Effect pH on Structural and Optical Properties of Nanostructure CdS Films Prepared by Chemical Bath Deposition Technique
تأثير الدالة الحامضية (pH) على الخصائص التركيبية البصرية لأغشيه CdS نانويه التركيب المحضرة بتقنية ترسيب بالحمام الكيميائي

Loading...
Loading...
Abstract

Nanostructures CdS films were prepared by chemical bath deposition technique on glass substrates, where the cadmium nitrate salt was used as a source of cadmium ions and thiourea (SC(NH2)2) as a source of sulphide ions(S-2). The deposition were carried out at different pH values. Structure of these films was characterized by X-ray diffraction and atomic force microscope (AFM). CdS films deposited have cubic(zinc blende) structure and the grain size of nanoclusters decreases with increasing pH value in solution. The optical properties study by transmission spectra and the films have highly transmittance in visible region of spectrum and reach to more than 86%. The CdS films have band gap increase from 2.42 to 2.58 eV with increasing pH value in solution .

تم ترسيب تراكيب نانوية (Nanostructure) من أغشية CdS على أرضيات زجاجية بتقنية ترسيب بالحمام الكيميائي، حيث استخدام ملح نترات الكادميوم كمصدر لايونات الكادميوم الموجبة والثيوريا كمصدر الايونات الكبريت.وأجريت عملية الترسيب عند قيم مختلفة للدالة الحامضية(pH).الخصائص التركيبية لهذه الأغشية شخصت بواسطة حيود الأشعة السينية(XRD) ومجهر القوة الذري(AFM)، حيث بينت إن أغشية CdS المرسبة تمتلك تركيب مكعب(مشبك الخارصين) ومعدل الحجم الحبيبي للعناقيد النانوية يقل مع زيادة قيمة الدالة الحامضية (pH) في المحلول. الخصائص البصرية درست باستخدام أطياف النفاذيه ، حيث بينت إن أغشية CdS لها نفاذيه عالية في المدى المرئي من الطيف وتصل إلى أكثر من 86 %. أغشية CdS تمتلك فجوة طاقة تزداد من 2.42 eVإلى2.58 eV مع زيادة قيمة الدالة الحامضية (pH) في المحلول.


Article
Deposited Nanostructure Cds Thin Film by Using Pulse Laser Deposition Technique for Fabrication of Heterojunction Solar Cell
ترسيب اغشية كادميوم سلفايد الرقيقة النانوية باستخدام تقنية الليزر النبضي لتصنيع خلية شمسية هجينة

Author: Heba Salam Tareq
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 2 Part (B) Scientific Pages: 313-320
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In the present study, nanostructure Cadmium sulfide (CdS) thin films on Si P-type substrates heterojunction solar cell has been made by using a pulsed 532 nm Nd:YAG laser. Deposition of films is achieved at 200 °C substrate temperatures and oxygen pressure 10-1 Torr. X-ray diffraction (XRD), Scanning electron microscopy (SEM), atomic force microscope (AFM) and UV-VIS transmittance analyses were employed to characterize thin films. XRD measurements approved that CdS film is a hexagonal Wurtzite structure. The morphology of deposited films were characterized by scanning electron microscope (SEM) and atomic force microscope (AFM), the grain size value (18) nm and rms roughness values are (12.6 nm) for thin films deposited at 200ºC. UV-VIS transmittance measurements have shown that our films are highly transparent in the visible wavelength region, with an average transmittance of ~90% . The direct optical band gap of the film has been found to be 2.2 eV.The photovoltaic characteristics included short circuit current (Jsc), open circuit voltage (Voc), where the maximum (Jsc) and (Voc)obtained at AM1 were 29.3 (mA cm-2) and 635(mV), respectively. The fill factor (FF) was (0.44). The fabricated cell exhibits good performance with 7.8 % conversion efficiency.

في هذا البحث , تم ترسيب اغشية رقيقة نانوية من الكادميوم سلفايد على قواعد من السليكون الاحادي البلورة من النوع القابل لتصنيع خلايا شمسية هجينة باستخدام ليزر النيودميوم-ياك النبضي ذو الطول الموجي 532 نانو متر.تم ترسيب الاغشية عند درجة حرارة قاعدة 200 درجة مئوي. اظهرت قياسات الاشعة السينية ان الاغشية المحضرة ذات طور الفرتزايت السداسي .حددت خصائص طبوغرافية السطح من خلال قياس المجهر الالكتروني الماسح و مجهر القوى الذرية , حيث بلغت قيمة الحجم الحبيبي18) ) نانو متر وقيمة خشونة السطح (12.6) نانومتر للأغشية المحضرة بدرجة حرارة قاعدة( 200) مئوي.اوضحت نتائج مطياف الاشعة المرئية والفوق البنفسجية امتلاك غشاء الكادميوم سلفايد نفاذية بلغت بحدود 90% و بلغت قيمة فجوة الطاقة المياشرة (2.2 الكترون.فولط) درست الخواص الفولطائية المتمثلة بتيار الدائرة القصيرة (Jsc) وفولتية الدائرة المفتوحة (Voc) بالاضافة لعامل الملئ (FF) ووجد ان اعظم قيمة لكل من (Jsc) و (Voc) لحالة AM1 هي 29.3 (mA cm-2) و 635(mV), على التوالي وان قيمة عامل الملئ هي (0.44) .الخلية المصنعة اظهرت قيمة كفاءة جيدة بلغت 7.8%.