Article
Evaluation of the effect of addition of polyester fiber on some mechanical properties of heat cure acrylic resin

Authors: Thikra M. Hachim ذكرى هاشم --- Zainab S. Abullah زينب عبد الله --- Yasamin T. Alausi ياسمين الالوسي
Journal: Journal of baghdad college of dentistry مجلة كلية طب الاسنان بغداد ISSN: 16800087 Year: 2013 Volume: 25 Issue: special issue 1 Pages: 23-29
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Background: This study aimed to evaluate the effect addition of polyester fibers on the some mechanical propertiesof heat cured acrylic resin (implant strength, flexural strength and hardness)Materials and methods: Ninety specimens were used in the study. Thirty specimens were used for impact strengthmeasurements (80mm X 10mm X 4mm) length, width and thickness respectively. The specimens divided into threetest groups (n=10), first group formed from heat cure acrylic resin without fiber reinforcement. Second group wasformed from heat cure acrylic resin was reinforced with 2 mm length polyester fiber and third group was formed fromheat cure acrylic resin reinforced with 4mm length polyester fiber, impact strength measured by impact testingdevice. 30 specimens with (65 mm X 10mm 2.5mm) length, width and thickness respectively were used in 3 groups(n=10) flexural strength test. The flexural strength was measured by using flexural testing device. 30 specimens with(65mm X 10m X 2.5mm) length width and thickness respectively were used for hardness test. The specimens weredivided into 3 group (n=10) as in impact strength and flexural strength.Hardness measured by using (shore D hardness tester TH210).Results: revealed statistically significant increase on impact strength especially on 4mm length when compared tocontrol group. Significant decreases in flexural strength of PMMP. When compared to control group with 4mm lengthfiber reinforcement. Non significant decrease when compared control group with 2mm length fiber reinforcedPMMA. Significant decrease in hardness of PMMA resin after reinforcement with 2mm, 4mm lengths polyester fibers.Conclusions: Strengthening with the polyester fiber decreased the flexural strength and hardness of the resin, butincreased impact strength. Thus when high impact acrylic resins are needed, fiber reinforced resins may be thematerial of choice

الھدف من ھذا البحث لتقییم تاثیر اضافة الیاف البولیستر للاكریلك الحراري على بعض الخواص المیكانیكیة للاكریلك الحراري (مقاومة الصدمة ,قوة الطي,صلادة السطح).استخدم في البحث 90 نموذج وقد قسمت الى 30 نموذج لكل خاصیة , 30 نموذج لقیاس قوة الصدمة بقیاسات ( 80 ملم* 10 ملم* 4ملم) الطول , العرض,السمك بالتتالي النماذج قسمتالى ثلاثة مجموعات (العدد= 10 ) للاختبار المجموعة الاولى شكلت من الاكریلك الحراري بدون اضافة الالیاف ,المجموعة الثانیة شكلت باضافة الالیاف بطول 2ملم,المجموعة الثالثةشكلت باضافة الالیاف بطول 4ملم. مقاومة الصدمة قیست بواسطة جھاز قیاس الصدمة .30 نموذج استخدمت لقیاس قوة الطي بقیاسات ( 65 ملم* 10 ملم* 2,5 ملم)الطول ,العرض,السمك بالتتالي ,قسمت الى ثلاثة مجامیع( العدد= 10 ) لكل مجموعة وتم قیاس قوة الطي بجھازقیاس قوة الطي. 30 نموذج استخدمت لقیاس صلادة السطح بنفس القیاسات المستخدمة لقیاس قوة الطي .عكست النتائج زیادة ملحوظة في مقاومة الصدمة وخاصة بعد اضافة الالیف بطول 4 ملم ونقصان ملحوظ في قوة الطي بعد اضافة الالیف بطول 4ملم مع نقصان غیر ملحوظ بعداضافة الالیاف بطول ال 2ملم. نقصان غیر ملحوظ لكلا الطولین على صلادة السطح. ھذه الدراسة استنتجت ان اضافة الیاف البولستر تقلل من قوة الطي والصلادة ولكن تزید من مقاومةالصدمة ولذلك عندما نرید ان نستخدم الاكریلك الحراري ذو المقاومة العالیة للصدمة نستخدم الاكریلك الحراري المدعم بالیاف البولیستر


Article
Reinforcement of Asphalt Concrete by Polyester Fibers to Improve Flexural Bending Fatigue Resistance
تعزيز الخرسانة الأسفلتية بالياف البوليستير لتحسين مقاومة الكلل لانحناء الثني

Authors: Mohammed Qadir Ismael محمد قادر اسماعيل --- Hiba M. Al-Taher هبة مالك الطاهر
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2015 Volume: 21 Issue: 1 Pages: 115-130
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Reinforcing asphalt concrete with polyester fibers considered as an active remedy to alleviate the harmful impact of fatigue deterioration. This study covers the investigation of utilizing two shapes of fibers size, 6.35 mm by 3.00 mm and 12.70 mm by 3.00 mm with mutual concentrations equal to 0.25 %, 0.50 % and 0.75 % by weight of mixture. Composition of asphalt mixture consists of different optimum (40-50) asphalt cement content, 12.50 mm nominal aggregate maximum size with limestone dust as a filler. Following the traditional asphalt cement and aggregate tests, three essential test were carried out on mixtures, namely: Marshall test (105 cylindrical specimens), indirect tensile strength test (21 cylindrical specimens) and flexural bending test (21 beam specimens). The results revealed that, more asphalt content needed as the fibers length and concentration increased. The fatigue life estimation depending on cyclic load to failure in the beam test support the idea that polyester fibers really improve the resistance of fatigue cracking since the repetitions to failure increased by 9.40 % for the 0.50 % of 12.70 mm fibers length. Both of Marshall stability and indirect tensile strength suffer from slight reduction in their values, whereas, the 0.75 % of 12.70 mm fibers length caused lowering in Marshall stability and indirect tensile strength by 11.70 % and 6.00 % respectively.

اعتبر تعزيز الخرسانة الاسفلتية بالياف البوليستير كعلاج فعال للتقليل من الاثر الضار لتدهور الكلل. يغطي هذا البحث التحقيق من استخدام شكلين من احجام الالياف, 6.35 مم *3.00 مم و 12.70مم*3.00مم وبنسب مشتركة تساوي 0.25%,0.50% و0.75% من وزن الخلطة.مكونات الخلطة الاسفلتية تتالف من محتوى امثل متعدد من السمنت الاسفلتي 40-50, 12.5مم من المقاس الاسمي الاقصى للركام مع غبار حجر الكلس كمادة مالئة. تبع اجراء الفحوص التقليدية للسمنت الاسفلتي والركام اجراء ثلاث فحوص رئيسة للخلطات واسمائها: فحص مارشال(105 عينة اسطوانية),فحص قوة الشد غير المباشر(21 عينة اسطوانية) وفحص انحناء الثني(21 عينة عتبة).اظهرت النتائج الحاجة الى المزيد من محتوى الاسفلت كلما زاد تركيز وطول الالياف. تقدير عمر الكلل اعتمادا على التحميل الدوري الى الفشل في فحص العتبة ساند فكرة ان الياف البوليستير فعلا تحسن مقاومة تشقق الكلل حيث ان التكررات للفشل زادت ب 9.40% ل 0.50% من الالياف بطول 12.70مم.كلا من ثبوتية مارشال وقوة الشد غير المباشر عانت من نقصان قليل لقيمهما, حيث, 0.75% من الالياف بطول 12.70مم سبب تخفيض لثبوتية مارشال و قوة الشد غير المباشر ب 11.70% و6.00% بالتعاقب.


Article
The Effect of Incorporation of Two Different Fibers on Some Mechanical Properties of Heat Cure Acrylic Resin Dr. Abdalbasit A Fatihallah BDS, MSc, PhD

Loading...
Loading...
Abstract

To evaluate the effect of addition of different fibers on some mechanicalproperties of heat cured acrylic resin (flexural strength, impact strength and hardness).210 specimens were used in the study.70 specimens were used for flexuralstrength with measurements (65mm*10mm*2.5mm) length, width and thicknessrespectively. The specimens were divided into seven test groups (n=10). The firstgroup is the Control one and it was without fiber reinforcement, second groupreinforced with 2mm polyester fibers, third group reinforced with 4mm polyesterfibers, fourth group reinforced with 2mm Polypropylene fibers, fifth group reinforcedwith 4mm Polypropylene fibers, sixth group reinforced with 2mm of both fibers(polyester and Polypropylene), and seventh group reinforced with 4mm of both fibers(polyester and Polypropylene). 70 specimens were used for impact strength in sevengroup (n=10) with measurements (80mm*10mm*4mm) length, width and thicknessrespectively. 70 specimens were used for hardness test in seven groups (n=10) withmeasurements (65mm*10mm*2.5mm) length, width and thickness respectively.The Results Show that there are highly significant differences between all groupsexcept for a significant differences between control and combination 2 mm fiberlength (mean differences=33.45). For the hardness test the comparisons show thatthere is no significant differences between groups except for a significant differencesbetween control and combination of both fibers with 2mm length (mean differences=-1.34). For impact strength; there are highly significant differences between all groupsexcept for a significant differences between Polyester fiber of 2mm length andcombination of the two fiber of 2 mm length (mean differences=-3.1).In conclusion, the addition of different fibers (polyester and Polypropylene) toacrylic resin gives it more resistance to break and more resistance to bend.

Listing 1 - 3 of 3
Sort by
Narrow your search

Resource type

article (3)


Language

English (3)


Year
From To Submit

2015 (1)

2014 (1)

2013 (1)