chrome while the porosity decreases . The compression stresses to fracture , have been increased with respect to (0.3%C) had porosity (27%) and decreased for (0.9%) has porosity (22%) . from the previous results , quenched alloy (Cu-13%Al-4%Ni-0.3%Cr) is the more compression strength

في هذه الدراسة تم تحضير سبيكة (نحاس- 13%ألمنيوم-4%نيكل) باستخدام تقنية ميثالورجيا المساحيق مع اضافة عنصر الكروم بنسب محددة (%0.3، 0.6%، 0.9% ) فبعد عملية الكبس أجريت عملية التلبيد في جو مفرغ من الهواء بضغط (10-4 توور )عند درجة حرارة (0500م) لفترة (120 دقيقة) وعند (900 0م ) لمدة (60 دقيقة) ثم التبريد داخل الفرن , بعد ذلك اجريت المعاملة الحرارية (الاخماد) عند درجة حرارة (0850م) لمدة(60 دقيقة) ثم الاخماد بماء بارد بدرجة حرارة (3-04م).تم دراسة البنية المجهرية بالمجهر الضوئي والمجهر الالكتروني الماسح(SEM) وكذلك تم دراسة المسامية والسلوك ألانضغاطي (الجهد-انفعال) للسبائك المخمدة و من خلال النتائج التي تم التوصل اليها وجد أن الصلادة تزداد مع زيادة نسبة الكروم بينما المسامية انخفضت اما بالنسبة لجهود الانضغاط حتى نقطة الكسر فأنها ازدادت بالنسبة لنسبة الكروم(%0.3) البالغة مساميتها (27%) وانخفضت بالنسبة لنسبة الكروم(%0.9) مساميتها (22%) واظهرت السبيكة (نحاس – 13%ألمنيوم-4%نيكل-0.3%كروم) المخمدة أكثر مقاومة للانضغاط.