Article
Laser Treatment of Plasma Spraying Alloyed Coatings
المعاملة الحراریة باللیزر لطبقات الرش بالبلازما السبائكیة

Authors: Mohammed Jasim Kadhim محمد جاسم كاظم --- Sami Ibrahim Jaffar سلمى ابراهيم جعفر --- Eman Adnan Anon ايمان عدنان عنوان
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2012 Volume: 30 Issue: 16 Pages: 343-354
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Ni23Cr6Al0.4Y plasma sprayed coating on nimonic75 substrate was remelted using a 1kW continues CO2 laser. The topography, microstructure, phases and chemical analysisof plasma sprayed and laser melted regions were examined using various techniquesincluding scanning electron microscope (SEM), electron probe microanalysis (EPMA),energy dispersive X-ray spectroscopy (EDS) and X-ray diffraction (XRD). The plasmasprayed coatings consisted heterogeneous microstructure of lamella with unmeltedparticles, voids, porosity and cracks. It was found that the depth of melting increasedwith increasing the specific energy. Homogenous and shiny melted regions wereachieved without voids, porosity and cracks after laser melting. Thin upper surfacelayers with shallow cracks were observed due to the rich layer of α-Al2O3 and YAlO3.No phases changed were found before and after laser melting of plasma sprayed layers.The phases formed are mixtures of γ’, β, YAlO3 in the matrix γ. The microstructureformed after laser melting is fine cells.Keywords: Plasma sprayed coating; Laser melting, Ni solid solution; YAlO3; α-Al2O3

المطلی ة عل ى س طح النایمون ك 75 باس تخدام Ni23Cr6Al0.4Y ت م ص ھر طبق ة ال رش بالبلازم ا ن وعاللی زر المس تمر ن وع ث انى اوكس ید الكرب ون وعن د ق درة 1 كیل و واط. الطوبوغرافی ة والبنی ة المجھری ة والاطوار و التحلیل الكیمیاوى لمناطق الرش بالبلازما ومناطق الانصھارباللیزر تم فحصھا باس تخدام تقنی اتوالمج س الالكترون ى للتحلی ل ال دقیق (SEM) مختلف ة تض منت المجھ ر الالكترون ى الماس حلق د وج د ب ان .(XRD) وحی ود الاش عة الس ینیة (EDS) ومطی اف مف رق الاش عة الس ینیة (EPMA)طبقات الرش بالبلازما تتكون من بنیة مجھریة غیر متجانسة من طبقات تحتوى على دقائق غی ر منص ھرةو فج وات و مس امیة وش قوق. ی زداد عم ق طبق ة الانص ھار م ع زی اة الطاق ة النوعی ة للی زر. ت م الحص ولعلى مناطق منصھرة براقة بدون فجوات ومسامیة و شقوق بعد الانصھار ب اللیزر. ت م تك وین طبق ة رقیق ةوذات ش قوق ناعم ة بع د المعامل ة ب اللیزر وب الاخص عن د الطاق ة النوعی ة YAlO غنی ة بالالومین ا والعالی ة. ل م ی تم ملاحظ ة اى تغی ر ب الاطوار الناتج ة قب ل وبع د الانص ھار ب اللیزر لطبق ات ال رش بالبلازم ا.و (γ’) Ni3Al كارض یة م ع الاط وار الوس طیة (γ) تتكون الاطوار م ن م زیج م ن المحل ول الجام د للنیك لالبنیة المجھریة الناتجة بعد المعاملة باللیزر تتكون من حبیبات ناعمة. .(β) NiAl


Article
HOT CORROSION OF CERIA-YTTRIA STABILIZED ZIRCONIA PLASMA SPRAYED THERMAL BARRIER COATING BY EUTECTIC VANDIUMPENTAOXIDE-SODIUM SULFATE
التاكل الساخن لطبقات الرش بالبلازما للحواجز الحرارية للسيريا-ياتريا المثبتة للزركونيا بالاويتكتيك لخماسي اوكسيد-الفناديوم- كبريتات الصوديوم

Loading...
Loading...
Abstract

The high temperature corrosion behavior of thermal barrier coating (TBC) system consisting of IN-738 LC superalloy substrate, air plasma sprayed Ni24.5Cr6Al0.4Y (wt%) bond coat and air plasma sprayed ZrO2-20 wt% ceria-3.6 wt% yttria (CYSZ) ceramic coat were characterized. The upper surfaces of CYSZ covered with 30 mg/cm2 , mixed 45 wt% Na2SO4-55 wt% V2O5 salt were exposed at different temperatures from 800 to 1000 oC and interaction times from 1 up to 8 h. The upper surface plan view of the coatings were identified for topography, roughness, chemical composition, phases and reaction products using scanning electron microscopy, energy dispersive spectroscopy, talysurf, and X-ray diffraction. XRD analyses of the plasma sprayed coatings after hot corrosion confirmed the phase transformation of nontransformable tetragonal (t') into monoclinic phase, presence of YVO4 and CeVO4 products. Analysis of the hot corrosion CYSZ coating confirmed the formation of high volume fraction of YVO4, with low volume fractions of CeOV4 and CeO2. The formation of these compounds were combined with formation of monoclinic phase (m) from transformation of nontransformable tetragonal phase (t').

تم تقييم التاكل الكيميائي بدرجة الحرارة العالية لطلاءات الحواجز الحراية المنتجة بالرش بالبلازما للزركونيا الحاوية على 20 wt% سيريا و 3.6 wt% ياتريا والمطلية على طبقة طلاء وسطية من Ni24.5Cr6Al0.4Y (wt%). ان طبقات الطلاء السيراميكية والوسطية المنتجة بالرش بالبلازما تم طلائها على سبيكة فائقة من .IN-738 LC طبقات الرش بالبلاما السيراميكية التي تم تغطيتها بمزيج ملحي من 45 wt% Na2SO4-55 wt% V2O5 وبمعدل تغطية 30 mg/cm2 تم اختبارها بدرجة حرارة من 800 الى oC 1000 ولفترات زمنية 1 و 8 ساعات. طوبوغرافية الاسطح والخشونة والتركيب الكيمائي والاطوار ونواتج التاكل للاسطح العلوية لطبقات الرش تم تحديدها باستخدام المجهر الالكتروني الماسح ومطياف مفرق الطاقة و جهاز قياس الخشونة وحيود الاشعة السينية. اثبتت نتائج حيود الاشعة السينية لطبقات الرش بعد التاكل الكيميائي تحول الطور السداسي الغير متحول t') ) الى الطور احادي الميل m)) و الاطوار YVO4 و CeVO4. اوضح تحليل طبقات الرش بالبلازما بعد التاكل بان الطور السائد بكسر حجمي كبير هو YVO4 وكمية قليلة من الاطوار CeOV4 و .CeO2 أن تكزن هذه الاطوارمصاحب لتكوين الطور الاحادي الميل m)) الناتج من تحول الطور السداسي الغير متحول (t') .


Article
HARDNESS AND FRATURE TOUGHNE OF PLASMA SPRAYED ZIRCONIA-CERIA-YTTRIA THERMAL BARRIER COATINGS
الصلادة وعساوة الكسر لطبقات الرش بالبلازما للحواجز الحرارية للزركونيا-سيريا-ياتريا

Loading...
Loading...
Abstract

Several studies have been made during the recent years to evaluate the plasma sprayed yttria partially stabilized zirconia thermal barrier coatings but less attention were undertaken on ceria-yttria stabilized zirconia. In this study, zirconia- 20 wt% ceria-3.6 wt% yttria thermal barrier coatings were produced by air plasma spraying deposited on IN 738 LC superalloy substrate. The objective of this study is to analysis the distribution of porosity, hardness and fracture toughness on the deposited coatings. Under optimum plasma spraying conditions, it is dangerous to consider the mean values of hardness and fracture toughness. The distributions of hardness and fracture toughness are highly scattered. The Weibull distribution is the main parameter to describe the plasma sprayed coatings hardness and fracture toughness.

اجريت خلال السنوات الاخيرة العديد الدراسات لتقييم طبقات الرش بالبلازما للحواجز الحرارية للياتريا المثبتة جزئيا للزركونيا لكن اهتمام اقل تم ايلائه للسيريا المثبتة للزركونيا. في هذه الدراسة تم انتاج طلاءات من الحواجز الحرارية للزركونيا- wt% 20 سيريا- wt% 3.6 ياتريا على ارضية من السبيكة الفائقة نوع IN 738 LC. ان الهدف لهذه الدراسة هو تحليل توزيع المسامية والصلادة وعساوة الكسر في الطلاءات الناتجة. تحت ظروف الطلاء المثلى فانه من الخطورة اعتماد القيم الوسطى للصلادة وعساوة الكسر. ان قيم الصلادة وعساوة الكسر تتستت بصورة كبيرة. ان توزيع ويبل هو المعامل الاساسي لوصف صلادة وعساوة الكسر لطبقات الرش بالبلازما .