Study the Partial Subistituation and Annealing on Electrical Properties of Compound Tl2-xAg2-ySryBayCa2Cu3O10+& Superconductor Fabricated by Nano Technique
دراسة تاثير التعويض الجزئي والتلدين المتكرر في الخصائص الكهربائية للمـــــركب Tl2-xAgxSr2-yBayCa2Cu3O10+δ الفائق التوصيل الكهربائي المحضر بتقنية النانو

Loading...
Loading...
Abstract

The crystal compounds Tl2-xAg2-ySryBayCa2Cu3O10+& are successfully prepared in different concentrations (x, y=0.1, 0.2, 0.3, 0.4, 0.5) by solid state reaction process. The samples were then subjected to Nano technique under hydrolic pressure 8 ton/cm2. samples have been annealed in (850 C0) for 72 hours. The results show a best value at x, y=0.3 ratio of Ag, Ba. Electrical resistivity at x, y= 0.3 of Ag, Ba are obtained when the best value of Tc= 141 K. Samples morphology were also observed by AFM (in three dimensions), the best value of Nano is 91.74 nm at x, y= 0.3. Morphological structures of the surface were also observed by (SEM) and (EDX) show that there are dark regions and light which indicate the presence of heavy elements and light elements on the installation.

تم تحضير العينات المركب Tl2-xAgxSr2-yBayCa2Cu3O10+δ بطريقة تفاعل الحالة الصلبة ومن ثم تم تحويل عناصرها الى حجم النانوي بوساطة طاحونة نانوية وبتراكيز مختلفة لـx,y اذا (x,y=0.1,0.2,0.3,0.4,0.5) وتم كبس العينات باستعمال مكبس هيدروليكي 2 8 ton/cmومن ثم تم تلدين النماذج بدرجة حرارة 850 0C لمدة (72) ساعة. لوحظ من خلالها ان افضل نسبة تعويض لـ x,y هي 0.3 اذ ان افضل درجة حرارة تحول هي Tc=(141) Kعند x,y=0.3 ,واظهرت دراسة وفحص النماذج بوساطة مجهر القوة الذرية AFM بان افضل معدل البعد النانوي هي 91.75 nm عند نسبة التعويض 0.3 . ومن ثم تم فحص النماذج بوساطة المجهر الالكتروني الماسح و(EDX) لمعرفة نسبة العناصر وتبين من خلال تصوير العينات هنالك مناطق داكنة ومناطق فاتحة يدل على وجود عناصر ثقيلة وعناصر خفيفة على التركيب.


Article
Degradation of Organic Dyes using Photo-Catalytic Technique
تكسر الاصباغ العضويه بتقنية المحفز بالضوء

Author: Ayad Dari Jaafar اياد داري جعفر
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2015 Volume: 8 Issue: 2 Pages: 128-136
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

The present investigation is concerned to study the prepared of nano composite catalyst of titanium dioxide and carbon nanotube (TiO2/CNT) based on photo-catalysts process. The synthesized composite catalyst was characterized by Brunauer, Emmett and Teller (BET), Scanning Electron Microscopy (SEM), X-ray diffraction (XRD), XRF and Raman Spectroscopy. Moreover, the nano composite catalyst was used as a dye to degradation of contaminated water that containing organic pollutants. The photo-catalytic degradation process was carried out at different operational parameters, (Initial concentration of hydrogen peroxide H2O2 of the medium, mixing speed, and flow rate for methylene blue (MB, C16H18N3SCl.3H2O) dye). The nano titanium dioxide / carbon nanotubes (TiO2/CNT) composite showed greater photo-degradation activity under solar and ultraviolet (UV) lamp.

يتناول البحث دراسة تحضير العامل المساعد النانوي المركب من اوكسيد التتانيوم وانابيب الكاربون (TiO2/CNT) لعملية التحفيزبالضوء, حيث تم دراسة خصائص العامل المساعد بقياس المساحة السطحية للمركب المحضر باستخدام طريقة ) BET (, و تقنياتالمجهر الالكتروني الماسح) SEM , ) XRD , XRF ومقياس رامان. علاوة على ذلك استخدم العامل المساعد النانوي المركبلتكسير ملوثات المياه العضويه مثل الاصباغ . بعد ذلك تمت دراسة عدة عوامل مؤثرة على عملية التكسر في عملية المحفزللضوء ) التركيز الابتدائي لبروكسيد الهيدروجين H2O2 ( mg/L (, وسرعة الخلط ) rpm (, والجريان الحجمي للصبغة والعاملالمساعد ) L/min ( (. اظهر العامل المساعد النانوي كفاءة عالية تحت تاثير اشعة الشمس والاشعة الفوق البنفسجية.