Article
Some Properties of Concrete Contains Waste Concrete as Fine Aggregate
بعض خواص الخرسانة المحتوية على مخلفات خرسانية كركام ناعم

Author: Jawad Talib Abodi جواد طالب عبودي
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2014 Volume: 18 Issue: 6 Pages: 88-103
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

In this research, experimental investigations have been carried out to assess the effect of partial replacement of fine aggregate by crushed concrete passed through a sieve size of No. 4.75 mm on workability, splitting tensile strength and compressive strength of recycled concrete at 7 and 28 days curing periods. Two sets of fine aggregate have been used, first set containing salts in conformity with the Iraqi Standard Specifications and another set not in conformity with the Iraqi Standard Specifications .The fine aggregate is replaced with crushed concrete in various percentage ( 25%, 50%, 75% and 100%), while 0% represents the control. Results showed that replacing 100% of crushed concrete after 28 days curing, the compressive strength has increased by 79% from the compressive strength of the control mix, while the splitting tensile strength has decreased, reaching 24% of the splitting tensile strength of the control mix.

في هذا البحث تم اجراء تحريات عملية لدراسة تأثير الاستبدال الجزئي للركام الناعم بخرسانة مكسرة مارة من المنخل رقم 4.75 ملمتر على قابلية التشغيل, مقاومة الشد ومقاومة الانضغاط للخرسانة المعادة بعمر 7و28 يوم انضاج . تم استعمال مجموعتين من الركام الناعم, المجموعة الاولى تحتوي على نسبة املاح مطابقة للمواصفات العراقية واخر تحتوي على نسبة املاح غير مطابقة للمواصفات العراقية. تم استبدال الركام الناعم بخرسانة مكسرة بنسب مختلفة (25%, 50%, 75%, 100%) بينما نسبة (0%) مثلت الخلطة المرجعية. بينت النتائج عند نسبة الاستبدال 100% بخرسانة مكسرة وعند عمر 28 يوم انضاج فان مقاومة الانضغاط ازدادت بنسبة 79% عن مقاومة الانضغاط للخلطة المرجعية بينما مقاومة الشد تناقصت وصولا الى 24% من مقاومة الشد للخلطة المرجعية.


Article
Physical and Mechanical Properties of Synthesized Doped Nanoferrite
دراسة الخواص الفيزيائية والميكانيكية للفرايت النانوي المطعم

Authors: Zainab I. Dhary زينب ابتهاج ضاري --- Mohammed S. Hamza محمد صلاب حمزة --- Fadhil A. Chyad فاضل عطية جياد
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2016 Volume: 12 Issue: 2 Pages: 10-17
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Nanoferrite materials have been synthesized by sol-gel auto combustion method. The effect of doping different percentages of Y2O3 (0.34 µm) on the physical and mechanical properties of selected mixed ferrite [(Li2.5Fe0.5) 0.9(Co4Fe2O4) 0.1] by adding 10% Cobalt ferrite was studied. Physical properties (i.e. .density, porosity and water absorption) were affected by the doping, where the density increased about 32% at 6 wt% Y2O3, while porosity has a drastically decreased about 80% at 6% Y2O3 and has a correlation effect on the mechanical properties(Splitting tensile strength and Vickers microhardnss). The fracture strength at 1 % wt. of Y2O3 has doubled value of the undoped sample and then decreased. The same behavior shows with the testing of Vickers micro hardness.SEM ( Scanning electron microscopy ) micrographs revealed that the microstructure of the fracture surface of the samples consist of detached approximately closely packed particles and also showed the formation of micro agglomerated particles with some voids . By doping with Y2O3 the pores decreased and a dense material obtained

حضرت مواد الفرايت النانوية بطريقة ( السول – جيل ) ذاتية الاحتراق وتم دراسة تأثير اضافة نسب مختلفة من اليتيريا ذو حجم حبيبي (0.34) مايكرون على الخواص الفيزيائية والميكانيكية للفرايت المحضر[(Li2.5Fe0.5)0.9(Co4Fe2O4)0.1] . ان الخواص الفيزيائية مثل ( الكثافة والمسامية وامتصاصية الماء ) تأثرت باضافة اليتيريا حيث ازدادت الكثافة بزيادة نسب الاضافة اما المسامية فقد تقلصت بصورة كبيرة والتي لها تأثير على الخواص الميكانيكية مثل ( متانة الشد وصلادة فيكرز ) . تضاعفت متانة الكسر عند بنسبة (1%) من اليتيريا ومن ثم تناقصت . نفس التصرف عند حساب صلادة فيكرز. اظهرت صور الالكتروني الماسح بأن التركيب المجهري لسطح الكسر للنماذج يحتوي تقريبا على حبيبات متجاورة متراصة وكذلك تكوين دقائق مايكروية متجمعة مع وجود فجوات . وبعد باضافة اليتيريا قلت المسامات وتم الحصول على مادة اكثر تراصاً.


Article
Some Properties of No-Fines Concrete Produced by Using Demolished Concrete as Recycled Coarse Aggregate

Authors: Sh. A. Salih --- I.N. Gorgis --- W.F. Abd
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2017 Volume: 35 Issue: 7 Part (A) Engineering Pages: 741-748
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This paper investigate some mechanical properties of no-fines concrete produced by using demolished concrete as coarse aggregate after crushing to different sizes. Different no-fine mixes were considered using Portland cement type I with two types of coarse aggregates, crushed natural gravel and crushed demolished concrete were used with two ratios by weight (1:5 and 1:7) cement/aggregate. Single size and graded aggregate were used with a maximum size of 20 mm. W /C ratio was kept as 0.4 for all mixes and supper plasticizer was used to keep the same flow and compaction factor value for all mixes . Using demolished concrete as coarse aggregate in no fine concrete led to decrease in the workability. As a comparison with natural coarse aggregate mixes, the average percentages of decreases for the flow, compaction factor and the fresh density were 2%, 2.3% and 6.4%, respectively. As well as the test results indicated that the compressive strength, splitting tensile strength, flexural strength and oven dry density for no fine made with crushed demolished concrete at age 28 days were decreased by about 29%, 22 %, 21% and 4% respectively as compared with no fine made by natural crushed aggregate.


Article
EFFECT OF HYBRID MICRO STEEL-POLYPROPYLENE FIBERS ON HIGH STRENGTH CONCRETE WITH MICRO SILICA FUME
تأثير هجين الياف الحديد الدقيقة-البولي بروبلين على الخرسانة عالية المقاومة الحاوية على غبار السلكا الدقيقة

Author: Othman Hameed Zinkaah عثمان حميد زنكاح
Journal: Muthanna Journal of Engineering and Technology(MJET) مجلة المثنى للهندسة والتكنولوجيا ISSN: 25720317 25720325 Year: 2014 Volume: 3 Issue: 1 Pages: 90-102
Publisher: Al-Muthanna University جامعة المثنى

Loading...
Loading...
Abstract

The present investigations consider the effect of hybrid micro steel- polypropylene fibers on high strength concrete. The fractions of steel and polypropylene fibers are 1% and 0.5% by volume respectively. Many mixes have been investigation by combination between steel fibers and polypropylene fibers with different percentages it is (0%S.F-100%P.P.F), (100%S.F-0%P.P.F), (25%S.F, 75%P.P.F), (50%S.F-50%P.P.F), (75%S.F-25%P.P.F) in addition to reference mix. Properties of high strength concrete such as compressive strength, splitting strength, flexural strength, static modulus of elasticity, and absorption have been studied. The results showed that, the compressive strength decrease by about 28% when adding (0%S.F-100%P.P.F), and there are a small increasing with adding (100%S.F-0%P.P.F). However the results showed that there are an inverse relationship between compressive strength and the amount of polypropylene fibers. Experimental work also showed that adding (0%S.F-100%P.P.F)decrease the splitting strength by about 16%, while using hybrid fibers increase the splitting strength but less than its increasing when adding (100%S.F-0%P.P.F). It can be concluded that, the maximum effect of hybrid fibers is on the flexural strength, it is reach to 128% more than reference mix. Furthermore absorption increases by using polypropylene fibers.

هذا البحث أخذ بنظر الاعتبار تأثير مزيج الألياف الحديدية وألياف البولي بروبلين على الخرسانة عالية المقاومة. إن نسبة ألياف الحديد والبولي بروبلين هي 1% و0,5% على التوالي. عدة خلطات تم الاستقصاء عنها وذلك بالمزج بين ألياف الحديد والبولي بروبلين بنسب مختلفة وهي (0% ألياف حديد-100% ألياف البولي بروبلين), (100% ألياف حديد-0% ألياف البولي بروبلين), (25% ألياف حديد-75% ألياف البولي بروبلين), (50% ألياف حديد-50% ألياف البولي بروبلين), (75% ألياف حديد-25% ألياف البولي بروبلين) بالإضافة إلى الخلطة المرجعية. مواصفات الخرسانة العالية المقاومة تم دراستها كمقاومة الانضغاط و مقاومة الانشطار ومعامل الإنحاء ومعامل المرونة ونسبة الامتصاص. النتائج أظهرت إن مقاومة الانضغاط تقل بنسبة 28% بإستخدام (0% ألياف حديد-100% ألياف البولي بروبلين) وعند استخدام (100% ألياف حديد-0% ألياف البولي بروبلين) تزداد مقاومة الانضغاط بنسبة صغيرة . لكن النتائج أظهرت إن هناك علاقة عكسية بين زيادة نسبة ألياف البولي بروبلين ومقاومة الانضغاط. النتائج العملية أظهرت أيظا إن إضافة (0% ألياف حديد-100% ألياف البولي بروبلين) تقلل من مقاومة الانشطار بنسبة 16% ولكن استخدام مزيج الألياف يزيد من مقاومة الانشطار ولكن هذه الزيادة أقل من الزيادة الناتجة من استخدام (100% ألياف حديد-0% ألياف البولي بروبلين). ويمكن الاستنتاج إن أكثر تأثير لمزيج الألياف هو على مقاومة الانحناء حيث تصل الزيادة إلى 128% أكثر من الخلطة المرجعية. بالإضافة إلى إن نسبة الامتصاص تزداد بإستخدام ألياف البولي بروبلين.


Article
EFFECT OF USING LIMESTONE AS A PARTIAL SUSTAINABLE MATERIAL ON DRYING SHRINKAGE OF CONCRETE

Authors: Jasmine Majed Taofeq --- Mouhamed Mosleh Salman
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2018 Volume: 22 Issue: 2 (Part-1) Pages: 30-45
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

Drying shrinkage can be reduced by using maximum practical amount of aggregate in the mix lowest water to cement ratio or by using some material helps to reduce shrinkage .Therefore different percentage of limestone ( 0 -10 -20 -30 %) were used by replacement of cement in both conventional and self-compacting concrete for studying strength and drying shrinkage .For each mix nine cubes (150 ×150 ×150 mm) for compressive strength ,six prisms (100 ×100 ×500 mm) for flexural strength,six cylinders ( 100 ×300 mm) for tensile splitting strength and four prisms (75 ×75 ×285 mm) for shrinkage test . Also, some tests such as slump flow, L-box and V-funnel made on fresh concrete for testing workability and segregation. The results increased by increasing filler material for all fresh concrete test except blocking ratio of L-box and maximum strength for CC was 45.84 MPa at 28 days when replaced 30 % of cement by limestone and 36 MPa at 56 days at 0% replacement for SCC. Maximum flexural for SCC was 2.50 MPa at 56 days with 30% replacement and 2.73 MPa for CC at 56 days with 0% replacement. Maximum splitting strength was 5.10 MPa at 56 days with 10% replacement for SCC and 4.11 MPa for CC at 28 days and 30% replacement. While for shrinkage test, the result was 557.5 micro strain at air and 390.3 micro strain for water at 90 days and 30% replacement for CC. while 680.5 micro strain at air and 436.1 micro strain for water at 90 days and 30% replacement for SCC.

Listing 1 - 5 of 5
Sort by
Narrow your search

Resource type

article (5)


Language

English (3)

Arabic and English (2)


Year
From To Submit

2018 (1)

2017 (1)

2016 (1)

2014 (2)